Polycarbonate (PC) Is an Injection Moldable Non-Chlorinated/Brominated Unfilled Light

• Feature: Plastics
• CAS No.: 25766-59-0
• Formula: C6h4c(CH3)2c6h4oco2-]N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PC-BFL-4000u
• EINECS: 618-371-8
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Natural Color
• Place of Origin: Guangdong, China
• Use: Radiator Front Cover.Automotive Parts
• Features: Lubricated, Good Wear Resistance, Low Friction and
• Application: Zippers Irish Flutes, Bagpipes, Practice Chanters
• Form: Resin Pellets
• Delivery Time: in 7 Days
• Applications: Appliance Handles, Spotlights, Electric Motors.
• Glass Fiber: %
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Polycarbonate (PC) is an injection moldable non-chlorinated/brominated unfilled light
   

   

 

Product Description
LEXAN BFL4000U Polycarbonate (PC) is an injection moldable non-chlorinated/brominated, unfilled, flame retardant grade with high flow. It is UV stabilized, light reflective and has an MVR of 22 (300°C/1.2kg) and a UL94 [email protected]mm.
General
Form	Resin Pellets
Feature		Outdoor	Excellent Processability       Non-Brominated & Non- Chlorinated Flame   Retardant
		Non-Chlorinated Diff      i	Good Surface Appearance  High Reflection
		us ve
UL Yellow Card                         E207780-531362
Uses	Automotive   Electrical		Consumer                         Industria   Building and Construction  Hydrocarbon and Energy
Physical			Nominal Value	Test Method
Density / Specific Gravity			1.38 1.38 g/cm³	ASTM D792 ISO 1183
Mold Shrinkage, Flow(3.2 mm)			0.5 - 0.7 %	SABIC Method
Melt Flow Rate[MFR](300 °C;1.2 kgf)			24 g/10min	ASTM D1238
Water Absorption(23 °C;saturated)			0.35 %	ISO 62-1
Moisture Absorption(50% RH;23 °C)			0.15 %	ISO 62
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C)			22 cm³/10 min	ISO 1133

 

Mechanical	Nominal Value	Test Method
Izod Impact, Notched
23 °C	470 J/m	ASTM D256
-30 °C	240 J/m	ASTM D256
80*10*4;23 °C	30 kJ/m²	ISO 180/1A
80*10*4;-30 °C	20 kJ/m²	ISO 180/1A
Instrumented Dart Impact, Total Energy(23 °C)	68 J	ASTM D3763
C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0)	30 kJ/m²	ISO 179 1eA
Tensile Stress, Yield
5 mm/min;Type I	54 MPa	ASTM D638
5 mm/min	50 MPa	ISO 527
Tensile Stress, Break
5 mm/min;Type I	47 MPa	ASTM D638
5 mm/min	44 MPa	ISO 527
Tensile Strain, Yield
5 mm/min;Type I	5 %	ASTM D638
5 mm/min	6 %	ISO 527
Tensile Strain, Break
5 mm/min;Type I	56 %	ASTM D638
5 mm/min	74 %	ISO 527
Tensile Modulus
5 mm/min	2240 MPa	ASTM D638
1 mm/min	2040 MPa	ISO 527
Flexural Stress, Yield
1.3 mm/min;50 mm;span	90 MPa	ASTM D790
2 mm/min	83 MPa	ISO 178
Flexural Modulus
1.3 mm/min;50 mm;span	2050 MPa	ASTM D790
2 mm/min	2170 MPa	ISO 178

 

Thermal	Nominal Value	Test Method
UL Recognized(≥ 1.5 mm)	V-0	UL 94
Vicat Softening Temperature
Rate B/50	136 °C	ASTM D1525
Rate B/50	137 °C	ISO 306
Rate B/120	139 °C	ISO 306
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 0.45 MPa;6.4 mm 1.82 MPa;6.4 mm	131 °C 134 °C 124 °C	ASTM D648
Heat Deflection Temperature[HDT], Annealed(3.2 mm;1.82 MPa)	115 °C	ASTM D648
CTE, Flow
-40 - 40 °C	7.5e-05 1/°C	ASTM E831
-40 - 40 °C	7.5e-05 1/°C	ISO 11359-2
CTE, XFlow
-40 - 40 °C	7.5e-05 1/°C	ASTM E831
-40 - 40 °C	7.5e-05 1/°C	ISO 11359-2
HDT/Bf(0.45)	130 °C	ISO 75/Bf
HDT/Af(1.8)	115 °C	ISO 75/Af
Relative Temp Index, Elec	120 °C	UL 746B
Relative Temp Index, Mechanical with Impact	105 °C	UL 746B
Relative Temp Index, Mechanical without Impact	120 °C	UL 746B
Electrical	Nominal Value	Test Method
Hot-wire Ignition, HWI(1.5 mm)	PLC 2	UL 746A
High Amp Arc Ignition, HAI(1.5 mm)	PLC 2	UL 746A

 

Processing	Nominal Value
Drying Temperature<Injection>	120 °C
Drying Time<Injection>	3 - 4 hrs
Drying Time, Cumulative<Injection>	48 hrs
Maximum Moisture Content<Injection>	0.02 %
Melt Temperature<Injection>	270 - 295 °C
Nozzle Temperature<Injection>	265 - 290 °C
Front, Zone 3 Temperature<Injection>	270 - 295 °C
Middle, Zone 2 Temperature<Injection>	260 - 280 °C
Rear, Zone 1 Temperature<Injection>	250 - 270 °C
Mold Temperature<Injection>	70 - 95 °C
Back Pressure<Injection>	0.3 - 0.7 MPa
Screw Speed <Injection>	40 - 70 rpm
Shot To Cylinder Size<Injection>	40 - 60 %
Vent Depth <Injection>	0.025 - 0.076 mm

      

Company Profile

Product Parameters

Our Customers

Our Certificates

 

Our Production

Our Package/Shipping

Our Advantages

 

Our Samples

 

Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.

Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.

With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry