| CAS No.: | 9002-98-6 |
|---|---|
| Formula: | C39h30n2o6 |
| EINECS: | 205-793-9 |
| Samples: |
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier | ULTEM 1010 Resin is an unreinforced amorphous polyetherimide (PEI) resin that may offer a high glass transition temperature (Tg) of 217°C and improved flow. Features are excellent mechanical, electrical and dimensional properties up to high temperatures. The material may offer very good chemical resistance for an amorphous material and is inherently flame retardant offering UL94 V0 and 5V ratings and aerospace FAR 25.853 compliance. The material is RoHS compliant and the natural, uncolored, material is halogen free according to standards IEC 61249-2-21, IPC 4101E and JEDEC JS709B. For colored variants compliance needs to be checked case by case. The base material is transparent amber colored but is also available in custom colors - transparent and opaque. |
||||||||
| General | ||||||||
| Form | Resin Pellets | |||||||
Feature |
Easy Release | Low Shrinkage | Chemical Resistant | |||||
| Good Dimensional | Good Thermal | Good Hardness | ||||||
| Hydrolysis Resistance | Good Platable | Clear/Transparent | ||||||
| Low Creep Sensitivity | Good Metal Adhesion | Gamma Sterilizable | ||||||
| Uv-C Resistant | High Electric Breakdown St th (Bd ) | Transparent To Microwave | ||||||
| UL Yellow Card E121562-101048269 | ||||||||
Uses |
Automotive Industria . Mass Transportation |
Consumer Packaging Electrical Building and Construction Hydrocarbon and Energy |
||||||
| Physical | Nominal Value | Test Method | ||||||
| Density / Specific Gravity | ||||||||
| 1.27 g/cm³ | ISO 1183 | |||||||
| 1.27 | ASTM D792 | |||||||
| Moisture Absorption 23 °C;50% RH/24hrs 23 °C;50% RH/Equilibrium |
0.2 % 0.7 % |
ISO 62-4 | ||||||
| Water Absorption | ||||||||
| 24 hrs;23 °C | 0.25 % | ISO 62-1 | ||||||
| 23 °C;saturated | 1.25 % | ISO 62-1 | ||||||
| 24 hrs;23 °C | 0.25 % | ASTM D570 | ||||||
| 23°C/Saturated | 1.25 % | ASTM D570 | ||||||
| Melt Volume Rate, MVR 5 kg;MVR at 360 °C 5 kg;MVR at 340 °C |
25 cm³/10 min 13 cm³/10 min |
ISO 1133 | ||||||
| Melt Flow Rate[MFR](337 °C;6.6 kgf) | 17.8 g/10min | ASTM D1238 | ||||||
| Poisson's Ratio | 0.36 | ASTM E132 | ||||||
| Mold Shrinkage, Flow(3.2 mm) | 0.5 - 0.7 % | Method | ||||||
| Mold Shrinkage, XFlow(3.2 mm) | 0.5 - 0.7 % | Method | ||||||
| Hardness, Rockwell M | ||||||||
| 109 | ASTM D785 | |||||||
| 106 | ISO 2039-2 | |||||||
| Mechanical | Nominal Value | Test Method | ||||||
| Izod Impact, Notched | ||||||||
| 23 °C | 32 J/m | ASTM D256 | ||||||
| -30 °C | 41 J/m | ASTM D256 | ||||||
| 80*10*4;23 °C | 5 kJ/m² | ISO 180/1A | ||||||
| 80*10*4;-30 °C | 5 kJ/m² | ISO 180/1A | ||||||
| Izod Impact, Reverse Notched(3.2 mm) | 1174 J/m | ASTM D256 | ||||||
| Izod Impact, Unnotched | ||||||||
| 23 °C | 1600 J/m | ASTM D4812 | ||||||
| -30 °C | 1500 J/m | ASTM D4812 | ||||||
| 80*10*4;23 °C | NB kJ/m² | ISO 180/1U | ||||||
| 80*10*4;-30 °C | NB kJ/m² | ISO 180/1U | ||||||
| C harpy Impact, V-Notched 23 °C;Edgew;80*10*4;sp =62 mm 0 -30 °C;Edgew;80*10*4;sp =62 mm 0 |
4 kJ/m² 4 kJ/m² |
ISO 179 1eA | ||||||
| Gardner(23 °C) | 33 J | Method | ||||||
| Taber Abrasion(CS-17;1 kg;1000cy) | 10 mg | ASTM D1044 | ||||||
| Tensile Modulus | ||||||||
| 5 mm/min | 3350 MPa | ASTM D638 | ||||||
| 1 mm/min | 3200 MPa | ISO 527 | ||||||
| Tensile Strain, Break | ||||||||
| 5 mm/min;Type I | 60 % | ASTM D638 | ||||||
| 50 mm/min;Type I | 60 % | ASTM D638 | ||||||
| 50 mm/min | 50 % | ISO 527 | ||||||
| Tensile Strain, Yield | ||||||||
| 5 mm/min;Type I | 7 % | ASTM D638 | ||||||
| 50 mm/min;Type I | 7 % | ASTM D638 | ||||||
| 50 mm/min | 6 % | ISO 527 | ||||||
| Tensile Stress, Yield | ||||||||
| 5 mm/min;Type I | 110 MPa | ASTM D638 | ||||||
