45% Glass Reinforced Hydrolysis Resistant PPA High Performance Polyamide

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PPA-HTN51G45
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-60% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

30% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide
 Heat-conducting nylon

Product Description

Product Description
45% Glass Reinforced, Hydrolysis Resistant, PPA, High Performance Polyamide
General
Form	Resin Pellets
Filler	45 % Glass Fiber
Feature	Good Thermal	Hydrolysis Resistance
UL Yellow Card                         E41938-101495695
Physical                                                                                 Nominal Value				Test Method
Density, dry                                                                           1.57 g/cm³				ISO 1183
Dry: Molding Shrinkage, Across Flow			0.60 %	ISO 294-4
Dry: Molding Shrinkage, Across Flow, Annealed			0.75 %	ISO 294-4
Dry: Molding Shrinkage, Flow			0.10 %	ISO 294-4
Dry: Molding Shrinkage, Flow, Annealed(170 °C;2 hr)			0.20 %	ISO 294-4
Dry: Water Absorption, Saturation(23 °C;2 mm)			3.6 %	ISO 62
Dry: Water Absorption, Equilibrium(50% RH;23 °C;2 mm)			1.2 %	ISO 62
Dry: Rockwell Hardness, M-Scale			109	ISO 2039-2
Dry: Rockwell Hardness, R-Scale			125	ISO 2039-2
Mechanical			Nominal Value	Test Method
Dry: Tensile Modulus			15000 MPa	ISO 527-2
Condition: Tensile Modulus			15000 MPa	ISO 527-2
Dry: Tensile Stress, Break			240 MPa	ISO 527-2
Condition: Tensile Stress, Break			230 MPa	ISO 527-2
Dry: Tensile Strain, Break			2.4 %	ISO 527-2
Condition: Tensile Strain, Break			2.1 %	ISO 527-2
Condition: Tensile creep modulus 1 hr 1.0e+3 hr			14000 MPa 12000 MPa	ISO 899-1
Dry: Flexural Modulus			13000 MPa	ISO 178
Condition: Flexural Modulus			13000 MPa	ISO 178
Dry: Flexural Stress			330 MPa	ISO 178
Dry: Poisson's Ratio			0.33	No Standard
Condition: Poisson's Ratio			0.33	No Standard
Dry: Charpy Notched Impact Strength -40 °C -30 °C 23 °C			13 kJ/m² 12 kJ/m² 12 kJ/m²	ISO 179 1eA
Condition: Charpy Notched Impact Strength(23 °C)			11 kJ/m²	ISO 179 1eA
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C			85 kJ/m² 90 kJ/m²	ISO 179 1eU
Condition: Charpy Unnotched Impact Strength(23 °C)			75 kJ/m²	ISO 179 1eU
Dry: Notched Izod Impact Strength -40 °C 23 °C			13 kJ/m² 12 kJ/m²	ISO 180/1A
Notched Izod Impact Strength: condition(23 °C)			12 kJ/m²	ISO 180/1A
Dry: Unnotched Izod Impact Strength(23 °C)			87 kJ/m²	ISO 180/1U
Thermal			Nominal Value	Test Method
Dry: Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa			286 °C 265 °C	ISO 75-2/B ISO 75-2/A
Dry: Glass Transition Temperature(10 °C;min)			135 °C	ISO 11357-2
Condition: Glass Transition Temperature(10 °C;min)			95.0 °C	ISO 11357-2
Dry: Melting temperature, first heat			300 °C	ISO 11357-3
Dry: CLTE, Flow -40 - 23 °C 55 - 160 °C			1.5E-5 cm/cm/°C 1.5E-5 cm/cm/°C 1.3E-5 cm/cm/°C	ISO 11359-2
Dry: CLTE, Transverse -40 - 23 °C			5.4E-5 cm/cm/°C 5.0E-5 cm/cm/°C	ISO 11359-2
Dry: Burning rate(1 mm;FMVSS 302)			29 mm/min	ISO 3795
Dry: Flame Rating 0.9 mm 1.5 mm			HB HB	IEC 60695-11- 10;UL 94;IEC 60695-11-20
Dry: Oxygen index			24 %	ISO 4589-2
Dry: FMVSS Flammability			B	FMVSS 302
Electrical			Nominal Value	Test Method
Condition: Surface resistivity			1.0E+14 ohms	IEC 62631-3-2
Dry: Volume Resistivity			> 1E+11 ohms ·cm	IEC 62631-3-1
Condition: Volume resistivity			1E+11 ohms ·cm	IEC 62631-3-1
Dry: Electric Strength			35 kV/mm	IEC 60243-1
Condition: Electric Strength			34 kV/mm	IEC 60243-1
Dry: Relative permittivity 1.0e+6 Hz 100 Hz			3.90 4.20	IEC 62631-2-1
Dry: Dissipation Factor 100 Hz 1.0e+6 Hz			9.0E-3 0.015	IEC 62631-2-1
Dry: Comparative Tracking Index			600 V	IEC 60112
Condition: Comparative Tracking Index			600 V	IEC 60112
Processing				Nominal Value
Drying Temperature<Injection>				100 °C
Drying Time - Desiccant Dryer<Injection>				6.0 - 8.0 hr
Suggested Max Moisture<Injection>				0.10 %
Processing Temp, Melt<Injection>				320 - 330 °C
Melt Temperature, Optimum<Injection>				325 °C
Mold Temperature<Injection>				140 - 180 °C
Mold Temperature, Optimum<Injection>				150 °C
Drying Recommended <Injection>				YES

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 