Audited Supplier | Product Description | |||
| 4795R is a high heat resistant poly(ester)carbonate injection molding resin. Flame Retardant. | |||
| General | |||
| Form Resin Pellets | |||
| Feature Good Thermal | |||
| Uses Consumer | Electrical | Building and Construction | |
| Physical | Nominal Value | Test Method | |
| Density / Specific Gravity | 1.2 1.2 g/cm³ |
ASTM D792 ISO 1183 |
|
| Mold Shrinkage, Flow(3.2 mm) | 0.97 % | Method | |
| Mold Shrinkage, XFlow(3.2 mm) | 0.97 % | Method | |
| Melt Flow Rate[MFR] | ASTM D1238 | ||
| 330 °C;2.16 kgf | 15 g/10min | ||
| 300 °C;1.2 kgf | 2.5 g/10min | ||
| Mechanical | Nominal Value | Test Method | |
| Izod Impact, Unnotched(23 °C) | 2140 J/m | ASTM D4812 | |
| Izod Impact, Notched(23 °C) | 578 J/m | ASTM D256 | |
| Instrumented Dart Impact, Energy at Peak(23 °C) | 73 J | ASTM D3763 | |
| Instrumented Dart Impact, Total Energy(23 °C) | 77 J | ASTM D3763 | |
| Tensile Stress, Yield(50 mm/min;Type I) | 68 MPa | ASTM D638 | |
| Tensile Stress, Break(50 mm/min;Type I) | 70 MPa | ASTM D638 | |
| Tensile Strain, Yield(50 mm/min;Type I) | 7.5 % | ASTM D638 | |
| Tensile Strain, Break(50 mm/min;Type I) | 117 % | ASTM D638 | |
| Tensile Modulus(50 mm/min) | 2170 MPa | ASTM D638 | |
| Flexural Stress, break(1.3 mm/min;50 mm;span) | 105 MPa | ASTM D790 | |
| Flexural Modulus(1.3 mm/min;50 mm;span) | 2200 MPa | ASTM D790 | |
| Thermal | Nominal Value | Test Method | |
| Vicat Softening Temperature(Rate B/50) | 164 °C | ASTM D1525 | |
| Heat Deflection Temperature[HDT], Unannealed | ASTM D648 | ||
| 0.45 MPa;3.2 mm | 160 °C | ||
| 3.2 mm;1.82 MPa | 147 °C | ||
| Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 | |
| Processing | Nominal Value | ||
| Drying Temperature<Injection> | 120 °C | ||
| Drying Time<Injection> | 3 - 4 hrs | ||
| Drying Time, Cumulative<Injection> | 48 hrs | ||
| Maximum Moisture Content<Injection> | 0.02 % | ||
| Melt Temperature<Injection> | 350 - 370 °C | ||
| Nozzle Temperature<Injection> | 345 - 365 °C | ||
| Front, Zone 3 Temperature<Injection> | 350 - 370 °C | ||
| Middle, Zone 2 Temperature<Injection> | 340 - 360 °C | ||
| Rear, Zone 1 Temperature<Injection> | 325 - 350 °C | ||
| Mold Temperature<Injection> | 80 - 115 °C | ||
| Back Pressure<Injection> | 0.3 - 0.7 MPa | ||
| Screw Speed <Injection> | 40 - 70 rpm | ||
| Shot To Cylinder Size<Injection> | 40 - 60 % | ||
| Vent Depth <Injection> | 0.025 - 0.076 mm | ||