35% Glass Reinforced PA4t Stable to Heat Enhanced Hydrolytic Stability for Automotive

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA4T-MX15HR
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 5%-60% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

35% Glass Reinforced PA4T Stable to heat Enhanced Hydrolytic Stability for Automotive 
 Heat-conducting nylon

Product Description

Product Description
35% Glass Reinforced, PA4T, Stable to heat, Enhanced Hydrolytic Stability, for Automotive applications
General
Form                                        Resin Pellets
Filler                                         35 % Glass Fiber
Feature                                           Good Thermal                   Hydrolysis Resistance
Uses                                         Automotive
Physical                                                                                 Nominal Value                                       Test Method
Density, dry                                                                           1.49 g/cm³                                              ISO 1183
Dry: Spiral Flow, Injection Pressure(1 mm;1.0e+3 bar)       5.50 cm
Dry: Molding Shrinkage, Across Flow                                 1.1 %                                                       ISO 294-4
Dry: Molding Shrinkage, Flow                                             0.35 %                                                     ISO 294-4
Mechanical	Nominal Value	Test Method
Dry: Tensile Modulus -40 °C 100 °C 120 °C 150 °C 200 °C	12500 MPa 12500 MPa 11600 MPa 11200 MPa 5300 MPa 3740 MPa	ISO 527-2
Condition: Tensile Modulus	12500 MPa	ISO 527-2
Dry: Tensile Stress, Break -40 °C 100 °C 120 °C 150 °C 200 °C	240 MPa 260 MPa 170 MPa 145 MPa 80.0 MPa 55.0 MPa	ISO 527-2
Condition: Tensile Stress, Break	220 MPa	ISO 527-2
Dry: Tensile Strain, Break -40 °C 100 °C 120 °C 150 °C 200 °C	2.6 % 2.7 % 2.7 % 2.8 % 8.0 % 8.0 %	ISO 527-2
Condition: Tensile Strain, Break	2.4 %	ISO 527-2
Dry: Charpy Notched Impact Strength(23 °C)	12 kJ/m²	ISO 179 1eA
Thermal	Nominal Value	Test Method
Dry: Heat Deflection Temperature, Unannealed(1.8 MPa)	300 °C	ISO 75-2/A
Dry: Glass Transition Temperature, DMTA, tan d	145 °C	ASTM D5026/D7028
Dry: Melting Temperature(10 °C/min)	330 °C	ISO 11357-3
Dry: CLTE, Flow	1.5E-5 cm/cm/°C	ISO 11359-2
Dry: CLTE, Transverse	5.2E-5 cm/cm/°C	ISO 11359-2

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 