| Feature: | Oxidative Degradable |
|---|---|
| CAS No.: | 32131-17-2 |
| Formula: | (C12h22n2o2)N |
| Samples: |
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier PA66 is an unreinforced high tough polyamide 66 for injection molding
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | ||
| PA66 20G0-200S is an unreinforced, high tough polyamide 66 for injection molding. | ||
| General | ||
| Form Resin Pellets | ||
| Feature Good Thermal High Impact Abrasion Resistant | ||
| Good Electrical Properties Outdoor | ||
| Physical Nominal Value Test Method | ||
| Density, dry 1.07 g/cm³ ISO 1183 | ||
| Dry: Molding Shrinkage(4 mm) 1.9 % Internal Method | ||
| Dry: Water Absorption, Equilibrium(50% RH;23 °C) 1.7 % ISO 62 | ||
| Mechanical Nominal Value Test Method | ||
| Dry: Tensile Modulus 1600 MPa ISO 527-1 | ||
| Condition: Tensile Modulus 900 MPa ISO 527-1 | ||
| Dry: Tensile Stress 45.0 MPa ISO 527-2 | ||
| Condition: Tensile Stress 38.0 MPa ISO 527-2 | ||
| Dry: Tensile Strain, Break 40 % ISO 527-2 | ||
| Condition: Tensile Strain, Break > 50 % ISO 527-2 | ||
| Dry: Flexural Modulus 1600 MPa ISO 178 | ||
| Condition: Flexural Modulus 1050 MPa ISO 178 | ||
| Dry: Flexural Stress 60.0 MPa ISO 178 | ||
| Condition: Flexural Stress 50.0 MPa ISO 178 | ||
| Dry: Charpy Notched Impact Strength ISO 179 | ||
| -40 °C 22 kJ/m² | ||
| 23 °C 90 kJ/m² | ||
| Condition: Charpy Notched Impact Strength ISO 179 | ||
| -40 °C 20 kJ/m² | ||
| 23 °C 120 kJ/m² | ||
| Thermal | Nominal Value | Test Method |
| Dry: Deflection Temperature Under Load, Unannealed | ||
| 0.45 MPa | 135 °C | ISO 75-2/B |
| 1.8 MPa | 65.0 °C | ISO 75-2/A |
| Dry: Melting Temperature, DSC | 263 °C | ISO 3146 |
| Dry: Flame Rating | HB | UL 94 |
| Electrical | Nominal Value | Test Method |
| Dry: Volume Resistivity | 1.0e+15 ohms ·cm | IEC 60093 |
| Condition: Volume resistivity | 1.0E+13 ohms ·cm | IEC 60093 |
| Dry: Electric Strength(2 mm) | 30 kV/mm | IEC 60243-1 |
| Condition: Electric Strength(2 mm) | 36 kV/mm | IEC 60243-1 |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 80 °C | |
| Drying Time<Injection> | 4.0 hr | |
| Suggested Max Moisture<Injection> | 0.20 % | |
| Rear Temperature<Injection> | 270 - 275 °C | |
| Middle Temperature<injection> | 280 - 285 °C | |
| Front Temperature<Injection> | 285 - 290 °C | |
| Mold Temperature<Injection> | 60 - 90 °C | |
| Injection Pressure<Injection> | 35.0 - 125 MPa | |
| Injection Rate<Injection> | Moderate - Fast | |
| Back Pressure<Injection> | 0.138 - 0.345 MPa | |
| Screw Speed <Injection> | 80 - 200 rpm | |