ABS Plastic Raw Material for Automotive Furniture and Industrial Applications

• CAS No.: 9003-56-9
• Formula: C45h51n3X2
• EINECS: 618-371-8
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: ABS-P2HGVXH
• Material: Acrylonitrile-Butadiene-Styrene Copolymers/ABS
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Place of Origin: Guangdong, China
• Use: Radiator Front Cover.Automotive Parts
• Features: Lubricated, Good Wear Resistance, Low Friction and
• Application: Zippers Irish Flutes, Bagpipes, Practice Chanters
• Form: Resin Pellets
• Delivery Time: in 7 Days
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Plastic Raw Material ABS High Flow Grade, Jet Black Grade Polyamide Resin
 
  

General
Form		Resin Pellets
Filler		16 % Glass Fiber
Feature		Good Thermal	High Mechanical Strength  Good Hardness And Rigidity
Usage	Automotive            Furniture          Industrial Applications
Physical			Nominal Value	Test Method
Density / Specific Gravity			1.16 g/cm³	ISO 1183
Melt Volume-Flow Rate, MVR(220 °C;10 kg)			3.0 cm³/10 min	ISO 1133
Molding Shrinkage			0.20 - 0.40 %	ISO 294-4
Ash Content			16 %
Ball Indentation Hardness			135 MPa	ISO 2039-1
Mechanical			Nominal Value	Test Method
Tensile Modulus			5500 MPa	ISO 527-2
Tensile Stress, Yield(23 °C)			74.0 MPa	ISO 527-2
Tensile Stress, Break(23 °C)			74.0 MPa	ISO 527-2
Tensile Strain, Break(23 °C)			2.0 %	ISO 527-2
Flexural Modulus(23 °C)			5400 MPa	ISO 178
Flexural Stress(23 °C)			101 MPa	ISO 178
C harpy Notched Impact Strength -30 °C 23 °C			5.0 kJ/m² 6.0 kJ/m²	ISO 179 1eA
C harpy Unnotched Impact Strength -30 °C 23 °C			20 kJ/m² 18 kJ/m²	ISO 179 1eU
Notched Izod Impact Strength -30 °C 23 °C			5.0 kJ/m² 7.0 kJ/m²	ISO 180/1A

 

Thermal	Nominal Value	Test Method
Heat Deflection Temperature, Annealed 0.45 MPa;4 h;80 °C 1.8 MPa;4 h;80 °C	106 °C 102 °C	ISO 75-2/B ISO 75-2/A
Vicat Softening Temperature	107 °C 105 °C	ISO 306/B120 ISO 306/B50
CLTE, Flow	4.0E-5 cm/cm/°C	ISO 11359-1
Burning rate(2 mm)	20 mm/min	ISO 3795
Flame Rating(1.5 mm)	HB	IEC 60695-11-10
Glow Wire Flammability Index(2 mm)	700 °C	IEC 60695-2-12
Electrical	Nominal Value	Test Method
Surface Resistivity	1.0E+14 ohms	IEC 62631-3-1
Volume Resistivity	> 1.0E+15 Ohms ·cm	IEC 62631-3-1
Electric Strength(1 mm)	32 kV/mm	IEC 60243-1
Relative Permittivity 100 Hz 1.0e+6 Hz	2.90 3.10	IEC 62631-2-1
Dissipation Factor 100 Hz 1.0e+6 Hz	9.0E-3 6.0E-3	IEC 62631-2-1
Comparative Tracking Index	575 V	IEC 60112
Processing		Nominal Value
Drying Temperature<Injection>		80 °C
Drying Time<Injection>		2.0 - 4.0 hr
Processing Temp, Melt<Injection>		230 - 260 °C
Mold Temperature<Injection>		60 - 80 °C
Injection Velocity<Injection>		14 m/min

 

Company Profile

Product Parameters

 

Product Description
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.
General
Form	Resin	Pellets
Physical			Nominal Value	Test Method
Density / Specific Gravity			1.40 g/cm³
Water Absorption			0.21 %	ASTM D570
Moisture Absorption at Equilibrium			0.80 %	ASTM D570
Linear Mold Shrinkage			2.2 %
Linear Mold Shrinkage, Transverse			1.8 %
Hardness, Rockwell R			111	ASTM D785
Mechanical			Nominal Value	Test Method
Tensile Strength, Yield			37.0 MPa	ASTM D638
Elongation at Break			30 %	ASTM D638
Flexural Strength			52.0 MPa	ASTM D790
Flexural Modulus			2100 MPa	ASTM D790
Compressive Strength			66.0 MPa	ASTM D695
Shear Strength			40.0 MPa	ASTM D732
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C			50 J/m 30 J/m	ASTM D256
Thermal			Nominal Value	Test Method
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa			152 °C 106 °C	ASTM D648
Flammability, UL94			HB	UL 94

 

Our Customers

Our Certificates

 

Our Production

Our Package/Shipping

Our Advantages

 

Our Samples

 

Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.

Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.

With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry.