Good Flame Retardancy ABS Heat Resistance 5va Display Chassis Modem Power Panel

• Feature: Plastics
• CAS No.: 25766-59-0
• Formula: C6h4c(CH3)2c6h4oco2-]N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: ABS-764G
• EINECS: 618-371-8
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Form: Resin Pellets
• Chemical Substances: Polycarbonate
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Good flame retardancy ABS Heat resistance 5VA Display Chassis Modem Power Panel

Product Description

Product Description
Features: Good flame retardancy; Heat resistance; 0.75mm V-2; 1.0mm V-0; 2.5mm 5VA Application: Display; Chassis; Modem; Power Panel; Power Outlet; Car Battery; Cash Register Housing; Printer Housing; Remote controls; light boxes; fax machines; projectors; large MFPs; coffee machines; TV front and rear frames and car audio consoles
General
Form	Resin Pellets
Feature	Good Thermal	Flame Retardant		Outdoor
UL Yellow Card                         E56070-103035269
Batteries                            Displays                             Housing
Light Covers                      Printer Parts                       Panel
Automotive                       Printer Chassis                  Remote Controls
Coffee Machine
Physical                                                                                 Nominal Value                                       Test Method
Density / Specific Gravity(23 °C)                                          1.22 g/cm³                                             ISO 1183
Melt Volume-Flow Rate, MVR(220 °C;10 kg)                      34 cm³/10 min                                       ISO 1133
Molding Shrinkage                                                              0.30 - 0.60 %                                          ISO 294-4
Mechanical                                                                            Nominal Value                                      Test Method
Tensile Stress, Yield(50 mm/min)                                        34.0 MPa                                                ISO 527-2/50
Tensile Stress, Break(50 mm/min)                                       27.0 MPa                                               ISO 527-2/50
Tensile Strain, Break(50 mm/min)                                       10 %                                                       ISO 527-2/50
Flexural Modulus(2 mm/min)                                              1800 MPa                                               ISO 178
Flexural Stress(2 mm/min)                                                   54.0 MPa                                                ISO 178
C harpy Notched Impact Strength                                                                                                      ISO 179
-30 °C                                                                                   7.0 kJ/m²
23 °C                                                                                     12 kJ/m²
Notched Izod Impact Strength                                                                                                          ISO 180/1A
-30 °C                                                                                   7.0 kJ/m²
23 °C                                                                                     13 kJ/m²
Thermal                                                                                Nominal Value					Test Method
Deflection Temperature Under Load, Unannealed(1.8 MPa)			82.0 °C		ISO 75-2/A
Deflection Temperature Under Load, Annealed(1.8 MPa)			92.0 °C		ISO 75-2/A
Vicat Softening Temperature
5 kg;50 ºC/hr			90.0 °C		ISO 306/B50
50 ºC/hr;1 kg			101 °C		ISO 306/A50
CLTE, Flow			8.3E-5 cm/cm/°C		ISO 11359-2
Flame Rating 0.75 mm 1 mm 2.5 mm			V-2 V-0 5VA		UL 94
Processing					Nominal Value
Drying Time					80 - 85 °C
Drying Temperature					2 - 4 h
Barrell Temperature - Front					190 - 220 °C
Barrell Temperature - Middle					190 - 220 °C
Barrell Temperature - Rear					180 - 210 °C
Mold Temperature					40 - 70 °C
Injection Pressure					50 - 80 %
Hold Pressure					20 - 50 %
Back Pressure					0.5 - 1 MPa

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....