Product Description | ||||
XHT3143T is a high flow, UV stabilized, high heat polycarbonate copolymer. It is only available in limited transparent colors | ||||
General | ||||
Form Resin Pellets | ||||
Feature Good Thermal Outdoor | ||||
Uses Automotive Electrical | ||||
Physical Nominal Value Test Method | ||||
Density / Specific Gravity 1.21 ASTM D792 1.2 g/cm³ ISO 1183 |
||||
Mold Shrinkage, Flow(3.2 mm) 0.6 - 0.9 % Method | ||||
Melt Flow Rate[MFR](330 °C;2.16 kgf) 33 g/10min ASTM D1238 | ||||
Water Absorption(23 °C;saturated) 0.3 % ISO 62-1 | ||||
Moisture Absorption(50% RH;23 °C) 0.3 % ISO 62 | ||||
Melt Volume Rate, MVR(2.16 kg;330 °C) 30 cm³/10 min ISO 1133 | ||||
Mechanical Nominal Value Test Method | ||||
Izod Impact, Notched ASTM D256 | ||||
23 °C 97 J/m | ||||
-30 °C 55 J/m | ||||
Instrumented Dart Impact, Total Energy(23 °C) 68 J ASTM D3763 | ||||
Unnotched Izod Impact Strength ISO 180/1U | ||||
unnotched;80*10*3;23 °C 0 NB kJ/m² | ||||
unnotched;80*10*3;-30 °C 0 NB kJ/m² | ||||
Notched Izod Impact Strength ISO 180/1A | ||||
notched;80*10*3;23 °C 0 9 kJ/m² | ||||
notched;80*10*3;-30 °C 0 9 kJ/m² | ||||
C harpy Impact, V-Notched ISO 179 1eA | ||||
23 °C;Edgew;80*10*3;sp =62mm 0 11 kJ/m² | ||||
-30 °C;Edgew;80*10*3;sp =62mm 0 9 kJ/m² | ||||
C harpy Impact, Unnotched ISO 179 1eU | ||||
23 °C;Edgew;80*10*3;sp =62mm 0 NB kJ/m² | ||||
-30 °C;Edgew;80*10*3;sp =62mm 0 NB kJ/m² | ||||
Tensile Stress, Yield | ||||
50 mm/min;Type I | 70 MPa | ASTM D638 | ||
50 mm/min | 70 MPa | ISO 527 | ||
Tensile Stress, Break | ||||
50 mm/min;Type I | 55 MPa | ASTM D638 | ||
50 mm/min | 60 MPa | ISO 527 | ||
Tensile Strain, Yield | ||||
50 mm/min;Type I | 6 % | ASTM D638 | ||
50 mm/min | 6 % | ISO 527 | ||
Tensile Strain, Break | ||||
50 mm/min;Type I | 70 % | ASTM D638 | ||
50 mm/min | 70 % | ISO 527 | ||
Tensile Modulus | ||||
5 mm/min | 2700 MPa | ASTM D638 | ||
1 mm/min | 2500 MPa | ISO 527 | ||
Flexural Stress, Yield | ||||
1.3 mm/min;50 mm;span | 120 MPa | ASTM D790 | ||
2 mm/min | 80 MPa | ISO 178 | ||
Flexural Modulus | ||||
1.3 mm/min;50 mm;span | 2600 MPa | ASTM D790 | ||
2 mm/min | 2500 MPa | ISO 178 | ||
Thermal | Nominal Value | Test Method | ||
Vicat Softening Temperature | ||||
Rate B/50 | 170 °C | ASTM D1525 | ||
Rate B/50 | 168 °C | ISO 306 | ||
Rate B/120 | 170 °C | ISO 306 | ||
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
166 °C 156 °C |
ASTM D648 | ||
CTE, Flow | ||||
-40 - 40 °C | 6.0E-05 1/°C | ASTM E831 | ||
-40 - 40 °C | 6.0E-05 1/°C | ISO 11359-2 | ||
CTE, XFlow | ||||
-40 - 40 °C | 6.0E-05 1/°C | ASTM E831 | ||
-40 - 40 °C | 6.0E-05 1/°C | ISO 11359-2 | ||
HDT/Af(1.8) | 152 °C | ISO 75/Af | ||
Processing | Nominal Value | |||
Drying Temperature<Injection> | 135 °C | |||
Drying Time<Injection> | 4 - 6 hrs | |||
Maximum Moisture Content<Injection> | 0.02 % | |||
Melt Temperature<Injection> | 290 - 325 °C | |||
Nozzle Temperature<Injection> | 285 - 320 °C | |||
Front, Zone 3 Temperature<Injection> | 290 - 325 °C | |||
Middle, Zone 2 Temperature<Injection> | 280 - 310 °C | |||
Rear, Zone 1 Temperature<Injection> | 270 - 300 °C | |||
Mold Temperature<Injection> | 95 - 130 °C | |||
Back Pressure<Injection> | 0.3 - 0.7 MPa | |||
Screw Speed <Injection> | 40 - 90 rpm | |||
Shot To Cylinder Size<Injection> | 40 - 60 % | |||
Vent Depth <Injection> | 0.025 - 0.08 mm |