| Feature: | Engineering Plastics |
|---|---|
| CAS No.: | Na |
| Formula: | Na |
| Samples: |
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier 
LUX2619-XH, this extrusion grade resin boasts a UL94 V-0 rating at 1.5 mm, making it an excellent choice for applications that require high flammability ratings.
Moreover, LUX2619-XH has been specifically formulated for superior light reflectivity, ensuring maximum luminance in applications where clarity is key.
With its outstanding mechanical properties and easy processing
| General | |||||
| Form | Resin | Pellets | |||
| Feature | High | Reflection | |||
| Uses | Lighting Applications | ||||
| Physical | Nominal Value | Test Method | |||
| Density / Specific Gravity | 1.34 g/cm³ | ASTM D792;ISO 1183 |
|||
| Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 7.5 g/10min | ASTM D1238 | |||
| Molding Shrinkage, Flow(3.2 mm) | 0.80 - 1.0 % | Internal Method | |||
| Water Absorption, Saturation(23 °C) | 0.35 % | ISO 62 | |||
| Water Absorption, Equilibrium(50% RH;23 °C) | 0.15 % | ISO 62 | |||
| Mechanical | Nominal Value | Test Method | |||
| Tensile Strength, Yield(50 mm/min;Type I) | 57.0 MPa | ASTM D638 | |||
| Tensile Strength, Break(50 mm/min;Type I) | 50.0 MPa | ASTM D638 | |||
| Tensile Elongation, Yield(50 mm/min;Type I) | 6.0 % | ASTM D638 | |||
| Tensile Elongation, Break(50 mm/min;Type I) | 74 % | ASTM D638 | |||
| Flexural Modulus(1.3 mm/min;50 mm;Span) | 2730 MPa | ASTM D790 | |||
| Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 97.0 MPa | ASTM D790 | |||
| Notched Izod Impact -30 °C 23 °C |
140 J/m 640 J/m |
ASTM D256 | |||
| Unnotched Izod Impact(23 °C) | 2100 J/m | ASTM D4812 | |||
| Instrumented Dart Impact, Total Energy(23 °C) | 69.0 J | ASTM D3763 | |||
| Thermal | Nominal Value | Test Method |
| Deflection Temperature Under Load, Unannealed 0.45 MPa;3.2 mm 1.8 MPa;3.2 mm |
141 °C 129 °C |
ASTM D648 |
| Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 147 °C | ASTM D1525 |
| CLTE, Flow(-40 - 40 °C) | 6.1E-5 cm/cm/°C | ASTM E831 |
| CLTE, Transverse(-40 - 40 °C) | 6.4E-5 cm/cm/°C | ASTM E831 |
| Flame Rating(1.5 mm) | V-2 | UL 94 |
| Glow Wire Flammability Index(1 - 3 mm) | 960 °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature [GWIT] 1 mm 3 mm |
875 °C 850 °C |
IEC 60695-2-13 |
| Processing | Nominal Value |
| Drying Temperature<Injection> | 120 °C |
| Drying Time<Injection> | 3.0 - 4.0 hr |
| Suggested Max Moisture<Injection> | 0.020 % |
| Suggested Shot Size<Injection> | 40 - 60 % |
| Rear Temperature<Injection> | 290 - 310 °C |
| Middle Temperature<injection> | 300 - 320 °C |
| Front Temperature<Injection> | 310 - 330 °C |
| Nozzle Temperature<Injection> | 305 - 325 °C |
| Processing Temp, Melt<Injection> | 310 - 330 °C |
| Mold Temperature<Injection> | 80 - 115 °C |
| Back Pressure<Injection> | 0.300 - 0.700 MPa |
| Screw Speed<Injection> | 40 - 70 rpm |
| Vent Depth<Injection> | 0.025 - 0.076 mm |
| Drying Time, Cumulative<Injection> | 48 hrs |
| Drying Temperature<Profile Extrusion> | 120 °C |
| Drying Time<Profile Extrusion> | 2 - 4 hrs |
| Melt Temperature<Profile Extrusion> | 240 - 295 °C |
| Barrel - Zone 1 Temperature<Profile Extrusion> | 240 - 285 °C |
| Barrel - Zone 2 Temperature<Profile Extrusion> | 240 - 285 °C |
| Barrel - Zone 3 Temperature<Profile Extrusion> | 240 - 285 °C |
| Hopper Temperature<Profile Extrusion> | 100 - 120 °C |
| Adapter Temperature<Profile Extrusion> | 230 - 285 °C |
| Die Temperature<Profile Extrusion> | 230 - 295 °C |
| Calibrator Temperature<Profile Extrusion> | 50 - 100 °C |