Audited Supplier | Product Description | ||||
| Ultramid® A 218 V30 Black 34 NG is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection moulding. This grade has been specially designed to improve its resistance to automotive cooling liquids, increasing lifetime of parts in permanent contact with such liquids. | ||||
| General | ||||
| Form | Resin Pellets | |||
| Filler | 30 % Glass Fiber | |||
| Excellent Processability Glycol Resistance Good Thermal Hydrolysis Resistance Ec 1907/2006 (Reach) |
||||
| Uses | Pump Parts | Automotive | ||
| Physical | Nominal Value | Test Method | ||
| Density, dry | 1.36 g/cm³ | ISO 1183 | ||
| Dry: Molding Shrinkage, Across Flow | 1.1 % | ISO 294-4 | ||
| Dry: Molding Shrinkage, Flow | 0.40 % | ISO 294-4 | ||
| Dry: Water Absorption(24 hr;23 °C) | 0.80 % | ISO 62 | ||
| Dry: Water Absorption, Equilibrium(50% RH;23 °C) | 1.7 % | ISO 62 | ||
| Mechanical | Nominal Value | Test Method |
| Dry: Tensile Modulus | 10000 MPa | ISO 527-1 |
| Condition: Tensile Modulus | 7500 MPa | ISO 527-1 |
| Dry: Tensile Stress, Break | 190 MPa | ISO 527-2 |
| Condition: Tensile Stress, Break | 135 MPa | ISO 527-2 |
| Dry: Tensile Elongation, Break 51 mm/min |
3.0 % 3.0 % |
ASTM D638 ISO 527-2 |
| Condition: Tensile Elongation, Break | 7.0 % | ISO 527-2 |
| Dry: Flexural Modulus | 9000 MPa 9000 MPa |
ASTM D790 ISO 178 |
| Condition: Flexural Modulus | 6400 MPa | ISO 178 |
| Dry: Flexural Strength | 290 MPa 280 MPa |
ASTM D790 ISO 178 |
| Condition: Flexural Strength | 185 MPa | ISO 178 |
| Dry: Charpy Notched Impact Strength(23 °C) | 11 kJ/m² | ISO 179/1eA |
| Condition: Charpy Notched Impact Strength(23 °C) | 16 kJ/m² | ISO 179/1eA |
| Dry: Charpy Unnotched Impact Strength -30 °C 23 °C |
67 kJ/m² 80 kJ/m² |
ISO 179/1eU |
| Condition: Charpy Unnotched Impact Strength -30 °C 23 °C |
70 kJ/m² 95 kJ/m² |
ISO 179/1eU |
| Dry: Notched Izod Impact 23 °C 23 °C |
120 J/m 10 kJ/m² |
ASTM D256 ISO 180 |
| Izod Notched Impact: condition(23 °C) | 18 kJ/m² | ISO 180 |
| Thermal | Nominal Value | Test Method |
| Dry: Deflection Temperature Under Load, Unannealed 1.8 MPa 1.8 MPa |
255 °C 250 °C |
ASTM D648 ISO 75-2/A |
| Dry: Melting Point | 262 °C | ISO 11357-3 |
| Condition: Flame Rating(3.2 mm) | HB | UL 94 |
| Dry: Flame Rating 0.8 mm 1.6 mm |
HB HB |
IEC 60695-11- 10;IEC 60695-11- 20 |
| Dry: Glow Wire Flammability Index(1.6 mm) | 650 °C | IEC 60695-2-12 |
| Dry: Oxygen index | 23 % | ISO 4589-2 |
| Electrical | Nominal Value | Test Method |
| Condition: Surface resistivity | 1.0E+12 ohms | IEC 62631-3-2 |
| Dry: Volume Resistivity | 1E+13 ohms·cm | IEC 62631-3-1 |
| Condition: Volume resistivity | 1E+11 ohms·cm | IEC 62631-3-1 |
| Dry: Electric Strength(2 mm) | 34 kV/mm | IEC 60243-1 |
| Condition: Electric Strength(2 mm) | 29 kV/mm | IEC 60243-1 |
| Dry: Relative permittivity(100 Hz) | 3.70 | IEC 62631-2-1 |
| Condition: Relative Permittivity(100 Hz) | 4.00 | IEC 62631-2-1 |
| Dry: Dissipation Factor(100 Hz) | 0.010 | IEC 62631-2-1 |
| Condition: Dissipation factor(100 Hz) | 0.11 | IEC 62631-2-1 |
| Dry: Comparative Tracking Index, Solution A | 400 V | IEC 60112 |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 80 °C | |
| Suggested Max Moisture<Injection> | 0.15 % | |
| Rear Temperature<Injection> | 270 - 280 °C | |
| Middle Temperature<injection> | 275 - 285 °C | |
| Front Temperature<Injection> | 280 - 290 °C | |
| Mold Temperature<Injection> | 70 - 100 °C |