Product Description | ||||||||
18 MFR. Improved flame retardance. Internal mold release. UV stabilized. | ||||||||
General | ||||||||
Form | Resin Pellets | |||||||
Feature | Outdoor | F2 | Diffusive | |||||
UL Yellow Card E207780-101325405 | ||||||||
Uses | Appliances Electronic Displays |
Lighting Applications Fluid Handling | Automotive Lighting | |||||
Physical | Nominal Value | Test Method | ||||||
Density / Specific Gravity | 1.19 - 1.20 g/cm³ | ASTM D792 | ||||||
Specific Volume | 0.830 cm³/g | ASTM D792 | ||||||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 18 g/10min | ASTM D1238 | ||||||
Molding Shrinkage, Flow(3.2 mm) | 0.50 - 0.70 % | Internal Method | ||||||
Water Absorption(24 hr) | 0.15 % | ASTM D570 | ||||||
Water Absorption, Equilibrium | ASTM D570 | |||||||
23 °C | 0.35 % | |||||||
100 °C | 0.58 % | |||||||
Outdoor Suitability | f2 | UL 746C | ||||||
Rockwell Hardness, M-Scale | 70 | ASTM D785 | ||||||
Rockwell Hardness, R-Scale | 118 | ASTM D785 | ||||||
Mechanical Nominal Value | Test Method | |||||||
Tensile Strength, Yield(50 mm/min;Type I) 62.0 MPa | ASTM D638 | |||||||
Tensile Strength, Break(50 mm/min;Type I) 65.0 MPa | ASTM D638 | |||||||
Tensile Elongation, Yield(50 mm/min;Type I) 7.0 % | ASTM D638 | |||||||
Tensile Elongation, Break(50 mm/min;Type I) 110 % | ASTM D638 | |||||||
Flexural Modulus(1.3 mm/min;50 mm;Span) 2340 MPa | ASTM D790 | |||||||
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) 93.0 MPa | ASTM D790 | |||||||
Taber Abrasion Resistance(1.0e+3 Cycles;1.0e+3 g;CS-1710.0 mg Wheel) |
ASTM D1044 | |||||||
C harpy Notched Impact Strength -30 °C;80 23 °C;80 |
12 kJ/m² 65 kJ/m² |
ISO 179 1eA | ||||||
C harpy Unnotched Impact Strength -30 °C;80 23 °C;80 |
No Break No Break |
ISO 179 1eU | ||||||
Notched Izod Impact 23 °C -30 °C;80*10*3 mm 23 °C;80*10*3 mm |
600 J/m 11 kJ/m² 65 kJ/m² |
ASTM D256 ISO 180/1A ISO 180/1A |
||||||
Unnotched Izod Impact 23 °C -30 °C;80*10*3 mm 23 °C;80*10*3 mm |
3200 J/m No Break No Break |
ASTM D4812 ISO 180/1U ISO 180/1U |
||||||
Gardner Impact(23 °C) 169 J | ASTM D3029 | |||||||
Tensile Impact Strength(Type S) 546 kJ/m² | ASTM D1822 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;6.4 mm 1.8 MPa;6.4 mm |
137 °C 132 °C |
ASTM D648 |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 154 °C | ASTM D1525 |
Ball Pressure Test(123 - 127 °C) | Pass | IEC 60695-10-2 |
CLTE, Flow(-40 - 95 °C) | 6.8E-5 cm/cm/°C | ASTM E831 |
Specific Heat | 1260 J/kg/°C | ASTM C351 |
Thermal Conductivity | 0.25 W/m-K | ASTM C177 |
RTI Elec | 80.0 °C | UL 746 |
RTI Imp | 80.0 °C | UL 746 |
RTI Str | 80.0 °C | UL 746 |
Flame Rating(0.8 - 1.7 mm) | V-2 | UL 94 |
Glow Wire Flammability Index 0.75 mm 1.5 mm |
750 °C 850 °C |
IEC 60695-2-12 |
Glow Wire Ignition Temperature, by VDE(0.75 mm) | 875 °C | IEC 60695-2-13 |
Glow Wire Ignition Temperature [GWIT](1.5 mm) | 850 °C | IEC 60695-2-13 |
Electrical | Nominal Value | Test Method |
Volume Resistivity | > 1.0E+17 ohms ·cm | ASTM D257 |
Dielectric Strength, in Air(3.2 mm) | 15 kV/mm | ASTM D149 |
Dielectric Constant 60 Hz 5.0e+4 Hz 1.0e+6 Hz |
3.17 3.17 2.96 |
ASTM D150 |
Dissipation Factor 50 Hz 60 Hz 1.0e+6 Hz |
9.0E-4 9.0E-4 0.010 |
ASTM D150 |
Comparative Tracking Index[CTI] | PLC 3 | UL 746 |
High Amp Arc Ignition, HAI, Surface | PLC 1 | UL 746 |
Hot-wire Ignition, HWI | PLC 3 | UL 746 |
Optical | Nominal Value | Test Method |
Refractive Index | 1.586 | ASTM D542 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Suggested Shot Size<Injection> | 40 - 60 % | |
Rear Temperature<Injection> | 260 - 280 °C | |
Middle Temperature<injection> | 270 - 295 °C | |
Front Temperature<Injection> | 280 - 305 °C | |
Nozzle Temperature<Injection> | 275 - 300 °C | |
Processing Temp, Melt<Injection> | 280 - 305 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Vent Depth <Injection> | 0.025 - 0.076 mm | |
Drying Time, Cumulative<Injection> | 48 hrs |