Product Description | ||||
Global grade. LEXAN LUX2110T is an injection moulding grade especially designed for manufacturing optical parts requiring easy flow properties combined with very high transmission and color stability. | ||||
General | ||||
Form | Resin Pellets | |||
Feature | Excellent Processability | High Clarity | ||
UL Yellow Card | E121562-102070825 | |||
Uses Lighting Applications Electronic Displays Constraction | ||||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.20 g/cm³ | ASTM D792 | ||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 19 g/10min | ASTM D1238 | ||
Molding Shrinkage, Flow, Tensile Bar | 0.60 - 0.90 % | Internal Method | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus(50 mm/min) | 2220 MPa | ASTM D638 | ||
Tensile Strength, Yield(50 mm/min;Type I) | 60.0 MPa | ASTM D638 | ||
Tensile Strength, Break(50 mm/min;Type I) | 68.0 MPa | ASTM D638 | ||
Tensile Elongation, Yield(50 mm/min;Type I) | 7.0 % | ASTM D638 | ||
Tensile Elongation, Break(50 mm/min;Type I) | 140 % | ASTM D638 | ||
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2360 MPa | ASTM D790 | ||
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | > 96.0 MPa | ASTM D790 | ||
Notched Izod Impact | ASTM D256 | |||
-30 °C | 140 J/m | |||
23 °C | 790 J/m | |||
Unnotched Izod Impact(23 °C) | 2100 J/m | ASTM D4812 | ||
Instrumented Dart Impact, Energy at Peak(23 °C) | 72.0 J | ASTM D3763 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Under Load, Unannealed | ASTM D648 | |||
0.45 MPa;3.2 mm | 142 °C | |||
1.8 MPa;3.2 mm | 129 °C | |||
Vicat Softening Temperature | 145 °C | ISO 306/B120 | ||
CLTE, Flow(-40 - 95 °C) | 6.5E-5 cm/cm/°C | ASTM E831 | ||
CLTE, Transverse(-40 - 95 °C) | 6.4E-5 cm/cm/°C | ASTM E831 |
Optical | Nominal Value | Test Method |
Transmittance (2.5e+3 µm) | > 90.0 % | ASTM D1003 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Suggested Shot Size<Injection> | 40 - 60 % | |
Rear Temperature<Injection> | 270 - 295 °C | |
Middle Temperature<injection> | 280 - 305 °C | |
Front Temperature<Injection> | 295 - 315 °C | |
Nozzle Temperature<Injection> | 290 - 310 °C | |
Processing Temp, Melt<Injection> | 295 - 315 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Vent Depth <Injection> | 0.025 - 0.076 mm | |
Drying Time, Cumulative<Injection> | 48 hrs |