45% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | ||||||||
AS-1945 HS is a 45% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material exceeds the performance required by the automotive industry for polymeric materials exposed to antifreeze at 226° F (108°C), even when tested at 275° F (135°C). Potential applications include a variety of automotive components such as thermostat housings, heater core endcaps, heater hose connectors, and water inlets, outlets and valves. Black: AS-1945 HS BK 324 |
||||||||
General | ||||||||
Form | Resin Pellets | |||||||
Filler | ||||||||
Feature |
||||||||
Good Dimensional Glycol Resistance | Enhanced Stiffness | |||||||
Good Thermal | ||||||||
UL Yellow Card | E95746-102842791 | |||||||
Automotive Under The | ||||||||
Uses |
Hood | Metal Replacement H i | Thick-walled Parts P |
|||||
ous ng | ower | |||||||
Valves/Valve Parts | Mechanical Parts | |||||||
Physical | Nominal Value | Test Method | ||||||
Density / Specific Gravity | 1.57 g/cm³ | ISO 1183/A | ||||||
Molding Shrinkage, Flow | ||||||||
Type D2 | 0.20 % | ASTM D955 | ||||||
0.20 % | ISO 294-4 | |||||||
Molding Shrinkage, Across Flow | ||||||||
Type D2 | 0.60 % | ASTM D955 | ||||||
0.60 % | ISO 294-4 | |||||||
Mechanical | Nominal Value | Test Method | ||||||
Tensile Modulus | 15200 MPa |
ASTM D638 |
||||||
135 °C;0 hours at 275° F | 10300 MPa 15100 MPa |
ASTM D638 ISO 527-2 |
||||||
Tensile Strength, Break | 252 MPa |
ASTM D638 |
||||||
135 °C;0 hours at 275° F | 107 MPa 244 MPa |
ASTM D638 ISO 527-2 |
||||||
Tensile Elongation, Break | 2.5 % | ASTM D638 | ||||||
Flexural Modulus | ||||||||
13800 MPa | ASTM D790 | |||||||
12600 MPa | ISO 178 | |||||||
Flexural Stress | 335 MPa | ISO 178 | ||||||
Flexural Stress, Yield | 359 MPa | ASTM D790 | ||||||
C harpy Notched Impact Strength | 13 kJ/m² | ISO 179 1eA | ||||||
Notched Izod Impact | 120 J/m |
ASTM D256 |
||||||
135 °C;1.0e+3 hours | 69 J/m 11 kJ/m² |
ASTM D256 ISO 180/1A |
||||||
Thermal | Nominal Value | Test Method | ||||||
Deflection Temperature Under Load, Unannealed(1.8 MPa) | 282 °C | ASTM D648;ISO 75-2/Af | ||||||
Melting Point | 312 °C | ISO 11357-3 | ||||||
Processing | Nominal Value | |||||||
Drying Temperature<Injection> | 121 °C | |||||||
Drying Time<Injection> | 4.0 hr | |||||||
Suggested Max Moisture<Injection> | 0.030 - 0.060 % | |||||||
Hopper Temperature<Injection> | 79 °C | |||||||
Rear Temperature<Injection> | 304 - 318 °C | |||||||
Front Temperature<Injection> | 316 - 329 °C | |||||||
Processing Temp, Melt<Injection> | 321 - 343 °C | |||||||
Mold Temperature<Injection> | 135 °C |