10 % Glass Fiber Reinforced PC Flame Retardant UL 94 Available Inopaque Colors Only

• Feature: Plastics
• CAS No.: 25766-59-0
• Formula: C6h4c(CH3)2c6h4oco2-]N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PC-9417
• EINECS: 618-371-8
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Polycarbonate
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

10 % glass fiber reinforced PC flame retardant UL 94 available inopaque colors only

Product Description

Product Description
923X is based on Polycarbonate (PC) siloxane copolymer resin and is a UV stabilized high flow opaque injection molding (IM) grade. This non-chlorinated, non-brominated flame retardant grade has UL-94 V0  1.5mm flame rating, extreme low temperature ductility (-40°C) characteristics and excellent processability, providing opportunities for shorter IM cycle times compared to standard PC. 923X resin is available in a wide range of opaque colours and targeted for a wide range of applications.
General
Form	Resin Pellets
Feature		Non-Brominated High Impact		Non-Chlorinated   Low Temperature Impact		Non-Brominated & Non- Chlorinated Flame Retardant
UL Yellow Card	E207780-101158295
Uses		Transportation Wire Insulation		Aerospace   Rail	Cell Phone Cases   Electrical
Medical                             Decorative Parts               Automotive
nergy    orage
Physical                                                                                 Nominal Value                                       Test Method
Density / Specific Gravity                                                     1.19 g/cm³					ASTM D792;ISO 1183
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg)                          16 g/10min                                             ASTM D1238
Melt Volume-Flow Rate, MVR(300 °C;1.2 kg)                     15 cm³/10 min                                        ISO 1133
Molding Shrinkage, Flow(3.2 mm)                                      0.40 - 0.80 %                                          Internal Method
Water Absorption, Saturation(23 °C)                                  0.40 %                                                    ISO 62
Water Absorption, Equilibrium(50% RH;23 °C)                  0.15 %                                                    ISO 62
Mechanical                                                                            Nominal Value                                      Test Method
Tensile Modulus
5 mm/min                                                                           2100 MPa                                               ASTM D638
2000 MPa                                              ISO 527-1/1
Tensile Strength, Yield
50 mm/min;Type I                                                              58.0 MPa                                                ASTM D638
56.0 MPa                                                ISO 527-2/50
Tensile Strength, Break 50 mm/min;Type I				60.0 MPa 57.0 MPa			ASTM D638 ISO 527-2/50
Tensile Elongation, Yield 50 mm/min;Type I				6.0 % 6.0 %			ASTM D638 ISO 527-2/50
Tensile Elongation, Break 50 mm/min;Type I				110 % 110 %			ASTM D638 ISO 527-2/50
Flexural Modulus 1.3 mm/min;50 mm;Span 2 mm/min				2400 MPa 2100 MPa			ASTM D790 ISO 178
Flexural Strength 1.3 mm/min;50 mm;Span 2 mm/min				90.0 MPa 87.0 MPa			ASTM D790 ISO 178
C harpy Notched Impact Strength -30 °C;80 23 °C;80				35 kJ/m² 70 kJ/m²			ISO 179/1eA
C harpy Unnotched Impact Strength -30 °C;80 23 °C;80				No Break No Break			ISO 179/1eU
Notched Izod Impact -30 °C 23 °C -30 °C;80*10*3 mm 23 °C;80*10*3 mm				650 J/m 780 J/m 30 kJ/m² 65 kJ/m²			ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A
Unnotched Izod Impact Strength -30 °C;80*10*3 mm 23 °C;80*10*3 mm				No Break No Break			ISO 180/1U
Instrumented Dart Impact, Total Energy(23 °C)				65.0 J			ASTM D3763
Thermal			Nominal Value				Test Method
Deflection Temperature Under Load, Unannealed 1.8 MPa;3.2 mm 80*10*4 mm;1.8 MPa;4 mm;64 mm;Span			123 °C 118 °C				ASTM D648 ISO 75-2/Af
Vicat Softening Temperature 50 °C/h;50 N;Rate A;Loading 2			140 °C 141 °C 139 °C				ASTM D1525  ISO 306/B120 ISO 306/B50
CLTE, Flow(-40 - 40 °C)			6.1E-5 cm/cm/°C				ASTM E831;ISO 11359-2
CLTE, Transverse(-40 - 40 °C)			6.2E-5 cm/cm/°C				ASTM E831;ISO 11359-2
RTI Elec			125 °C				UL 746B
RTI Imp			115 °C				UL 746B
RTI Str			120 °C				UL 746B
Flame Rating > 1.5 mm > 3 mm			V-0 5VA				UL 94
Glow Wire Flammability Index 1.5 mm 3 mm			960 °C 960 °C				IEC 60695-2-12
Glow Wire Ignition Temperature [GWIT] 1.5 mm 3 mm			825 °C 825 °C				IEC 60695-2-13
Electrical			Nominal Value				Test Method
Comparative Tracking Index, CTI			PLC 3				UL 746A
Comparative Tracking Index			150 V				IEC 60112
High Amp Arc Ignition, HAI > 1.5 mm > 3 mm				PLC 1 PLC 0			UL 746A
Hot-wire Ignition, HWI > 1.5 mm > 3 mm				PLC 3 PLC 2			UL 746A
Processing				Nominal Value
Drying Temperature<Injection>				120 °C
Drying Time<Injection>				3.0 - 4.0 hr
Suggested Max Moisture<Injection>				0.020 %
Rear Temperature<Injection>				270 - 295 °C
Middle Temperature<injection>				280 - 305 °C
Front Temperature<Injection>				295 - 315 °C
Nozzle Temperature<Injection>				290 - 310 °C
Processing Temp, Melt<Injection>				295 - 315 °C
Mold Temperature<Injection>				70 - 95 °C
Back Pressure<Injection>				0.300 - 0.700 MPa
Screw Speed <Injection>				40 - 70 rpm
Drying Time, Cumulative<Injection>				48 hr

 
 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....