| 50 mm/min;Type I | 115 MPa | ASTM D638 | ||||||
| 50 mm/min | 110 MPa | ISO 527 | ||||||
| Flexural Modulus | ||||||||
| 1.3 mm/min;50 mm;span | 3200 MPa | ASTM D790 | ||||||
| 2.6 mm/min;100 mm;Span | 3400 MPa | ASTM D790 | ||||||
| 2 mm/min | 3300 MPa | ISO 178 | ||||||
| Flexural Stress, Yield | ||||||||
| 1.3 mm/min;50 mm;span | 165 MPa | ASTM D790 | ||||||
| 2.6 mm/min;100 mm;Span | 160 MPa | ASTM D790 | ||||||
| 2 mm/min | 160 MPa | ISO 178 | ||||||
| Ball Indentation Hardness(H358/30) | 140 MPa | ISO 2039-1 | ||||||
| Thermal | Nominal Value | Test Method | ||||||
| Oxygen Index | 44 % 47 % |
ASTM D2863 ISO 4589 |
||||||
| NBS Smoke Density, Flaming(Ds 4 min) | 2 | ASTM E662 | ||||||
| Glow Wire Flammability Index(3.2 mm) | 960 °C | IEC 60695-2-12 | ||||||
| UL Recognized ≥ 3 mm ≥ 0.75 mm ≥ 0.4 mm |
5VA V-0 V-2 |
UL 94 | ||||||
| Thermal Conductivity | ||||||||
| 0.22 W/m-K | ASTM C177 | |||||||
| 0.22 W/m-K | ISO 8302 | |||||||
| Vicat Softening Temperature | ||||||||
| Rate B/50 | 211 °C | ASTM D1525 | ||||||
| Rate A/50 | 215 °C | ISO 306 | ||||||
| Rate B/120 | 212 °C | ISO 306 | ||||||
| Rate B/50 | 211 °C | ISO 306 | ||||||
| Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 0.45 MPa;6.4 mm 3.2 mm;1.82 MPa 1.82 MPa;6.4 mm |
207 °C 210 °C 190 °C 201 °C |
ASTM D648 | ||||||
| CTE, Flow | ||||||||
| -20°C to 150°C | 5.6E-05 1/°C | ASTM E831 | ||||||
| -20°C to 150°C | 5.2E-05 1/°C | ISO 11359-2 | ||||||
| CTE, XFlow | ||||||||
| -20°C to 150°C | 5.4E-05 1/°C | ASTM E831 | ||||||
| -20°C to 150°C | 5.2E-05 1/°C | ISO 11359-2 | ||||||
| Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 | ||||||
| HDT/Af(1.8) | 192 °C | ISO 75/Af | ||||||
| HDT/Bf(0.45) | 209 °C | ISO 75/Bf | ||||||
| Relative Temp Index, Elec | 170 °C | UL 746B | ||||||
| Relative Temp Index, Mechanical with Impact | 170 °C | UL 746B | ||||||
| Relative Temp Index, Mechanical without Impact | 170 °C | UL 746B | ||||||
| Electrical | Nominal Value | Test Method | ||||||
| Volume Resistivity | ||||||||
| 1.0E+15 ohms ·cm | IEC 60093 | |||||||
| 1.0E+17 ohms ·cm | ASTM D257 | |||||||
| Surface Resistivity, ROA | > 1.E+15 ohms | IEC 60093 | ||||||
| Dielectric Strength, in Oil | ||||||||
| 0.8 mm | 33 kV/mm | IEC 60243-1 | ||||||
| 1.6 mm | 25 kV/mm | IEC 60243-1 | ||||||
| 3.2 mm | 16 kV/mm | IEC 60243-1 | ||||||
| 1.6 mm | 28 kV/mm | ASTM D149 | ||||||
| 3.2 mm | 19.7 kV/mm | ASTM D149 | ||||||
| Relative Permittivity | ||||||||
| 1.0e+6 Hz | 2.9 | IEC 60250 | ||||||
| 50/60 Hz | 2.9 | IEC 60250 | ||||||
| 100 Hz | 3.15 | ASTM D150 | ||||||
| 1.0e+3 Hz | 3.15 | ASTM D150 | ||||||
| Dissipation Factor | ||||||||
| 1.0e+6 Hz | 6.0E-03 | IEC 60250 | ||||||
| 50/60 Hz | 5.0E-04 | IEC 60250 | ||||||
| 1.1e+9 Hz | 1.2E-03 | |||||||
| 5.0e+9 Hz | 2.4E-03 | |||||||
| 1.0e+10 Hz | 2.7E-03 | |||||||
| 100 Hz | 1.5E-03 | ASTM D150 | ||||||
| 1.0e+3 Hz | 1.2E-03 | ASTM D150 | ||||||
| Dielectric Constant | ||||||||
| 1.1e+9 Hz | 3.01 | |||||||
| 5.0e+9 Hz | 3.02 | |||||||
| 1.0e+10 Hz | 3.02 | |||||||
| Comparative Tracking Index | 150 V | IEC 60112 | ||||||
| Comparative tracking index M | 100 V | IEC 60112 | ||||||
| Dielectric Strength, in Air(1.6 mm) | 32.7 kV/mm | ASTM D149 | ||||||
| Comparative Tracking Index, CTI | PLC4 | UL 746A | ||||||
| Hot-wire Ignition, HWI ≥ 3 mm ≥ 0.75 mm |
PLC 1 PLC 2 |
UL 746A | ||||||
| High Amp Arc Ignition, HAI ≥ 3 mm ≥ 0.75 mm |
PLC 3 PLC4 |
UL 746A | ||||||
| High Voltage Arc Tracking Rate, HVTR | PLC 2 | UL 746A | ||||||
| Arc Resistance, Tungsten Electrode | PLC5 | ASTM D495 | ||||||
Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.
Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.
With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}