Product Description | |||
Suitable for both injection and extrusion.Applications: Injection and extruded use such as rod and sheetInformation provided by API Kolon. | |||
General | |||
Form | Resin Pellets | ||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.41 g/cm³ | ASTM D792 | |
Moisture Absorption at Equilibrium(60% RH) | 0.22 % | ASTM D570 | |
Linear Mold Shrinkage | 2 % | ASTM D955 | |
Melt Flow | 6.0 g/10min | ASTM D1238 | |
Hardness, Rockwell M | 80 | ASTM D785 | |
Mechanical | Nominal Value | Test Method | |
Tensile Strength | 60.0 MPa | ASTM D638 | |
Elongation at Break | 75 % | ASTM D638 | |
Flexural Strength | 90.0 MPa | ASTM D790 | |
Flexural Modulus | 2350 MPa | ASTM D790 | |
Izod Impact, Notched(Temperature; 23 °C) | 76 J/m | ASTM D256 | |
Thermal | Nominal Value | Test Method | |
CTE, Flow | 130 µm/m-°C | ASTM D696 | |
Melting Point | 166 °C | ASTM D1525 | |
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
158 °C 110 °C |
ASTM D648 | |
Vicat Softening Point | 162 °C | ASTM D1525 | |
Flammability, UL94 | HB | UL 94 | |
Electrical | Nominal Value | Test Method | |
Volume Resistivity | 1.00e+14 ohms·cm | ASTM D257 | |
Surface Resistance | 1.00e+16 Ohms | ASTM D257 | |
Dielectric Constant | 3.7 | ASTM D150 | |
Dielectric Strength | 19.0 kV/mm | ASTM D149 | |
Dissipation Factor(Frequency; 1000000 Hz) | 0.0060 | ASTM D150 |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |