CAS No.: | 9002-98-6 |
---|---|
Formula: | C39h30n2o6 |
EINECS: | 205-793-9 |
Samples: |
BAG
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | |||||||||||
ULTEM MD131AR Resin is an unreinforced amorphous polyetherimide (PEI) resin that may offer a high glass transition temperature (Tg) of 217°C and global food compliance, improve food sticking. Features are excellent mechanical, electrical and dimensional properties up to high temperatures. The material may offer very good chemical resistance for an amorphous material. The material is available in opaque colors. | |||||||||||
General | |||||||||||
Form | Resin Pellets | ||||||||||
Feature | Chemical Resistant Good Thermal | Fda Good Colorability |
Good Dimensional Stain Resistant |
||||||||
Uses Appliances | 3d Printing | Non-specific Food Applications |
|||||||||
Physical | Nominal Value | Test Method | |||||||||
Density / Specific Gravity | 1.27 g/cm³ | ASTM D792;ISO 1183 | |||||||||
Melt Mass-Flow Rate, MFR(337 °C;6.6 kg) | 18 g/10min | ASTM D1238 | |||||||||
Melt Volume-Flow Rate, MVR | ISO 1133 | ||||||||||
5 kg;340 °C | 13 cm³/10 min | ||||||||||
360 °C;5 kg | 25 cm³/10 min | ||||||||||
Molding Shrinkage, Across Flow(3.2 mm) | 0.50 - 0.70 % | Internal Method | |||||||||
Molding Shrinkage, Flow(3.2 mm) | 0.50 - 0.70 % | Internal Method | |||||||||
Water Absorption(24 hr;23 °C) | 0.25 % | ASTM D570;ISO 62 | |||||||||
Water Absorption, Saturation(23 °C) | 1.3 % | ASTM D570;ISO 62 | |||||||||
Water Absorption, Equilibrium | ISO 62 | ||||||||||
50% RH;24 hrs;23 °C | 0.20 % | ||||||||||
50% RH;23 °C | 0.70 % | ||||||||||
Rockwell Hardness, M-Scale | 109 106 |
ASTM D785 ISO 2039-2 |
|||||||||
Ball Indentation Hardness(H 358/30) | 140 MPa | ISO 2039-1 | |||||||||
Mechanical | Nominal Value | Test Method | |||||||||
Tensile Modulus | |||||||||||
5 mm/min | 3350 MPa | ASTM D638 | |||||||||
3200 MPa | ISO 527-1/1 | ||||||||||
Tensile Strength, Yield | |||||||||||
50 mm/min;Type I 115 MPa | ASTM D638 | ||||||||||
5 mm/min;Type I 110 MPa | ASTM D638 | ||||||||||
110 MPa | ISO 527-2/50 | ||||||||||
Tensile Elongation, Yield | |||||||||||
5 mm/min;Type I 7.0 % | ASTM D638 | ||||||||||
50 mm/min;Type I 7.0 % | ASTM D638 | ||||||||||
6.0 % | ISO 527-2/50 | ||||||||||
Tensile Elongation, Break | |||||||||||
5 mm/min;Type I 60 % | ASTM D638 | ||||||||||
50 mm/min;Type I 60 % | ASTM D638 | ||||||||||
50 % | ISO 527-2/50 | ||||||||||
Flexural Modulus | |||||||||||
1.3 mm/min;50 mm;Span 3200 MPa | ASTM D790 | ||||||||||
2.6 mm/min;100 mm;Span 3400 MPa | ASTM D790 | ||||||||||
2 mm/min 3300 MPa | ISO 178 | ||||||||||
Flexural Stress, at Yield(2 mm/min) 160 MPa | ISO 178 | ||||||||||
Flexural Stress, Yield 1.3 mm/min;50 mm;Span 2.6 mm/min;100 mm;Span |
165 MPa 160 MPa |
ASTM D790 | |||||||||
Poisson's Ratio 0.36 | ASTM E132 | ||||||||||
Taber Abrasion Resistance(1.0e+3 Cycles;1.0e+3 g;CS-1710.0 mg Wheel) | ASTM D1044 | ||||||||||
C harpy Notched Impact Strength -30 °C;80*10*4;sp =62mm 0 23 °C;80*10*4;sp =62mm 0 |
4.0 kJ/m² 4.0 kJ/m² |
ISO 179/1eA | |||||||||
Notched Izod Impact | |||||||||||
-30 °C 41 J/m | ASTM D256 | ||||||||||
23 °C 32 J/m | ASTM D256 | ||||||||||
80*10*4 mm;-30 °C 5.0 kJ/m² | ISO 180/1A | ||||||||||
80*10*4 mm;23 °C 5.0 kJ/m² | ISO 180/1A | ||||||||||
Unnotched Izod Impact | |||||||||||
-30 °C | 1500 J/m | ASTM D4812 | |||||||||
23 °C | 1600 J/m | ASTM D4812 | |||||||||
80*10*4 mm;-30 °C | No Break | ISO 180/1U | |||||||||
80*10*4 mm;23 °C | No Break | ISO 180/1U | |||||||||
Reverse Notch Izod Impact(3.2 mm) | 1200 J/m | ASTM D256 | |||||||||
Gardner Impact(23 °C) | 33.0 J | Internal Method | |||||||||
Thermal | Nominal Value | Test Method | |||||||||
Deflection Temperature Under Load, Unannealed | |||||||||||
0.45 MPa;3.2 mm | 207 °C | ASTM D648 | |||||||||
0.45 MPa;6.4 mm | 210 °C | ASTM D648 | |||||||||
1.8 MPa;3.2 mm | 190 °C | ASTM D648 | |||||||||
1.8 MPa;6.4 mm | 201 °C | ASTM D648 | |||||||||
80*10*4 mm;0.45 MPa;4 mm;64 mm;Span | 209 °C | ISO 75-2/Bf | |||||||||
80*10*4 mm;1.8 MPa;4 mm;64 mm;Span | 192 °C | ISO 75-2/Af | |||||||||
Vicat Softening Temperature | |||||||||||
50 °C/h;50 N;Rate A;Loading 2 | 211 °C 212 °C 215 °C |
ISO 306/B50;ASTM D1525 ISO 306/B120 ISO 306/A50 |
|||||||||
Ball Pressure Test(123 - 127 °C) | Pass | IEC 60695-10-2 | |||||||||
CLTE, Flow | |||||||||||
-20 - 150 °C | 5.6E-5 cm/cm/°C | ASTM E831 | |||||||||
-20 - 150 °C | 5.2E-5 cm/cm/°C | ISO 11359-2 | |||||||||
CLTE, Transverse | |||||||||||
-20 - 150 °C | 5.4E-5 cm/cm/°C | ASTM E831 | |||||||||
-20 - 150 °C | 5.2E-5 cm/cm/°C | ISO 11359-2 | |||||||||
Thermal Conductivity | 0.22 W/m-K | ASTM C177;ISO 8302 | |||||||||
Oxygen Index | 44 % 47 % |
ASTM D2863 ISO 4589-2 |
|||||||||
NBS Smoke Density - Flaming, Ds(4 min) | 2.00 | ASTM E662 | |||||||||
Electrical | Nominal Value | Test Method | |||||||||
Surface Resistivity | > 1.0E+15 Ohms | IEC 60093 | |||||||||
Volume Resistivity | |||||||||||
1.0e+17 ohms ·cm | ASTM D257 | ||||||||||
1.0e+15 ohms ·cm | IEC 60093 | ||||||||||
Dielectric Strength, in Air(1.6 mm) | 33 kV/mm | ASTM D149 | |||||||||
Dielectric Strength, in Oil | |||||||||||
1.6 mm | 28 kV/mm | ASTM D149 | |||||||||
3.2 mm | 20 kV/mm | ASTM D149 | |||||||||
0.8 mm | 33 kV/mm | IEC 60243-1 | |||||||||
1.6 mm | 25 kV/mm | IEC 60243-1 | |||||||||
3.2 mm | 16 kV/mm | IEC 60243-1 | |||||||||
Dielectric Constant | |||||||||||
100 Hz | 3.15 | ASTM D150 | |||||||||
1.0e+3 Hz | 3.15 | ASTM D150 | |||||||||
1.1e+9 Hz | 3.01 | Internal Method | |||||||||
5.0e+9 Hz | 3.02 | Internal Method | |||||||||
1.0e+10 Hz | 3.02 | Internal Method | |||||||||
50 Hz | 2.90 | IEC 60250 | |||||||||
