Polyamide 6 Injection Molding Resin with Improved Thermal Conductivity
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | ||
Star T PA6 75E12 is a Polyamide 6 Injection Molding Resin with Improved Thermal Conductivity | ||
General | ||
Form Resin Pellets | ||
Feature Thermally Conductive | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 2.26 g/cm³ | ASTM D792 |
Molding Shrinkage, Flow(4 mm) | 0.80 - 1.2 % | Internal Method |
Mechanical | Nominal Value | Test Method |
Tensile Stress, Yield | 85.0 MPa | ISO 527-2 |
Tensile Strain, Break | 1.4 % | ISO 527-2 |
Flexural Modulus | 12500 MPa | ISO 178 |
Flexural Stress | 123 MPa | ISO 178 |
Notched Izod Impact Strength(23 °C) | 3.8 kJ/m² | ISO 180/1A |
Unnotched Izod Impact Strength(23 °C) | 20 kJ/m² | ISO 180/1U |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed(1.8 MPa;64 mm;Span;80x10x4 mm) | 136 °C | ISO 75-2/Af |
Thermal Conductivity, Across Flow | 1.5 W/m-K | Internal Method |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time<Injection> | 4.0 hr | |
Suggested Max Moisture<Injection> | 0.20 % | |
Rear Temperature<Injection> | 250 - 260 °C | |
Middle Temperature<injection> | 260 - 280 °C | |
Front Temperature<Injection> | 260 - 280 °C | |
Processing Temp, Melt<Injection> | 260 - 280 °C | |
Mold Temperature<Injection> | 60 - 90 °C |