Feature: | Oxidative Degradable |
---|---|
Material: | Polyamide(Nylon 6.66)/PA |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | ||||
LNP STAT-LOY 63000CT compound is based on Polycarbonate / Polyester alloy containing proprietary additives suitable for advanced semiconductor packaging applications. Added features of this grade include: LNP Clean Compounding Technology, Permanently Anti-Static, Translucent. | ||||
General | ||||
Form | Resin Pellets | |||
Filler | proprietary additives | |||
Anti-Static Low (To None) Ion ContentDiffusive Feature Lnp Clean Compound Technology |
||||
Uses | Industria | Electrical | ||
Physical | Nominal Value | Test Method | ||
Density | 1.16 g/cm³ | ASTM D792 | ||
Mold Shrinkage, Flow | 0.6 % | SABIC Method | ||
Mold Shrinkage, XFlow | 0.6 % | SABIC Method | ||
Melt Flow Rate[MFR](260 °C;2.16 kgf) | 16 g/10min | ASTM D1238 | ||
Moisture Absorption(50% RH;23 °C) | 0.7 % | ISO 62 | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Notched(23 °C) | 580 J/m | ASTM D256 | ||
Charpy Impact, Notched(23 °C) | 69 kJ/m² | ISO 179/2C | ||
Tensile Stress, Yield 5 mm/min;Type I 5 mm/min |
35 MPa 34 MPa |
ASTM D638 ISO 527 |
||
Tensile Strain, Break 5 mm/min;Type I 5 mm/min |
200 % 140 % |
ASTM D638 ISO 527 |
||
Tensile Modulus 5 mm/min 1 mm/min |
1160 MPa 1180 MPa |
ASTM D638 ISO 527 |
||
Flexural Stress, break(1.3 mm/min;50 mm;span) | 50 MPa | ASTM D790 | ||
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
1160 MPa 1140 MPa |
ASTM D790 ISO 178 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;6.4 mm 1.82 MPa;6.4 mm |
83 °C 73 °C |
ASTM D648 |
HDT/Af(1.8) | 68 °C | ISO 75/Af |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 1.0E+11 - 5.0E+12 ohms | ASTM D257 |
Volume Resistivity | 1.0E+11 - 5.0E+12 ohms·cm | ASTM D257 |
Static Decay(5000V to <50V) | < 2 Seconds | FTMS101B |
Optical | Nominal Value | Test Method |
Light Transmission(2.54 mm) | 81 % | ASTM D1003 |
Haze(2.54 mm) | 10 % | ASTM D1003 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 90 - 95 °C | |
Drying Time<Injection> | 6 - 8 hrs | |
Melt Temperature<Injection> | 230 - 250 °C | |
Nozzle Temperature<Injection> | 230 - 250 °C | |
Front, Zone 3 Temperature<Injection> | 230 - 250 °C | |
Middle, Zone 2 Temperature<Injection> | 225 - 240 °C | |
Rear, Zone 1 Temperature<Injection> | 220 - 230 °C | |
Mold Temperature<Injection> | 40 - 50 °C |