POM Xgc25 Is a Polyacetalcopolymer Reinforced with Approx. 25% Glass Fibres

• Customization: Available
• Feature: Resin Pellets
• CAS No.: 25037-45-0
• Model NO.: POM-XGC25
• EINECS: 25037-45-0
• Material: Polyacetal/POM
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Place of Origin: Guangdong, China
• Use: Fully Automatic Coffee Brewers; Knife Handles
• Features: Lubricated, Good Wear Resistance, Low Friction and
• Application: Zippers Irish Flutes, Bagpipes, Practice Chanters
• Form: Resin Pellets
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 50.00cm * 15.00cm
• Package Gross Weight: 25.000kg

Product Description

XGC25 is a Polyacetalcopolymer reinforced with approx. 25% glass fibres
 
  
 

Product Description
Hostaform® XGC25 is a Polyacetalcopolymer reinforced with approx. 25% glass fibres. Compared to the Hostaform® C 9021 GV 1/30 Hostaform® XGC25 has a higher strength.
General
Form	Resin Pellets
Filler	25 % Glass Fiber
Physical		Nominal Value	Test Method
Density / Specific Gravity		1.59 g/cm³	ISO 1183
Melt Volume-Flow Rate, MVR(190 °C;5 kg)		4.8 cm³/10 min	ISO 1133
Molding Shrinkage, Across Flow		0.95 %	ISO 294-4
Molding Shrinkage, Flow		0.60 %	ISO 294-4
Mechanical		Nominal Value	Test Method
Tensile Modulus		9000 MPa	ISO 527-2/1A/1
Tensile Stress, Break		155 MPa	ISO 527-2/1A/5
Tensile Strain, Break		3.5 %	ISO 527-2/1A/5
Flexural Modulus(23 °C)		8300 MPa	ISO 178
Charpy Notched Impact Strength			ISO 179 1eA
-30 °C		11 kJ/m²
23 °C		13 kJ/m²
Charpy Unnotched Impact Strength(23 °C)		70 kJ/m²	ISO 179 1eU
Thermal		Nominal Value	Test Method
Heat Deflection Temperature, Unannealed(1.8 MPa)		161 °C	ISO 75-2/A
Melting Point(10 °C/min)		166 °C	ISO 11357-3
CLTE, Flow		3.0E-5 cm/cm/°C	ISO 11359-2
CLTE, Transverse		6.0E-5 cm/cm/°C	ISO 11359-2

 

Processing	Nominal Value
Drying Temperature<Injection>	100 - 120 °C
Drying Time<Injection>	3.0 - 4.0 hr
Suggested Max Moisture<Injection>	0.15 %
Hopper Temperature<Injection>	20 - 30 °C
Rear Temperature<Injection>	170 - 180 °C
Middle Temperature<injection>	180 - 190 °C
Front Temperature<Injection>	190 - 200 °C
Nozzle Temperature<Injection>	190 - 210 °C
Processing Temp, Melt<Injection>	190 - 210 °C
Mold Temperature<Injection>	80 - 120 °C
Injection Pressure<Injection>	60.0 - 120 MPa
Injection Rate<Injection>	Slow
Holding Pressure<Injection>	60.0 - 120 MPa
Back Pressure<Injection>	0.00 - 2.00 MPa
Manifold Temperature<Injection>	190 - 210 °C
Zone 4 Temperature<Injection>	190 - 210 °C
Feed Temperature<Injection>	60 - 80 °C

Company Profile

Product Parameters

 

Product Description
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation.
General
Form	Resin	Pellets
Physical			Nominal Value	Test Method
Density / Specific Gravity			1.40 g/cm³
Water Absorption			0.21 %	ASTM D570
Moisture Absorption at Equilibrium			0.80 %	ASTM D570
Linear Mold Shrinkage			2.2 %
Linear Mold Shrinkage, Transverse			1.8 %
Hardness, Rockwell R			111	ASTM D785
Mechanical			Nominal Value	Test Method
Tensile Strength, Yield			37.0 MPa	ASTM D638
Elongation at Break			30 %	ASTM D638
Flexural Strength			52.0 MPa	ASTM D790
Flexural Modulus			2100 MPa	ASTM D790
Compressive Strength			66.0 MPa	ASTM D695
Shear Strength			40.0 MPa	ASTM D732
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C			50 J/m 30 J/m	ASTM D256
Thermal			Nominal Value	Test Method
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa			152 °C 106 °C	ASTM D648
Flammability, UL94			HB	UL 94

 

Our Customers

Our Certificates

 

Our Production

Our Package/Shipping

Our Advantages

 

Our Samples

 

Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.

Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.

With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry.