| Feature: | Oxidative Degradable |
|---|---|
| CAS No.: | 32131-17-2 |
| Formula: | (C12h22n2o2)N |
| Samples: |
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier Polyamine Nylon 66 is a 25% glass fiber reinforced injection molding PA66 grade
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | |||||
| A3HG5 is a 25% glass fiber reinforced injection molding PA66 grade. Applications Typical applications include machinery components and housings of high stiffness and dimensional stability. | |||||
| General | |||||
| Form | Resin Pellets | ||||
| Filler | 25 % Glass Fiber | ||||
| Feature | Good Dimensional Ec 1907/2006 (Reach) |
Good Hardness | Fuel Resistant | ||
| UL Yellow Card E36632-531624 | |||||
| Uses Housing | Mechanical Parts | ||||
| Physical | Nominal Value | Test Method | |||
| Density, dry | 1.32 g/cm³ | ASTM D792;ISO 1183 | |||
| Dry: Melt Volume-Flow Rate, MVR(275 °C;5 kg) | 50 cm³/10 min | ISO 1133 | |||
| Dry: Molding Shrinkage - Flow(3.18 mm) | 0.30 % | No Standard | |||
| Dry: Water Absorption, Saturation | 6.0 % |
ASTM D570 |
|||
| 23 °C | 6.0 % | ISO 62 | |||
| Dry: Water Absorption, Equilibrium | |||||
| 50% RH | 1.9 % | ASTM D570 | |||
| 50% RH;23 °C | 1.9 % | ISO 62 | |||
| Mechanical | Nominal Value | Test Method | |||
| Dry: Tensile Modulus(23 °C) | 8600 MPa | ISO 527-2 | |||
| Condition: Tensile Modulus(23 °C) | 6500 MPa | ISO 527-2 | |||
| Dry: Tensile Strength, Break | |||||
| 23 °C | 179 MPa | ASTM D638 | |||
| -40 °C | 196 MPa | ISO 527-2 | |||
| 23 °C | 170 MPa | ISO 527-2 | |||
| Condition: Tensile Strength, Break -40 °C 23 °C |
186 MPa 120 MPa |
ISO 527-2 | |||
| Thermal | Nominal Value | Test Method | |||
| Dry: Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa |
250 °C 250 °C |
ISO 75-2/B;ASTM D648 ISO 75-2/A;ASTM D648 |
|||
| Dry: Peak Melting Temperature | 260 °C | ASTM D3418;ISO 3146 | |||
| Dry: CLTE, Flow | 1.0E-5 cm/cm/°C 3.0E-5 cm/cm/°C |
ASTM E831 No Standard |
|||
| Dry: CLTE, Transverse | 6.5E-5 cm/cm/°C | No Standard | |||
| Dry: RTI Elec 0.8 mm 1.5 mm 3 mm |
130 °C 130 °C 130 °C |
UL 746 | |||
| Dry: RTI Imp 1.5 mm 3 mm |
120 °C 120 °C |
UL 746 | |||
| Dry: RTI Str 1.5 mm 3 mm |
130 °C 130 °C |
UL 746 | |||
| Dry: Flame Rating 0.8 mm 1.5 mm 3 mm |
HB HB HB |
UL 94 | |||
| Electrical Nominal Value Test Method | |||||
| Dry: Volume Resistivity | |||||
| 1.5 mm 1.0e+15 ohms ·cm ASTM D257 | |||||
| 1.0e+15 ohms ·cm IEC 60093 | |||||
| Condition: Volume resistivity | |||||
| 1.5 mm 1.0E+12 ohms ·cm ASTM D257 | |||||
| 1.0E+12 ohms ·cm IEC 60093 | |||||
| Dry: Dielectric Constant(1.0e+6 Hz) 3.50 IEC 60250 | |||||
| Condition: Dielectric Constant(1.0e+6 Hz) 5.50 IEC 60250 | |||||
| Dry: Dissipation Factor IEC 60250 | |||||
| 100 Hz 0.014 | |||||
| 1.0e+6 Hz 0.014 | |||||
| Condition: Dissipation factor IEC 60250 | |||||
| 100 Hz 0.30 | |||||
| 1.0e+6 Hz 0.16 | |||||
| Dry: Comparative Tracking Index 550 V IEC 60112 | |||||
| Condition: Comparative Tracking Index 550 V IEC 60112 | |||||
| Processing Nominal Value | |||||
| Drying Temperature<Injection> 80 °C | |||||
| Drying Time<Injection> 2.0 - 4.0 hr | |||||
| Suggested Max Moisture<Injection> 0.15 % | |||||
| Processing Temp, Melt<Injection> 280 - 305 °C | |||||
| Mold Temperature<Injection> 80 - 90 °C | |||||
| Injection Pressure<Injection> GRD 3.50 - 12.5 MPa | |||||
| Injection Rate<GDDFInjection> Fast | |||||