Audited Supplier THERMOCOMP UX08325 compound is Polyphthalamide (PPA) resin containing glass fiber
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | ||||
| LNP THERMOCOMP UX08325 compound is based on Polyphthalamide (PPA) resin containing 30% glass fiber. Added features of this grade include: Improved Plating Surface and Mechanical Performance suitable for Laser Direct Structuring (LDS) applications, SMT Process capable. | ||||
| General | ||||
| Form | Resin Pellets | |||
| Filler | ||||
Feature |
||||
| Good Thermal Good Hardness | Circuit Solution | |||
| Lds | ||||
| UL Yellow Card | E207780- 101334270 | |||
Uses |
Automotive Printed Circuit Boards |
Consumer Electrical |
Laser Direct Structuring | |
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.55 g/cm³ | ASTM D792 | ||
| Mold Shrinkage, Flow | 0.41 % | Method | ||
| Mold Shrinkage, XFlow | 0.52 % | Method | ||
| Moisture Absorption(50% RH;23 °C) | 0.53 % | ISO 62 | ||
| Mechanical | Nominal Value | Test Method | ||
| Izod Impact, Unnotched(23 °C) | 351 J/m | ASTM D4812 | ||
| Izod Impact, Notched | ||||
| 23 °C | 31 J/m | ASTM D256 | ||
| 80*10*4;23 °C | 2 kJ/m² | ISO 180/1A | ||
| Tensile Stress, Break | ||||
| 5 mm/min;Type I | 135 MPa | ASTM D638 | ||
| 5 mm/min | 125 MPa | ISO 527 | ||
| Tensile Strain, Break | ||||
| 5 mm/min;Type I | 1.8 % | ASTM D638 | ||
| 5 mm/min | 1.6 % | ISO 527 | ||
| Tensile Modulus | ||||
| 5 mm/min | 1.1E+04 MPa | ASTM D638 | ||
| 1 mm/min | 1.1E+04 MPa | ISO 527 | ||
| Flexural Stress, Yield | ||||
| 1.3 mm/min;50 mm;span | 197 MPa | ASTM D790 | ||
| 2 mm/min | 194 MPa | ISO 178 | ||
| Flexural Stress, break(1.3 mm/min;50 mm;span) | 194 MPa | ASTM D790 | ||
| Flexural Modulus | ||||
| 1.3 mm/min;50 mm;span | 9770 MPa | ASTM D790 | ||
| 2 mm/min | 9610 MPa | ISO 178 | ||
| Flexural Strain, Break(2 mm/min) | 2 % | ISO 178 | ||
| Thermal | Nominal Value | Test Method | ||
| UL Recognized(≥ 1.5 mm) | HB | UL 94 | ||
| Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 263 °C | ASTM D648 | ||
| CTE, Flow(-40 - 40 °C) | 2.2e-05 1/°C | ASTM E831 | ||
| CTE, XFlow(-40 - 40 °C) | 5.4E-05 1/°C | ASTM E831 | ||
| HDT/Af(1.8) | 261 °C | ISO 75/Af | ||
| Electrical | Nominal Value | Test Method | ||
| Relative Permittivity(1.0e+9 Hz) | 4.2 | ASTM D150 | ||
| Dissipation Factor(1.0e+9 Hz) | 1.0E-02 | ASTM D150 | ||
| Processing | Nominal Value | |||
| Drying Temperature<Injection> | 120 - 150 °C | |||
| Drying Time<Injection> | 4 hrs | |||
| Maximum Moisture Content<Injection> | 0.15 % | |||
| Melt Temperature<Injection> | 315 - 330 °C | |||
| Front, Zone 3 Temperature<Injection> | 325 - 340 °C | |||
| Middle, Zone 2 Temperature<Injection> | 315 - 325 °C | |||
| Rear, Zone 1 Temperature<Injection> | 310 - 320 °C | |||
| Mold Temperature<Injection> | 140 - 165 °C | |||
| Back Pressure<Injection> | 0.2 - 0.3 MPa | |||
| Screw Speed <Injection> | 30 - 60 rpm | |||