Heat Conducting ABS Engineering Plastics High Temperature Flame Retardant

• Feature: Plastics
• CAS No.: 25766-59-0
• Formula: C6h4c(CH3)2c6h4oco2-]N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: ABS-765-B
• EINECS: 618-371-8
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Form: Resin Pellets
• Chemical Substances: Polycarbonate
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Heat Conducting ABS Engineering Plastics High Temperature Flame Retardant

Product Description

Product Description
Features: Good Flow; 1.5mm V-2; 2.5mm V-0; 2.5mm 5VB; 3.0mm 5VA (TBBA series) Applications: Displays; Chassis; Modems; Power Panels; Power Outlets; Car Batteries; Cash Register Housings ; printer enclosures; remote controls; light boxes; fax machines; projectors; large MFPs; coffee makers; TV front and rear frames and car audio  consoles Impact Resistant
General
Form	Resin Pellets
Feature	Excellent Processability	Medium Impact Resistance
UL Yellow Card                         E56070-565070
Batteries                            Displays                             Housing
Light Covers                      Printer Parts                       Panel
Printer Chassis                    Audio Speaker				Remote Controls
omponen s                     Coffee Machine
Physical                                                                                 Nominal Value                                       Test Method
Density / Specific Gravity(23 °C)                                          1.16 g/cm³                                             ISO 1183
Melt Volume-Flow Rate, MVR(220 °C;10 kg)                      44 cm³/10 min                                       ISO 1133
Molding Shrinkage                                                              0.30 - 0.60 %                                          ISO 294-4
Mechanical                                                                            Nominal Value                                      Test Method
Tensile Strength, Yield(50 mm/min)                                   39.0 MPa                                                ISO 527-2/50
Tensile Strength, Break(50 mm/min)                                  30.0 MPa                                                ISO 527-2/50
Tensile Elongation, Break(50 mm/min)                               10 %                                                       ISO 527-2/50
Flexural Modulus(2 mm/min)                                              1800 MPa                                               ISO 178
Flexural Strength(2 mm/min)                                              57.0 MPa                                                 ISO 178
C harpy Notched Impact Strength                                                                                                      ISO 179
-30 °C                                                                                    11 kJ/m²
23 °C                                                                                     25 kJ/m²
Notched Izod Impact                                                                                                                         ISO 180/1A
-30 °C                                                                                    11 kJ/m²
23 °C                                                                                     24 kJ/m²
Thermal                                                                                Nominal Value					Test Method
Deflection Temperature Under Load, Unannealed(1.8 MPa)			77.0 °C		ISO 75-2/A
Deflection Temperature Under Load, Annealed(1.8 MPa)			85.0 °C		ISO 75-2/A
Vicat Softening Temperature
5 kg;50 ºC/hr			80.0 °C		ISO 306/B50
50 ºC/hr;1 kg			94.0 °C		ISO 306/A50
CLTE, Flow			8.55E-5		ISO 11359-2
Flame Rating 1.5 mm 2.5 mm 2.5 mm 3 mm			V-2 V-0 5VB 5VA		UL 94
Processing					Nominal Value
Drying Temperature<Injection>					80 - 85 °C
Drying Time<Injection>					2.0 - 4.0 hr
Rear Temperature<Injection>					180 - 210 °C
Middle Temperature<injection>					190 - 220 °C
Front Temperature<Injection>					190 - 220 °C
Mold Temperature<Injection>					40 - 70 °C
Injection Rate<Injection>					Slow-Moderate
Back Pressure<Injection>					0.5 - 1 MPa
Injection Pressure<Injection>					50 - 60 %
Holding Pressure<Injection>					40 - 50 %

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....