Implant Peek Pellet for Neurosurgery and Maxillofacial Repair Chemical Machinery DIY

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PEEK-550G
• EINECS: 211-024-8
• Material: Peek
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Place of Origin: China
• Brand Name: Forever
• Processing Mode: Injection Molding/Extrusion
• Product Name: Implantable Peek Granule
• Grade: Medical Implantable Grade
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 0%-60% Glass Fiber/Mineral/Carbon Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Implant PEEK Pellet for Neurosurgery and Maxillofacial Repair Chemical Machinery Diy
 PEEK

Product Description

Product Description
Features: Corrosion resistance, flame retardancy, low smoke resistance, abrasion resistance, wave permeability,     excellent electrical insulation properties, high toughness, Applications: Multifilament, Monofilament, Screws, Seal Rings, Bearings, Circuit Boards
General
Form                                        Resin Pellets
Ductile                               Fda                                     Low Smoke
Insulating                                          Transparent To  Microwave
Uses	Bcf Multifilaments   Industrial Parts		Bearings     Monofilaments	Seals     Printed Circuit Boards
Physical                                                                                 Nominal Value                                       Test Method
Density / Specific Gravity                                                                                                                    ISO 1183
Crystalline                                                                           1.3 g/cm³
Amorphous                                                                        1.26 g/cm³
Durometer Hardness, Shore D(23 ºC)                                  85                                                           ISO 868
Water Absorption at Saturation(23 ºC;3.2 mm;by immersion;thick Tensile Bar)			0.07 %                                                    ISO 62-1
Water Absorption at Equilibrium(23 ºC;3.2 mm;by immersion;thick Tensile Bar)			0.4 %                                                      ISO 62-1
Mold Shrinkage, MD                                                            1 %                                                          ISO 294-4
Mold Shrinkage, TD                                                             1.3 %                                                       ISO 294-4
Melt Flow Rate[MFR](5 kg;380 ºC)                                       20 g/10 min                                           ISO 1133
Mechanical                                                                            Nominal Value                                      Test Method
Tensile Strength, Break(23 ºC)                                             100 MPa                                                 ISO 527
Elongation at Yield(23 ºC)                                                    40 %                                                       ISO 527
Flexural Strength(23 ºC)                                                       170 MPa                                                 ISO 178
Flexural Modulus(23 ºC)                                                       4200 MPa                                              ISO 178
Compressive Strength(23 ºC)                                               125 MPa
C harpy Impact Strength, Notched                                      6 kJ/m²                                                   ISO 604
Notched Izod Impact Strength                                            6.5 kJ/m²                                                ISO 180
Mold Shrinkage, TD                                                             1.3 %                                                       ISO 294-4
Thermal		Nominal Value			Test Method
Melting Point		343 °C			ISO 11357
Glass Transition Temp, Tg(onset)		143 °C			ISO 11357
Specific Heat Capacity(23 ºC)		2.2 kg/ºC			DSC
CTE, Flow		45 ppm/K			ISO 11359
CLTE, Transverse		120 ppm/K			ISO 11359
Deflection Temperature(1.8 MPa)		152 °C			ISO 75-f
Thermal Conductivity(23 ºC)		0.29 W/m-K			ISO 22007-4
Electrical		Nominal Value			Test Method
Dielectric Strength(2mm)		23 kV/mm			IEC 60243-1
Comparative Tracking Index		150 V			IEC 60112
Dielectric Constant 23 ºC;1.0e+3 Hz 50 Hz;23 ºC		3.2 4.5			IEC 60250
Dielectric Loss - Tangent(23 ºC;1.0e+6 Hz)		0.003			IEC 60250
Volume Resistivity 23 ºC;1 V 275 ºC		1.0E+16 ohms ·cm 1.0E+9 ohms ·cm			IEC 60093

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 