60 Hz | 2.90 | IEC 60250 | |||||||||
1.0e+6 Hz | 2.90 | IEC 60250 | |||||||||
Dissipation Factor | |||||||||||
100 Hz | 1.5E-3 | ASTM D150 | |||||||||
1.0e+3 Hz | 1.2E-3 | ASTM D150 | |||||||||
1.1e+9 Hz | 1.2E-3 | Internal Method | |||||||||
5.0e+9 Hz | 2.4E-3 | Internal Method | |||||||||
1.0e+10 Hz | 2.7E-3 | Internal Method | |||||||||
50 Hz | 5.0E-4 | IEC 60250 | |||||||||
60 Hz | 5.0E-4 | IEC 60250 | |||||||||
1.0e+6 Hz | 6.0E-3 | IEC 60250 | |||||||||
Arc Resistance, Tungsten Electrode | PLC5 | ASTM D495 | |||||||||
Comparative Tracking Index | 150 V | IEC 60112 | |||||||||
Comparative Tracking Index, Solution B | 100 V | IEC 60112 | |||||||||
Processing | Nominal Value | ||||||||||
Drying Temperature<Injection> | 150 °C | ||||||||||
Drying Time<Injection> | 4.0 - 6.0 hr | ||||||||||
Suggested Max Moisture<Injection> | 0.020 % | ||||||||||
Suggested Shot Size<Injection> | 40 - 60 % | ||||||||||
Rear Temperature<Injection> | 330 - 400 °C | ||||||||||
Middle Temperature<injection> | 340 - 405 °C | ||||||||||
Front Temperature<Injection> | 345 - 415 °C | ||||||||||
Nozzle Temperature<Injection> | 345 - 405 °C | ||||||||||
Processing Temp, Melt<Injection> | 350 - 410 °C | ||||||||||
Mold Temperature<Injection> | 135 - 180 °C | ||||||||||
Back Pressure<Injection> | 0.300 - 0.700 MPa | ||||||||||
Vent Depth <Injection> | 0.025 - 0.076 mm | ||||||||||
Drying Time, Cumulative<Injection> | 24 hr | ||||||||||
Screw Speed, C ircumferential Speed <Injection> | 0.2 - 0.3 m/sec | ||||||||||
Drying Temperature<Extrusion Blow Molding> | 140 - 150 °C | ||||||||||
Drying Time<Extrusion Blow Molding> | 4 - 6 hr | ||||||||||
Drying Time, Cumulative<Extrusion Blow Molding> | 24 hr | ||||||||||
Maximum Moisture Content<Extrusion Blow Molding> | 0.01 - 0.02 % | ||||||||||
Melt Temperature, Parison<Extrusion Blow Molding> | 320 - 355 °C | ||||||||||
Barrel - Zone 1 Temperature<Extrusion Blow Molding> | 325 - 350 °C | ||||||||||
Barrel - Zone 2 Temperature<Extrusion Blow Molding> | 330 - 355 °C | ||||||||||
Barrel - Zone 3 Temperature<Extrusion Blow Molding> | 330 - 355 °C | ||||||||||
Barrel - Zone 4 Temperature<Extrusion Blow Molding> | 330 - 355 °C | ||||||||||
Adapter - Zone 5 Temperature<Extrusion Blow Molding> |
330 - 355 °C | ||||||||||
Head - Zone 6 - Top Temperature<Extrusion Blow Molding> |
330 - 355 °C | ||||||||||
Head - Zone 7 - Bottom Temperature<Extrusion Blow Molding> |
330 - 355 °C | ||||||||||
Screw Speed <Extrusion Blow Molding> | 10 - 70 rpm | ||||||||||
Mold Temperature<Extrusion Blow Molding> | 65 - 175 °C | ||||||||||
Die Temperature<Extrusion Blow Molding> | 325 - 355 °C |
Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.
Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.
With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry
Suppliers with verified business licenses