PA6 GF 45% Polyamide 6 PA 6 Nylon Plastic Virgin Recycled Nylon6 CF10%, GF45%, GF35, GF45 Granules PA6 GF30

• Feature: Oxidative Degradable
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 20% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year

Product Description

PA6 GF 45% polyamide 6 PA 6 Nylon plastic Virgin Recycled Nylon6 cf10% , gf45% , gf35 , gf45 granules PA6 GF30
20% Glass Reinforced, Heat Stabilized, Flame Retardant (halogen- phosphorous-free)

 
 

Product Description
20% Glass Reinforced, Heat Stabilized, Flame Retardant (halogen- phosphorous-free)
General
Form
Filler
Feature			Red Phosphorous Free		Non-Brominated & Non-  Good Thermal Chlorinated Flame
			Retardant
UL Yellow Card
Physical				Nominal Value		Test Method
Dry:	Density			1.34 g/cm³		ISO 1183
Dry:	Molding Shrinkage, Across Flow			1.0 %		ISO 294-4
Dry:	Molding Shrinkage, Flow			0.60 %		ISO 294-4
Dry:	Water Absorption, Saturation(23 °C)			6.5 %		ISO 62
Dry:	Water Absorption, Equilibrium(50% RH;23 °C)			2.0 %		ISO 62

 

Mechanical	Nominal Value	Test Method
Dry: Tensile Modulus	5700 MPa	ISO 527-2
Condition: Tensile Modulus	2500 MPa	ISO 527-2
Dry: Tensile Stress, Break	80.0 MPa	ISO 527-2
Condition: Tensile Stress, Break	45.0 MPa	ISO 527-2
Dry: Tensile Strain, Break	3.0 %	ISO 527-2
Condition: Tensile Strain, Break	15 %	ISO 527-2
Dry: Charpy Notched Impact Strength -30 °C 23 °C	4.0 kJ/m² 4.0 kJ/m²	ISO 179 1eA
Condition: Charpy Notched Impact Strength -30 °C 23 °C	4.0 kJ/m² 9.0 kJ/m²	ISO 179 1eA
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C	40 kJ/m² 46 KJ/m²	ISO 179 1eU
Condition: Charpy Unnotched Impact Strength -30 °C 23 °C	40 kJ/m² 93 kJ/m²	ISO 179 1eU
Thermal	Nominal Value	Test Method
Dry: Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa	210 °C 170 °C	ISO 75-2/B ISO 75-2/A
Dry: Melting Temperature(10 °C/min)	220 °C	ISO 11357-3
Dry: Flammability Classification 0.8 mm 1.5 mm	V-2 V-2	IEC 60695-11-10, - 20
Dry: Glow Wire Flammability Index 1 mm 1.6 mm	960 °C 960 °C	IEC 60695-2-12

 

Electrical	Nominal Value	Test Method
Condition: Surface resistivity	1.0E+14 ohms	IEC 60093
Dry: Volume Resistivity	1.0e+15 ohms·cm	IEC 60093
Condition: Volume resistivity	1.0E+13 ohms·cm	IEC 60093
Dry: Electric Strength	30 kV/mm	IEC 60243-1
Condition: Electric Strength	25 kV/mm	IEC 60243-1
Dry: Relative permittivity 100 Hz 1000000 Hz	4.30 3.80	IEC 60250
Condition: Relative Permittivity 100 Hz 1000000 Hz	10.0 3.90	IEC 60250
Dry: Dissipation Factor 100 Hz 1000000 Hz	0.013 0.021	IEC 60250
Condition: Dissipation factor 100 Hz 1000000 Hz	0.30 0.10	IEC 60250
Dry: Comparative Tracking Index	600 V	IEC 60112
Condition: Comparative Tracking Index	600 V	IEC 60112

Mechanical	Nominal Value	Test Method
Dry: Tensile Modulus	9500 MPa	ISO 527-1
Condition: Tensile Modulus	6000 MPa	ISO 527-1
Dry: Tensile Stress, Break	180 MPa	ISO 527-2
Condition: Tensile Stress, Break	110 MPa	ISO 527-2
Dry: Tensile Strain, Break	3.5 %	ISO 527-2
Condition: Tensile Strain, Break	7.0 %	ISO 527-2
Dry: Flexural Modulus	8600 MPa	ISO 178
Dry: Flexural Stress	235 MPa	ISO 178
Dry: Charpy Notched Impact Strength -30 °C 23 °C	11 kJ/m² 12 kJ/m²	ISO 179/1eA
Condition: Charpy Notched Impact Strength -30 °C 23 °C	11 kJ/m² 25 kJ/m²	ISO 179/1eA
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C	75 kJ/m² 90 kJ/m²	ISO 179/1eU
Condition: Charpy Unnotched Impact Strength -30 °C 23 °C	75 kJ/m² 110 kJ/m²	ISO 179/1eU

 

Thermal	Nominal Value	Test Method
Dry: Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa	220 °C 200 °C	ISO 75-2/B ISO 75-2/A
Dry: Melting Point(10 °C/min)	220 °C	ISO 11357-3
Dry: CLTE, Flow	2.0E-5 cm/cm/°C	ISO 11359-2
Dry: CLTE, Transverse	7.0E-5 cm/cm/°C	ISO 11359-2
Dry: RTI Elec 0.75 mm 3 mm	65.0 °C 65.0 °C	UL 746B
Dry: RTI Imp 0.75 mm 3 mm	65.0 °C 65.0 °C	UL 746B
Dry: RTI Str 0.75 mm 3 mm	65.0 °C 65.0 °C	UL 746B
Dry: Effective Thermal Diffusivity	1.12E-7 m²/s
Dry: Flame Rating 1.5 mm 3 mm 0.75 mm	HB HB HB	IEC 60695-11- 10;UL 94;IEC 60695-11-20 IEC 60695-11- 10;UL 94;IEC 60695-11-20 IEC 60695-11- 10;IEC 60695-11- 20

 

                                                                                                                  Forever Co.,Ltd

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....