Feature: | Plastics |
---|---|
CAS No.: | 25766-59-0 |
Formula: | C6h4c(CH3)2c6h4oco2-]N |
Samples: |
25kg/bag
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | |||
CALIBRE™ 30x-6 MFR are general purpose Polycarbonate resins that offer exceptional impact resistance, heat distortion resistance and optical clarity as well as high melt strength for various extrusion processes. The CALIBRE 300-6 series products are available in 4 additive packages: CALIBRE 300: No mold release or UV Stabilizer. CALIBRE 301: Mold release. CALIBRE 302: UV stabilizer. CALIBRE 303: Mold release and UV stabilizer. Material is transparent but can be custom colored. Govt. and Industry Standards: Underwriters Laboratory, Inc. (UL) Applications: Sheet extrusion Electrical & lighting components Appliances Transportation Automotive applications Houseware Recreation Packaging applications Power equipment |
|||
General | |||
Form | Resin Pellets | ||
Feature | High Viscosity High Melt Stability |
High Clarity High Impact | |
Lighting Applications Displays Sheet | |||
Automotive | Electrical | ||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.20 g/cm³ | ASTM D792;ISO 1183 | |
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 6.0 g/10min | ASTM D1238;ISO 1133 | |
Molding Shrinkage, Flow | 0.50 - 0.70 % | ISO 294-4 | |
Water Absorption, Saturation(23 °C) | 0.32 % | ISO 62 | |
Water Absorption, Equilibrium(50% RH;23 °C) | 0.12 % | ISO 62 | |
Rockwell Hardness, M-Scale | 73 | ASTM D785 | |
Rockwell Hardness, R-Scale | 118 | ASTM D785 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | ||
1 mm/min | 2300 MPa 2300 MPa |
ASTM D638 ISO 527-1/1 |
Tensile Strength, Yield | ||
50 mm/min | 60.0 MPa 60.0 MPa |
ASTM D638 ISO 527-2/50 |
Tensile Strength, Break | ||
50 mm/min | 72.0 MPa 72.0 MPa |
ASTM D638 ISO 527-2/50 |
Tensile Elongation, Yield | ||
50 mm/min | 6.0 % 6.0 % |
ASTM D638 ISO 527-2/50 |
Tensile Elongation, Break | ||
50 mm/min | 140 % 150 % |
ASTM D638 ISO 527-2/50 |
Flexural Modulus | 2410 MPa |
ASTM D790 |
2 mm/min | 2400 MPa | ISO 178 |
Flexural Strength | 96.5 MPa |
ASTM D790 |
2 mm/min | 97.0 MPa | ISO 178 |
C harpy Notched Impact Strength -30 °C 23 °C |
14 kJ/m² 55 kJ/m² |
ISO 179/1eA |
Notched Izod Impact | ||
23 °C | 910 J/m | ASTM D256 |
23 °C | 93 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C;3.33 m/sec) | 90.4 J | ASTM D3763 |
Tensile Impact Strength | 588 kJ/m² | ASTM D1822 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa 1.8 MPa |
145 °C 129 °C 126 °C |
ASTM D648 ASTM D648 ISO 75-2/A |
Deflection Temperature Under Load, Annealed 0.45 MPa 1.8 MPa 0.45 MPa 1.8 MPa |
145 °C 142 °C 146 °C 143 °C |
ASTM D648 ASTM D648 ISO 75-2/B ISO 75-2/A |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 151 °C | ISO 306/B50;ASTM D1525 |
Ball Indentation Temperature | > 125 °C | IEC 60335-1 |
CLTE, Flow(-40 - 80 °C) | 6.8E-5 cm/cm/°C | ISO 11359-2 |
Flame Rating 1.5 mm 3 mm 3 mm;Calibre 301 0.75 mm;Calibre 301 1.5 mm;Calibre 301 |
HB HB HB V-2 V-2 |
UL 94 |
Glow Wire Flammability Index 1 mm 2 mm 3 mm |
900 °C 875 °C 875 °C |
IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT] 1 mm 2 mm 3 mm |
800 °C 775 °C 775 °C |
IEC 60695-2-13 |
Oxygen Index | 26 % | ISO 4589-2 |
Electrical | Nominal Value | Test Method |
Volume Resistivity | > 1.0E+15 Ohms ·cm | IEC 60093 |
Dielectric Strength | 17 kV/mm | ASTM D149;IEC 60243-1 |
Relative Permittivity 100 Hz 1.0e+6 Hz |
3.00 3.00 |
IEC 60250 |
Dissipation Factor 50 Hz 1.0e+6 Hz |
1.0E-3 2.0E-3 |
ASTM D150 |
Comparative Tracking Index, Solution A(2 mm) | 250 V | IEC 60112 |
Optical | Nominal Value | Test Method |
Refractive Index | 1.586 | ISO 489 |
Transmittance (3.0e+3 µm) | 87.0 - 91.0 % | ASTM D1003 |
Haze | < 1.00 % | ASTM D1003 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 4.0 hr |