Product Description | |||||||
LNP THERMOCOMP DX11355 compound is based on Polycarbonate (PC) resin containing proprietary fillers and available in black color only. Added features of this grade include: Improved Plating Surface and Mechanical Performance suitable for Laser Direct Structuring (LDS) applications, Improved Impact, Non-Brominated, Non- Chlorinated Flame Retardant. |
|||||||
General | |||||||
Form | Resin Pellets | ||||||
Feature |
Non-Brominated & Non- Chlorinated Flame Retardant |
Non-Chlorinated Colorable Lds |
Enhanced Ductility Circuit Solution |
||||
UL Yellow Card | E207780-101214685 | ||||||
Uses | Automotive Electrical |
Consumer Laser Direct Structuring | |||||
Physical | Nominal Value | Test Method | |||||
Density / Specific Gravity | 1.27 g/cm³ | ASTM D792 | |||||
Moisture Absorption(23 °C;50% RH/24 hrs) | 1.0E-02 % | ASTM D570 | |||||
Mold Shrinkage, Flow(24 hrs) | 0.5 % | ASTM D955 | |||||
Mold Shrinkage, XFlow(24 hrs) | 0.5 % | ASTM D955 | |||||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 12 g/10min | ASTM D1238 | |||||
Mechanical | Nominal Value | Test Method | |||||
Izod Impact, Notched | ASTM D256 | ||||||
23 °C | 800 J/m | ||||||
-30 °C | 167 J/m | ||||||
Izod Impact, Unnotched(-30 °C) | 2120 J/m | ASTM D4812 | |||||
Tensile Stress, Yield(50 mm/min;Type I) | 58 MPa | ASTM D638 | |||||
Tensile Stress, Break(50 mm/min;Type I) | 52 MPa | ASTM D638 | |||||
Tensile Strain, Yield(50 mm/min;Type I) | 5.4 % | ASTM D638 | |||||
Tensile Strain, Break(50 mm/min;Type I) | 70 % | ASTM D638 | |||||
Tensile Modulus(50 mm/min) | 2600 MPa | ASTM D638 | |||||
Flexural Stress, Yield(1.3 mm/min;50 mm;span) | 90 MPa | ASTM D790 | |||||
Flexural Stress, break(1.3 mm/min;50 mm;span) | 89 MPa | ASTM D790 | |||||
Flexural Modulus(1.3 mm/min;50 mm;span) | 2400 MPa | ASTM D790 | |||||
Thermal | Nominal Value | Test Method | |||||
UL Recognized(≥ 0.6 mm) | V-0 | UL 94 | |||||
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 114 °C | ASTM D648 | |||||
CTE, Flow(-40 - 40 °C) | 6.2e-05 1/°C | ASTM E831 | |||||
CTE, XFlow(-40 - 40 °C) | 6.7e-05 1/°C | ASTM E831 | |||||
Relative Temp Index, Elec | 80 °C | UL 746B | |||||
Relative Temp Index, Mechanical with Impact | 80 °C | UL 746B | |||||
Relative Temp Index, Mechanical without Impact | 80 °C | UL 746B | |||||
Electrical | Nominal Value | Test Method | |||||
Relative Permittivity(1.0e+9 Hz) | 2.92 | IEC 60250 | |||||
Dissipation Factor(1.0e+9 Hz) | 7.0E-03 | IEC 60250 | |||||
Processing | Nominal Value | ||||||
Drying Temperature<Injection> | 100 - 110 °C | ||||||
Drying Time<Injection> | 3 - 4 hrs | ||||||
Drying Time, Cumulative<Injection> | 8 hrs | ||||||
Maximum Moisture Content<Injection> | 0.02 % | ||||||
Melt Temperature<Injection> | 275 - 300 °C | ||||||
Nozzle Temperature<Injection> | 275 - 300 °C | ||||||
Front, Zone 3 Temperature<Injection> | 260 - 300 °C | ||||||
Middle, Zone 2 Temperature<Injection> | 255 - 295 °C | ||||||
Rear, Zone 1 Temperature<Injection> | 250 - 290 °C | ||||||
Hopper Temperature<Injection> | 60 - 80 °C | ||||||
Mold Temperature<Injection> | 60 - 90 °C | ||||||
Back Pressure<Injection> | 0.3 - 0.7 MPa | ||||||
Screw Speed <Injection> | 40 - 70 rpm | ||||||
Shot To Cylinder Size<Injection> | 30 - 80 % | ||||||
Vent Depth <Injection> | 0.038 - 0.076 mm |