PPA BK337 is a 45% Glass Reinforced, Flame Retardant, High Performance Polyamide
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | |||
HTNFR52G45NHF BK337 is a 45% Glass Reinforced, Flame Retardant, High Performance Polyamide with improved flow. It is also a PPA resin and it uses a non-halogenated flame retardant. | |||
General | |||
Form Resin Pellets | |||
Filler 45 % Glass Fiber | |||
Feature Chlorinated Flame | |||
Retardant | |||
UL Yellow Card E41938-102212557 | |||
Physical Nominal Value Test Method | |||
Resin ID PA(6T/66)-GF45FR (40) ISO 1043 | |||
Part Marking Code, ISO 11469 PA(6T/66)-GF45FR (40) ISO 11469 | |||
Part Marking Code >PPA-GF45FR SAE J1344 | |||
Density / Specific Gravity 1.61 g/cm³ ISO 1183 | |||
Dry: Molding Shrinkage, Across Flow 0.60 % | ISO 294-4, ISO 2577 | ||
Dry: Molding Shrinkage, Flow 0.20 % | ISO 294-4, ISO 2577 | ||
Mechanical Nominal Value Test Method | |||
Dry: Tensile Modulus 15700 MPa ISO 527-1/-2 | |||
Dry: Tensile Stress, Break 174 MPa ISO 527-1/-2 | |||
Dry: Tensile Strain, Break 1.8 % ISO 527-1/-2 | |||
Dry: Flexural Modulus 15600 MPa ISO 178 | |||
Dry: Flexural Stress 255 MPa ISO 178 | |||
Dry: Charpy Notched Impact Strength ISO 179 1eA | |||
-30 °C 8.0 kJ/m² | |||
23 °C 8.0 kJ/m² | |||
Dry: Charpy Unnotched Impact Strength ISO 179 1eU | |||
-30 °C 45 kJ/m² | |||
23 °C 47 kJ/m² | |||
Dry: Poisson's Ratio 0.33 | |||
Thermal | Nominal Value | Test Method | |
Dry: Heat Deflection Temperature, Unannealed(1.8 | MPa) 283 °C | ISO 75-1/-2 | |
Dry: Melting Temperature(First Heat) | 310 °C | ISO 11357-1/-3 | |
Dry: CLTE, Flow -40 - 23 °C 55 - 160 °C |
1.7E-5 cm/cm/°C 1.5E-5 cm/cm/°C 1.5E-5 cm/cm/°C |
ISO 11359-1/-2 ISO 11359-2 ISO 11359-2 |
|
Dry: CLTE, Transverse -40 - 23 °C 55 - 160 °C |
5.5E-5 cm/cm/°C 5.0E-5 cm/cm/°C 9.5E-5 cm/cm/°C |
ISO 11359-1/-2 ISO 11359-2 ISO 11359-2 |
|
RTI Elec 0.4 mm 3 mm |
140 °C 140 °C |
UL 746B | |
Dry: RTI Elec 0.75 mm 1.5 mm |
140 °C 140 °C |
UL 746B | |
RTI, strength 0.75 mm 3 mm |
125 °C 130 °C |
UL 746B | |
Dry: RTI, strength(1.5 mm) | 125 °C | UL 746B | |
Dry: Burning Behav. at thickness h(0.4 mm) | V-0 | IEC 60695-11-10 | |
Flammability(0.4 mm) | V-0 | UL 94 | |
Processing | Nominal Value | ||
Drying Temperature<Injection> | 100 °C | ||
Drying Time - Desiccant Dryer<Injection> | 6.0 - 8.0 hr | ||
Suggested Max Moisture<Injection> | 0.10 % | ||
Processing Temp, Melt<Injection> | 320 - 325 °C | ||
Mold Temperature<Injection> | 90 - 130 °C | ||
Drying Recommended <Injection> | YES |