| Feature: | Oxidative Degradable |
|---|---|
| CAS No.: | 32131-17-2 |
| Formula: | (C12h22n2o2)N |
| Samples: |
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier PA66 grade modified with 25% glass fiber for improved stiffness and strength
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | ||||||
| Starflam 525K BK0778 (formerly ECO525K BK0778) is a non-halogenated flame retardant, PA66 grade modified with 25% glass fiber for improved stiffness and strength. | ||||||
| General | ||||||
| Form Resin Pellets | ||||||
| Filler Proprietary Filler | ||||||
| Feature | Excellent Processability Corrosion Resistant Anti Aging Light-Weight |
Good Dimensional | ||||
| Uses Connector Electrical Engineering | ||||||
| Physical Nominal Value Test Method | ||||||
| Density, dry 1.40 g/cm³ ISO 1183 | ||||||
| Dry: Molding Shrinkage, Across Flow(23 °C;2 mm) 1.1 % ISO 294-4 | ||||||
| Dry: Molding Shrinkage, Flow(23 °C;2 mm) 0.30 % ISO 294-4 | ||||||
| Dry: Water Absorption(24 hr;23 °C) 1.2 % ISO 62 | ||||||
| Dry: Water Absorption, Equilibrium(50% RH;23 °C) 1.9 % ISO 62 | ||||||
| Mechanical Nominal Value Test Method | ||||||
| Dry: Tensile Modulus(23 °C) 8500 MPa ISO 527-2 | ||||||
| Condition: Tensile Modulus(23 °C) 6900 MPa ISO 527-2 | ||||||
| Dry: Tensile Stress, Break(23 °C) 127 MPa ISO 527-2 | ||||||
| Condition: Tensile Stress, Break(23 °C) 91.0 MPa ISO 527-2 | ||||||
| Dry: Tensile Strain, Break(23 °C) 2.7 % ISO 527-2 | ||||||
| Condition: Tensile Strain, Break(23 °C) 3.0 % ISO 527-2 | ||||||
| Dry: Flexural Modulus(23 °C) 9100 MPa ISO 178 | ||||||
| Condition: Flexural Modulus(23 °C) 5900 MPa ISO 178 | ||||||
| Dry: Flexural Strength(23 °C) 193 MPa ISO 178 | ||||||
| Condition: Flexural Strength(23 °C) 127 MPa ISO 178 | ||||||
| Dry: Charpy Notched Impact Strength ISO 179 1eA | ||||||
| -40 °C 8.3 kJ/m² | ||||||
| -30 °C 8.3 kJ/m² | ||||||
| 23 °C 8.9 kJ/m² | ||||||
| Condition: Charpy Notched Impact Strength | ISO 179 1eA | |||||
| -40 °C | 7.9 kJ/m² | |||||
| -30 °C | 7.6 kJ/m² | |||||
| 23 °C | 11 kJ/m² | |||||
| Dry: Charpy Unnotched Impact Strength | ISO 179 1eU | |||||
| -40 °C | 55 kJ/m² | |||||
| -30 °C | 57 kJ/m² | |||||
| 23 °C | 57 kJ/m² | |||||
| Condition: Charpy Unnotched Impact Strength | ISO 179 1eU | |||||
| -40 °C | 53 kJ/m² | |||||
| -30 °C | 53 kJ/m² | |||||
| 23 °C | 62 kJ/m² | |||||
| Dry: Notched Izod Impact Strength | ISO 180 | |||||
| -40 °C | 7.7 kJ/m² | |||||
| -30 °C | 7.8 kJ/m² | |||||
| 23 °C | 8.1 kJ/m² | |||||
| Notched Izod Impact Strength: condition | ISO 180 | |||||
| -40 °C | 7.7 kJ/m² | |||||
| -30 °C | 7.9 kJ/m² | |||||
| 23 °C | 10 kJ/m² | |||||
| Thermal | Nominal Value | Test Method | ||||
| Dry: Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa |
256 °C 237 °C |
ISO 75-2/B ISO 75-2/A |
||||
| Condition: Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa |
254 °C 228 °C |
ISO 75-2/B ISO 75-2/A |
||||
| Dry: Melting Temperature | 260 °C | ISO 11357-3 | ||||
| Dry: CLTE, Flow(23 - 55 °C;2 mm) | 2.3E-5 cm/cm/°C | ISO 11359-2 | ||||
| Dry: CLTE, Transverse(23 - 55 °C;2 mm) | 6.7E-5 cm/cm/°C | ISO 11359-2 | ||||
| Dry: Flame Rating 0.2 mm 0.4 mm 0.75 mm 1.5 mm 3 mm |
V-0 V-0 V-0 V-0 - 5VA V-0 - 5VA |
UL 94 | ||||
| Dry: Glow Wire Flammability Index 0.4 mm 0.75 mm 1.5 mm 3 mm |
960 °C 960 °C 960 °C 960 °C |
IEC 60695-2-12 | ||||
| Electrical | Nominal Value | Test Method | ||||
| Dry: Dielectric Strength(1 mm) | 42 kV/mm | IEC 60243 | ||||
| Dry: Comparative Tracking Index(3 mm) | > 600 V | IEC 60112 | ||||
| Dry: High Amp Arc Ignition, HAI 0.4 mm 0.75 mm 1.5 mm 3 mm |
PLC 0 PLC 0 PLC 0 PLC 0 |
UL 746A | ||||
| Dry: Hot-wire Ignition, HWI 0.4 mm 0.75 mm 1.5 mm 3 mm |
PLC 2 PLC 1 PLC 0 PLC 0 |
UL 746A | ||||
| Processing | Nominal Value | |||||
| Drying Temperature<Injection> | < 80 °C | |||||
| Drying Time<Injection> | 4.0 - 6.0 hr | |||||
| Rear Temperature<Injection> | 275 - 300 °C | |||||
| Middle Temperature<injection> | 275 - 300 °C | |||||
| Front Temperature<Injection> | 275 - 300 °C | |||||
| Nozzle Temperature<Injection> | 275 - 300 °C | |||||
| Processing Temp, Melt<Injection> | 275 - 300 °C | |||||
| Mold Temperature<Injection> | 60 - 120 °C | |||||