Product Description | ||||||
FXE4271L is a 10% glass filled, impact modified polycarbonate with excellent light-shield capability. It is designed for high flow, superior surface appearance, enhance release and good impact ductility. FXE4271L is available in white color only and ideal for light-shield applications. | ||||||
General | ||||||
Form | Resin Pellets | |||||
Filler | 10 % Glass Fiber | |||||
Feature | ||||||
Light Shielding | ||||||
UL Yellow Card E207780-101619221 | ||||||
Uses | Electrical | |||||
Physical | Nominal Value | Test Method | ||||
Density / Specific Gravity | 1.25 1.25 g/cm³ |
ASTM D792 ISO 1183 |
||||
Mold Shrinkage, Flow(3.2 mm) | 0.2 - 0.3 % | Method | ||||
Mold Shrinkage, XFlow(3.2 mm) | 0.4 - 0.5 % | Method | ||||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 15 g/10min | ASTM D1238 | ||||
Water Absorption(23 °C;saturated) | 0.13 % | ISO 62-1 | ||||
Moisture Absorption(50% RH;23 °C) | 0.04 % | ISO 62 | ||||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 14 cm³/10 min | ISO 1133 | ||||
Mechanical | Nominal Value | Test Method | ||||
Izod Impact, Unnotched(23 °C) | 1880 J/m | ASTM D4812 | ||||
Izod Impact, Notched(23 °C) | 205 J/m | ASTM D256 | ||||
Instrumented Dart Impact, Total Energy(23 °C) | 36 J | ASTM D3763 | ||||
Tensile Stress, Yield(5 mm/min;Type I) | 48 MPa | ASTM D638 | ||||
Tensile Stress, Break(5 mm/min;Type I) | 37 MPa | ASTM D638 | ||||
Tensile Strain, Yield(5 mm/min;Type I) | 4 % | ASTM D638 | ||||
Tensile Strain, Break(5 mm/min;Type I) | 11 % | ASTM D638 | ||||
Tensile Modulus(5 mm/min) | 3850 MPa | ASTM D638 | ||||
Flexural Stress, Yield(1.3 mm/min;50 mm;span) | 87 MPa | ASTM D790 | ||||
Flexural Modulus(1.3 mm/min;50 mm;span) | 3600 MPa | ASTM D790 | ||||
Thermal | Nominal Value | Test Method | ||||
UL Recognized(≥ 0.4 mm) | HB | UL 94 | ||||
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
127 °C 120 °C |
ASTM D648 | ||||
Vicat Softening Temperature(Rate B/120) | 132 °C | ISO 306 | ||||
Relative Temp Index, Elec | 80 °C | UL 746B | ||||
Relative Temp Index, Mechanical with Impact | 80 °C | UL 746B | ||||
Relative Temp Index, Mechanical without Impact | 80 °C | UL 746B | ||||
Optical | Nominal Value | Test Method | ||||
Light Transmission At 0.4 Mm(0.4 mm) | < 2.5 % | Method | ||||
Processing | Nominal Value | |||||
Drying Temperature<Injection> | 120 °C | |||||
Drying Time<Injection> | 3 - 4 hrs | |||||
Drying Time, Cumulative<Injection> | 48 hrs | |||||
Maximum Moisture Content<Injection> | 0.02 % | |||||
Melt Temperature<Injection> | 290 - 310 °C | |||||
Nozzle Temperature<Injection> | 280 - 305 °C | |||||
Front, Zone 3 Temperature<Injection> | 290 - 310 °C | |||||
Middle, Zone 2 Temperature<Injection> | 275 - 300 °C | |||||
Rear, Zone 1 Temperature<Injection> | 265 - 290 °C | |||||
Mold Temperature<Injection> | 70 - 95 °C | |||||
Back Pressure<Injection> | 0.3 - 0.7 MPa | |||||
Screw Speed <Injection> | 40 - 70 rpm | |||||
Shot To Cylinder Size<Injection> | 40 - 60 % | |||||
Vent Depth <Injection> | 0.025 - 0.076 mm |