Audited Supplier RZL36 compound is based on Nylon 66 resin containing 30% milled glass 15% PTFE PA66
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | ||||
| STAR AFX 218 V50 BK 31N is a high flow polyamide 66 resin, reinforced with 50% of glass fibre, heat stabilized, for injection moulding. Due to its outstanding flow caracteristics, this grade shows exceptional processing behaviour and excellent surface aspect of the finished part. |
||||
| General | ||||
| Form Resin Pellets | ||||
| Filler 50 % Glass Fiber | ||||
| Feature | Rohs Ec 1907/2006 (Reach) |
Good Dimensional Anti Aging | Good Hardness High Reflection |
|
| Uses Automotive Gear Wheels | ||||
| Physical Nominal Value Test Method | ||||
| Density / Specific Gravity 1.55 g/cm³ ISO 1183 | ||||
| Water Absorption(24 hr;23 °C) 0.6 % ISO 62 | ||||
| Molding shrinkage, parallel(50% RH;23 °C;72 hr) 0.3 % | ISO 2577;ISO 294- 4 | |||
| Molding shrinkage, normal(50% RH;23 °C;72 hr) 0.65 % | ISO 2577;ISO 294- 4 | |||
| Mechanical Nominal Value Test Method | ||||
| Dry: Tensile Modulus(1 mm/min) 17000 MPa ISO 527-1/-2 | ||||
| Condition: Tensile Modulus(1 mm/min) 12500 MPa ISO 527-1/-2 | ||||
| Dry: Stress at break 255 MPa ISO 527-1/-2 | ||||
| Condition: Stress at break 180 MPa ISO 527-1/-2 | ||||
| Dry: Strain at break 2.5 % ISO 527-1/-2 | ||||
| Condition: Strain at break 3.5 % ISO 527-1/-2 | ||||
| Flexural Modulus(2 mm/min) 14000 MPa ISO 178 | ||||
| Flexural Strength(2 mm/min) 380 MPa ISO 178 | ||||
| Dry: Charpy Impact Strength(23 °C) 100 kJ/m² ISO 179/1eU | ||||
| Condition: Charpy Impact Strength(23 °C) 100 kJ/m² ISO 179/1eU | ||||
| Dry: Charpy Notched Impact Strength(23 °C) 15 kJ/m² ISO 179/1eA | ||||
| Condition: Charpy Notched Impact Strength(23 °C) 21 kJ/m² ISO 179/1eA | ||||
| Dry: Izod Impact Strength, Unnotched(23 °C) 88 kJ/m² ISO 180/1U | ||||
| Condition: Izod Impact Strength, Unnotched(23 °C) 91 kJ/m² ISO 180/1U | ||||
| Dry: Izod Notched Impact Strength(23 °C) 17 kJ/m² ISO 180/1A | ||||
| Izod Notched Impact Strength: condition(23 °C) 21 kJ/m² ISO 180/1A | ||||
| Thermal Nominal Value | Test Method | |||
| Melting Temperature(10 °C/min) 262 °C | ISO 11357-1 | |||
| Temp. of deflection under load(1.8 MPa) 256 °C | ISO 75 | |||
| Flammability(0.75 mm) HB | UL 94 | |||
| Glow Wire Flammability Index(0.75 mm) 650 °C | IEC 60695-2-12 | |||
| