Poly Butylene Terephthalate (PBT) 30% Glass Fiber PBT Stiffness and Dimensional Stability

• Feature: Plastics
• CAS No.: 63440-93-7
• Formula: C24h24o8
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PBT-WF006
• EINECS: 618-371-8
• Material: Polybutylene Terephthalate/PBT
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Natural Color
• Place of Origin: Guangdong, China
• Use: Radiator Front Cover.Automotive Parts
• Features: Lubricated, Good Wear Resistance, Low Friction and
• Application: Zippers Irish Flutes, Bagpipes, Practice Chanters
• Form: Resin Pellets
• Delivery Time: in 7 Days
• Applications: Appliance Handles, Spotlights, Electric Motors.
• Glass Fiber: 15%
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Poly butylene terephthalate (PBT) 30% glass fiber PBT Stiffness and Dimensional Stability
   

  
 

Product Description
LNP ELCRIN WF006XiQ compound is based on Poly butylene terephthalate (PBT) resin utilizing ELCRIN iQ upcycling technology containing minimum 37% Post-Consumer Recycling (PCR) weight content and 30% glass fiber. Added features of this grade include: Excellent Strength, Stiffness and Dimensional Stability. Potential applications may include handles, connectors.
General
Form                                        Resin Pellets
Filler                                         30 % Glass Fiber
Feature	Good Dimensional   Pcr	Good Hardness                 37 % Pcr
Uses	Automotive   Electrical	Connector                         Consumer
Physical                                                                                 Nominal Value                                       Test Method
Density / Specific Gravity 1.54                                                        ASTM D792 1.54 g/cm³                                            ISO 1183
Water Absorption
24 hrs;23 °C                                                                         0.1 %                                                       ASTM D570
23 °C;saturated                                                                  0.09 %                                                    ISO 62-1
Mold Shrinkage, Flow(3.2 mm)                                           0.5 - 0.7 %                                               SABIC Method
Mold Shrinkage, XFlow(3.2 mm)                                         0.8 - 1 %                                                  SABIC Method
Melt Flow Rate[MFR](250 °C;5 kgf)                                     52 g/10min                                             ASTM D1238
Moisture Absorption(50% RH;23 °C)                                  0.1 %                                                       ISO 62
Melt Volume Rate, MVR(5 kg;MVR at 250 °C)                     38 cm³/10 min                                       ISO 1133

 

Mechanical	Nominal Value	Test Method
Izod Impact, Unnotched(23 °C)	770 J/m	ASTM D4812
Izod Impact, Notched
23 °C	82 J/m	ASTM D256
-30 °C	83 J/m	ASTM D256
80*10*4;23 °C	8 kJ/m²	ISO 180/1A
80*10*4;-30 °C	8 kJ/m²	ISO 180/1A
Instrumented Dart Impact, Total Energy(23 °C)	7 J	ASTM D3763
C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0)	14 kJ/m²	ISO 179 1eA
Tensile Stress, Yield
5 mm/min;Type I	114 MPa	ASTM D638
5 mm/min	139 MPa	ISO 527
Tensile Stress, Break
5 mm/min;Type I	114 MPa	ASTM D638
5 mm/min	139 MPa	ISO 527
Tensile Strain, Yield
5 mm/min;Type I	2.2 %	ASTM D638
5 mm/min	1.6 %	ISO 527
Tensile Strain, Break
5 mm/min;Type I	2.2 %	ASTM D638
5 mm/min	1.6 %	ISO 527
Tensile Modulus
5 mm/min	1.2E+04 MPa	ASTM D638
1 mm/min	1.1E+04 MPa	ISO 527
Flexural Stress, Yield
1.3 mm/min;50 mm;span	210 MPa	ASTM D790
2 mm/min	210 MPa	ISO 178
Flexural Stress, break(1.3 mm/min;50 mm;span)	189 MPa	ASTM D790
Flexural Modulus
1.3 mm/min;50 mm;span	9100 MPa	ASTM D790
2 mm/min	9100 MPa	ISO 178

 

Thermal	Nominal Value	Test Method
Heat Deflection Temperature[HDT], Unannealed 3.2 mm;1.82 MPa 1.82 MPa;6.4 mm	203 °C 207 °C	ASTM D648
CTE, Flow
-40 - 40 °C	2.5e-05 1/°C	ASTM E831
-40 - 40 °C	2.5e-05 1/°C	ISO 11359-2
CTE, XFlow
-40 - 40 °C	8.9e-05 1/°C	ASTM E831
-40 - 40 °C	8.9e-05 1/°C	ISO 11359-2
Ball Pressure Test, Approximate Maximum	200 °C	IEC 60695-10-2
HDT/Bf(0.45)	217 °C	ISO 75/Bf
Electrical	Nominal Value	Test Method
Volume Resistivity	> 1E+15 ohms ·cm	ASTM D257
Dielectric Strength, in Air(3.2 mm)	23 kV/mm	ASTM D149
Processing		Nominal Value
Drying Temperature<Injection>		120 °C
Drying Time<Injection>		3 - 4 hrs
Drying Time, Cumulative<Injection>		12 hrs
Maximum Moisture Content<Injection>		0.02 %
Melt Temperature<Injection>		250 - 265 °C
Nozzle Temperature<Injection>		245 - 265 °C
Front, Zone 3 Temperature<Injection>		250 - 265 °C
Middle, Zone 2 Temperature<Injection>		245 - 260 °C
Rear, Zone 1 Temperature<Injection>		240 - 255 °C
Mold Temperature<Injection>		65 - 90 °C
Back Pressure<Injection>		0.3 - 0.7 MPa
Screw Speed <Injection>		50 - 80 rpm
Shot To Cylinder Size<Injection>		40 - 80 %
Vent Depth <Injection>		0.025 - 0.038 mm

      

Company Profile

Product Parameters

Our Customers

Our Certificates

 

Our Production

Our Package/Shipping

Our Advantages

 

Our Samples

 

Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.

Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.

With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry