Product Description | ||||
High heat resistant polyphtha late carbonate, provides DTUL of 300F at 264 psi. | ||||
General | ||||
Form Resin Pellets | ||||
Feature Good Thermal | ||||
Uses | Automotive Electrical |
Consumer | Healthcare | |
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.2 1.19 g/cm³ |
ASTM D792 | ||
Specific Volume | 0.83 cm³/g | ASTM D792 | ||
Water Absorption(24 hrs;23 °C) | 0.19 % | ASTM D570 | ||
Mold Shrinkage, Flow(3.2 mm) | 0.8 - 1 % | Method | ||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 2 g/10min | ASTM D1238 | ||
Hardness, Rockwell R | 127 | ASTM D785 | ||
Hardness, Rockwell M | 92 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Unnotched(23 °C) | 3204 J/m | ASTM D4812 | ||
Izod Impact, Notched(23 °C) | 373 J/m | ASTM D256 | ||
Tensile Strength, Type S | 577 kJ/m² | ASTM D1822 | ||
Falling Dart Impact(23 °C;D 3.0e+3) | 149 J | ASTM D3029 | ||
Tensile Stress, Yield(50 mm/min;Type I) | 65 MPa | ASTM D638 | ||
Tensile Stress, Break(50 mm/min;Type I) | 77 MPa | ASTM D638 | ||
Tensile Strain, Break(50 mm/min;Type I) | 78 % | ASTM D638 | ||
Flexural Stress, Yield(1.3 mm/min;50 mm;span) | 97 MPa | ASTM D790 | ||
Flexural Modulus(1.3 mm/min;50 mm;span) | 2330 MPa | ASTM D790 | ||
Thermal | Nominal Value | Test Method | ||
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 148 °C | ASTM D648 | ||
CTE, Flow(-40°C to 95°C) | 8.1e-05 1/°C | ASTM E831 | ||
Specific Heat | 1.26 J/g-°C | ASTM C351 | ||
Thermal Conductivity | 0.21 W/m-K | ASTM C177 | ||
Electrical | Nominal Value | Test Method | ||
Volume Resistivity | > 2.5E+17 ohms ·cm | ASTM D257 | ||
Dielectric Strength, in Air(3.2 mm) | 20 kV/mm | ASTM D149 | ||
Relative Permittivity 50/60 Hz 1.0e+6 Hz |
3.27 3.1 |
ASTM D150 | ||
Dissipation Factor 50/60 Hz 100 Hz |
1.6E-03 0.026 |
ASTM D150 | ||
Optical | Nominal Value | Test Method | ||
Light Transmission(2.54 mm) | 85 % | ASTM D1003 | ||
Haze(2.54 mm) | 1 % | ASTM D1003 | ||
Refractive Index | 1.6 | ASTM D542 | ||
Processing | Nominal Value | |||
Drying Temperature<Injection> | 120 °C | |||
Drying Time<Injection> | 3 - 4 hrs | |||
Drying Time, Cumulative<Injection> | 48 hrs | |||
Maximum Moisture Content<Injection> | 0.02 % | |||
Melt Temperature<Injection> | 350 - 370 °C | |||
Nozzle Temperature<Injection> | 345 - 365 °C | |||
Front, Zone 3 Temperature<Injection> | 350 - 370 °C | |||
Middle, Zone 2 Temperature<Injection> | 340 - 360 °C | |||
Rear, Zone 1 Temperature<Injection> | 325 - 350 °C | |||
Mold Temperature<Injection> | 80 - 115 °C | |||
Back Pressure<Injection> | 0.3 - 0.7 MPa | |||
Screw Speed <Injection> | 40 - 70 rpm | |||
Shot To Cylinder Size<Injection> | 40 - 60 % | |||
Vent Depth <Injection> | 0.025 - 0.076 mm |