| Feature: | Engineering Plastics |
|---|---|
| CAS No.: | Na |
| Formula: | Na |
| Samples: |
customize according to your exact requirements
|
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier SLX2571T-XH is an outstanding transparent weatherable polycarbonate copolymer designed for blowmolding and extrusion applications.
This high-performance copolymer offers superior weatherability, excellent impact resistance, and unmatched optical clarity in demanding outdoor environments.
It features excellent resistance to UV radiation, heat, and chemicals, making it ideal for a range of applications including light covers, signs, outdoor displays, and various other outdoor-related products. Additionally, its easy processing and consistent performance make it an excellent choice for high-quality products that require reliable performance in challenging environments.
With its unique combination of superior properties and exceptional reliability, SLX2571T-XH is the ideal choice for any application that demands a reliable and high-performance transparent weatherable polycarbonate copolymer.
| General | ||||
| Form | Resin Pellets | |||
| Feature: Anti-Scratch Color Consistency Outdoor | ||||
| Uses | Consumer | Electrical | ||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.2 1.2 g/cm³ |
ASTM D792 ISO 1183 |
||
| Mold Shrinkage, Flow(3.2 mm) | 0.6 - 0.8 % | SABIC Method | ||
| Melt Flow Rate[MFR](300 °C;1.2 kgf) | 3 g/10min | ASTM D1238 | ||
| Water Absorption(23 °C;saturated) | 0.35 % | ISO 62-1 | ||
| Moisture Absorption(50% RH;23 °C) | 0.15 % | ISO 62 | ||
| Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 2 cm³/10 min | ISO 1133 | ||
| Mechanical | Nominal Value | Test Method | ||
| Izod Impact, Notched | ASTM D256 | |||
| 23 °C | 848 J/m | |||
| -30 °C | 141 J/m | |||
| Instrumented Dart Impact, Total Energy(23 °C) | 74 J | ASTM D3763 | ||
| Unnotched Izod Impact Strength(unnotched;80*10*3;23 °C 0) | NB kJ/m² | ISO 180/1U | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| notched;80*10*3;23 °C 0 | 70 kJ/m² | |||
| notched;80*10*3;-30 °C 0 | 10 kJ/m² | |||
| Charpy Impact, V-Notched | ISO 179 1eA | |||
| 23 °C;Edgew;80*10*3;sp=62mm 0 | 75 kJ/m² | |||
| -30 °C;Edgew;80*10*3;sp=62mm 0 | 15 kJ/m² | |||
| Charpy Impact, Unnotched(23 °C;Edgew;80*10*3;sp=62mm 0) |
NB kJ/m² | ISO 179 1eU | ||
| Tensile Stress, Yield 50 mm/min;Type I 50 mm/min |
62 MPa 63 MPa |
ASTM D638 ISO 527 |
||
| Tensile Stress, Break 50 mm/min;Type I 50 mm/min |
64 MPa 63 MPa |
ASTM D638 ISO 527 |
| Tensile Strain, Yield 50 mm/min;Type I 50 mm/min |
7.5 % 6 % |
ASTM D638 ISO 527 |
| Tensile Strain, Break 50 mm/min;Type I 50 mm/min |
106 % 98 % |
ASTM D638 ISO 527 |
| Tensile Modulus 5 mm/min 1 mm/min |
2400 MPa 2350 MPa |
ASTM D638 ISO 527 |
| Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min |
101 MPa 94 MPa |
ASTM D790 ISO 178 |
| Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
2400 MPa 2240 MPa |
ASTM D790 ISO 178 |
| Thermal | Nominal Value | Test Method |
| Vicat Softening Temperature | ||
| Rate B/50 | 143 °C | ASTM D1525 |
| Rate B/50 | 143 °C | ISO 306 |
| Rate B/120 | 145 °C | ISO 306 |
| Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 126 °C | ASTM D648 |
| CTE, Flow -40 - 40 °C -40 - 40 °C |
6.0E-05 1/°C 6.0E-05 1/°C |
ASTM E831 ISO 11359-2 |
| CTE, XFlow -40 - 40 °C -40 - 40 °C |
6.4e-05 1/°C 6.4e-05 1/°C |
ASTM E831 ISO 11359-2 |
| HDT/Af(1.8) | 125 °C | ISO 75/Af |
| Processing | Nominal Value |
| Drying Temperature<Extrusion Blow Molding> | 115 - 120 °C |
| Drying Time<Extrusion Blow Molding> | 4 - 6 hrs |
| Drying Time, Cumulative<Extrusion Blow Molding> | 48 hrs |
| Maximum Moisture Content<Extrusion Blow Molding> | 0.02 % |
| Minimum Moisture Content<Extrusion Blow Molding> | 1.0E-02 % |
| Melt Temperature, Parison<Extrusion Blow Molding> | 265 - 275 °C |
| Barrel - Zone 1 Temperature<Extrusion Blow Molding> | 260 - 275 °C |
| Barrel - Zone 2 Temperature<Extrusion Blow Molding> | 260 - 275 °C |
| Barrel - Zone 3 Temperature<Extrusion Blow Molding> | 260 - 275 °C |
| Barrel - Zone 4 Temperature<Extrusion Blow Molding> | 260 - 275 °C |
| Adapter - Zone 5 Temperature<Extrusion Blow Molding> |
260 - 275 °C |
| Head - Zone 6 - Top Temperature<Extrusion Blow Molding> |
260 - 275 °C |
| Head - Zone 7 - Bottom Temperature<Extrusion Blow Molding> |
260 - 275 °C |
| Screw Speed<Extrusion Blow Molding> | 15 - 50 rpm |
| Mold Temperature<Extrusion Blow Molding> | 65 - 95 °C |
| Die Temperature<Extrusion Blow Molding> | 270 - 280 °C |