| Product Description |
| LDS (Laser Direct Structuring), Black color only, Improved Impact |
| General |
| Form Resin Pellets |
| Feature Lds Ductile Laser Markable |
| UL Yellow Card E340159-100746643 |
| Uses Laser Direct Structuring Cell Phone Cases |
| Physical Nominal Value Test Method |
| Density / Specific Gravity 1.19 g/cm³ ISO 1183 |
| Melt Mass-Flow Rate, MFR(260 °C;5 kg) 14 g/10min ISO 1133 |
| Melt Volume-Flow Rate, MVR(260 °C;5 kg) 13 cm³/10 min ISO 1133 |
| Molding Shrinkage, Across Flow 0.50 - 0.70 % Internal Method |
| Molding Shrinkage, Flow 0.50 - 0.70 % Internal Method |
| Water Absorption, Saturation(23 °C) 0.60 % ISO 62 |
| Water Absorption, Equilibrium(50% RH;23 °C) 0.20 % Internal Method |
| Mechanical Nominal Value Test Method |
| Tensile Modulus 2250 MPa ISO 527-2/1 |
| Tensile Stress, Yield 51.0 MPa ISO 527-2/50 |
| Tensile Strain, Yield 4.0 % ISO 527-2/50 |
| Tensile Strain, Break > 50 % ISO 527-2/50 |
| Flexural Modulus(2 mm/min) 2250 MPa ISO 178 |
| Flexural Stress(2 mm/min) 80.0 MPa ISO 178 |
| C harpy Notched Impact Strength ISO 179 |
| -30 °C 25 kJ/m² |
| 23 °C 60 kJ/m² |
| C harpy Unnotched Impact Strength ISO 179 |
| -30 °C No Break |
| 23 °C No Break |
| Notched Izod Impact Strength ISO 180/4A |
| -20 °C 30 kJ/m² |
| 23 °C 50 kJ/m² |
| Multi-Axial Instrumented Impact Energy(23 °C) 35.0 J ISO 6603-2 |
| Thermal |
Nominal Value |
Test Method |
| Heat Deflection Temperature, Unannealed(1.8 MPa) |
102 °C |
ISO 75-2/A |
| Vicat Softening Temperature |
122 °C |
ISO 306 |
| CLTE, Flow |
7.0E-5 cm/cm/°C |
ISO 11359-2 |
| CLTE, Transverse |
7.0E-5 cm/cm/°C |
ISO 11359-2 |
| Flame Rating(0.7 mm) |
HB |
UL 94 |
| Electrical |
Nominal Value |
Test Method |
| Surface Resistivity |
> 1.0E+15 Ohms |
IEC 60093 |
| Volume Resistivity |
> 1.0E+15 Ohms ·cm |
IEC 60093 |
| Dielectric Constant(1.0e+6 Hz) |
2.80 |
IEC 60250 |
| Dissipation Factor(1.0e+6 Hz) |
5.0E-3 |
IEC 60250 |
| Processing |
|
Nominal Value |
| Drying Temperature - Hot Air Dryer<Injection> |
|
100 - 110 °C |
| Drying Time - Hot Air Dryer<Injection> |
|
4.0 - 6.0 hr |
| Rear Temperature<Injection> |
|
250 - 270 °C |
| Middle Temperature<injection> |
|
250 - 270 °C |
| Front Temperature<Injection> |
|
250 - 270 °C |
| Nozzle Temperature<Injection> |
|
250 - 270 °C |
| Mold Temperature<Injection> |
|
40 - 80 °C |