Feature: | Plastics |
---|---|
Material: | Acrylonitrile-Butadiene-Styrene Copolymers/ABS |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | |||
High Flow Grade, Jet Black Grade CHARACTERISTICS: Jet black, High flow | |||
General | |||
Form | Resin Pellets | ||
Feature Excellent Processability Ec 1907/2006 (Reach) | |||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity 23 °C 23 °C |
1.04 g/cm³ 1.04 g/cm³ |
ASTM D792 ISO 1183 |
|
Melt Mass-Flow Rate, MFR | ASTM D1238;ISO | ||
1133 | |||
200 °C;5 kg | 4.0 g/10min | ||
220 °C;10 kg | 40 g/10min | ||
Rockwell Hardness, R-Scale(23 °C) | 105 | ASTM D785;ISO 2039-2 |
|
Mechanical | Nominal Value | Test Method | |
Tensile Strength(23 °C) | 43.0 MPa | ASTM D638;ISO 527-2 |
|
Flexural Modulus(23 °C) | 2450 MPa | ASTM D790;ISO 178 |
|
Flexural Strength(23 °C) | 75.0 MPa | ASTM D790;ISO 178 |
|
Unnotched Izod Impact(23 °C;6.35 mm) | 190 J/m | ASTM D256 | |
Thermal | Nominal Value | Test Method | |
Deflection Temperature Under Load, Unannealed(1.8 MPa;12 7 mm) | 84.0 °C | ISO 75-2/A;ASTM D648 |
|
Deflection Temperature Under Load, Annealed(1.8 MPa;80 °C;8 hr) | 94.0 °C | ISO 75-2/A;ASTM D648 |
|
Vicat Softening Temperature(10 N;Loading 1) | 100 °C | ASTM D1525;ISO 306/A | |
Flame Rating, Black(1.5 mm) | HB | UL 94 |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |