Product Description |
50% glass fiber reinforced PA66, Heat stabilized & lubricated FEATURES: High strength & rigidity Good dimensional stability Good surface appearance APPLICATIONS: Auto wing mirror base Household appliance's parts |
General |
Form Resin Pellets |
Filler 50 % Glass Fiber |
|
Feature |
High Mechanical Strength A d Ri idit |
Internally Lubricated |
n g y |
Uses Appliance Components Automotive Exterior |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.55 g/cm³ ISO 1183 |
Molding Shrinkage 0.20 - 0.50 % ISO 2577 |
Water Absorption, Equilibrium(50% RH;23 °C) 1.3 % ISO 62 |
Mechanical Nominal Value Test Method |
Tensile Stress 215 MPa ISO 527-2/10 |
Tensile Strain, Break 2.1 % ISO 527-2/10 |
Flexural Modulus(2 mm/min) 14500 MPa ISO 178 |
Flexural Stress(2 mm/min) 305 MPa ISO 178 |
Notched Izod Impact Strength(23 °C) 14 kJ/m² ISO 180/1A |
Thermal Nominal Value Test Method |
Heat Deflection Temperature, Unannealed |
0.45 MPa 260 °C ISO 75-2/B |
1.8 MPa 250 °C ISO 75-2/A |
Flame Rating HB UL 94 |
Electrical Nominal Value Test Method |
Volume Resistivity 1.0e+15 ohms ·cm IEC 60093 |
Processing |
Nominal Value |
Drying Temperature<Injection> |
90 - 110 °C |
Drying Time<Injection> |
2.0 - 4.0 hr |
Rear Temperature<Injection> |
230 - 250 °C |
Middle Temperature<injection> |
260 - 280 °C |
Front Temperature<Injection> |
270 - 300 °C |
Processing Temp, Melt<Injection> |
240 - 300 °C |
Mold Temperature<Injection> |
60 - 90 °C |
Injection Rate<Injection> |
Moderate-Fast |