CAS No.: | 9003-56-9 |
---|---|
Formula: | C45h51n3X2 |
EINECS: | 618-371-8 |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
ABS (Acrylonitrile Butadiene Styrene) that is suitable for multiple purposes and is specifically designed for injection molding. This ABS material has a beneficial combination of engineering properties, meaning it exhibits desirable characteristics such as strength, durability, and impact resistance. Additionally, ABS material complies with NSF Standard 61.
General |
||
Form Resin Pellets |
||
Feature Nsf |
||
Appliances |
Lighting Applications |
Lawn And Garden Equipment |
Usage |
||
Constraction |
Outdoor |
|
Physical |
Nominal Value |
Test Method |
Density / Specific Gravity |
1.04 g/cm³ |
ASTM D792 |
Melt Mass-Flow Rate, MFR |
||
230 °C;3.8 kg |
5.6 g/10min |
ASTM D1238 |
220 °C;10 kg |
18 g/10min |
ISO 1133 |
Molding Shrinkage, Flow(3.2 mm) |
0.50 - 0.80 % |
Internal Method |
Melt Viscosity(240 °C;1.0e+3 sec^-1) |
225 Pa · s |
ASTM D3835 |
Mechanical |
Nominal Value |
Test Method |
Tensile Modulus(5 mm/min) |
2270 MPa |
ASTM D638 |
Tensile Strength, Yield(5 mm/min;Type I) |
44.0 MPa |
ASTM D638 |
Tensile Strength, Break(5 mm/min;Type I) |
34.0 MPa |
ASTM D638 |
Tensile Elongation, Yield(5 mm/min;Type I) |
2.0 % |
ASTM D638 |
Tensile Elongation, Break(5 mm/min;Type I) |
24 % |
ASTM D638 |
Flexural Modulus(1.3 mm/min;50 mm;Span) |
2340 MPa |
ASTM D790 |
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) |
72.0 MPa |
ASTM D790 |
Notched Izod Impact(23 °C) |
320 J/m |
ASTM D256 |
Instrumented Dart Impact, Total Energy(23 °C) |
31.0 J |
ASTM D3763 |
Thermal |
Nominal Value |
Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;3.2 mm 1.8 MPa;3.2 mm |
94.0 °C 80.0 °C |
ASTM D648 |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) |
99.0 °C |
ASTM D1525 |
CLTE, Flow(-40 - 40 °C) |
8.8E-5 cm/cm/°C |
ASTM E831 |
CLTE, Transverse(-40 - 40 °C) |
8.8E-5 cm/cm/°C |
ASTM E831 |
RTI Elec |
60.0 °C |
UL 746 |
RTI Imp |
60.0 °C |
UL 746 |
RTI Str |
60.0 °C |
UL 746 |
Flame Rating(1.5 mm) |
HB |
UL 94 |
Electrical |
Nominal Value |
Test Method |
Arc Resistance, Tungsten Electrode |
PLC 6 |
ASTM D495 |
Comparative Tracking Index[CTI] |
PLC 0 |
UL 746 |
High Amp Arc Ignition, HAI, Surface |
PLC 0 |
UL 746 |
High Voltage Arc Tracking Rate, HVTR |
PLC 3 |
UL 746 |
Hot-wire Ignition, HWI |
PLC 3 |
UL 746 |
Processing |
Nominal Value |
|
Drying Temperature<Injection> |
80 - 95 °C |
|
Drying Time<Injection> |
2.0 - 4.0 hr |
|
Suggested Max Moisture<Injection> |
0.10 % |
|
Suggested Shot Size<Injection> |
50 - 70 % |
|
Rear Temperature<Injection> |
190 - 210 °C |
|
Middle Temperature<injection> |
205 - 225 °C |
|
Front Temperature<Injection> |
215 - 240 °C |
|
Nozzle Temperature<Injection> |
220 - 260 °C |
|
Processing Temp, Melt<Injection> |
220 - 260 °C |
|
Mold Temperature<Injection> |
50 - 70 °C |
|
Back Pressure<Injection> |
0.300 - 0.700 MPa |
|
Screw Speed <Injection> |
30 - 60 rpm |
|
Vent Depth <Injection> |
0.038 - 0.051 mm |
|
Drying Time, Cumulative<Injection> |
8 hrs |