Feature: | Oxidative Degradable |
---|---|
CAS No.: | 32131-17-2 |
Formula: | (C12h22n2o2)N |
EINECS: | 211-024-8 |
Material: | Polyamide(Nylon 6.66)/PA |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Nylon 66 resin containing 30% glass bead and graphite High Impact, Wear Resistant
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | ||||
RBG16I compound is based on Nylon 6/6 resin containing 30% glass bead and graphite. Added features of this grade include: High Impact, Wear Resistant. | ||||
General | ||||
Form Resin Pellets | ||||
Filler 30 % Glass Bead Graphite | ||||
Feature | Low Warpage Abrasion Resistant |
Good Dimensional Internally Lubricated | High Impact | |
Uses Consumer Electrical Building and Construction | ||||
Physical Nominal Value Test Method | ||||
Molding Shrinkage, Flow, Tensile Bar 0.2 - 0.4 % Method | ||||
Density / Specific Gravity 1.37 g/cm³ ISO 1183 | ||||
Mechanical Nominal Value Test Method | ||||
Izod Impact, Unnotched(80*10*4;23 °C) 40 kJ/m² ISO 180/1U | ||||
Izod Impact, Notched(80*10*4;23 °C) 6 kJ/m² ISO 180/1A | ||||
Tensile Stress, Yield(5 mm/min) 64 MPa ISO 527 | ||||
Tensile Strain, Yield(5 mm/min) 3.6 % ISO 527 | ||||
Tensile Modulus(1 mm/min) 4300 MPa ISO 527 | ||||
Flexural Stress, Yield(2 mm/min) 100 MPa ISO 178 | ||||
Flexural Modulus(2 mm/min) 3500 MPa ISO 178 | ||||
Thermal Nominal Value Test Method | ||||
CTE, Flow(23°C to 60°C) 7.1e-05 1/°C ISO 11359-2 | ||||
CTE, XFlow(23°C to 60°C) 7.9e-05 1/°C ISO 11359-2 | ||||
HDT/Bf(0.45) 223 °C ISO 75/Bf | ||||
HDT/Af(1.8) 78 °C ISO 75/Af | ||||
Processing | Nominal Value | |||
Back Pressure<Injection> | 0.2 - 0.3 MPa | |||
Drying Temperature<Injection> | 80 °C | |||
Drying Time<Injection> | 4 hrs | |||
Front, Zone 3 Temperature<Injection> | 295 - 305 °C | |||
Maximum Moisture Content<Injection> | 0.15 - 0.25 % | |||
Melt Temperature<Injection> | 280 - 305 °C | |||
Middle, Zone 2 Temperature<Injection> | 280 - 295 °C | |||
Mold Temperature<Injection> | 95 - 110 °C | |||
Rear, Zone 1 Temperature<Injection> | 265 - 275 °C | |||
Screw Speed <Injection> | 30 - 60 rpm |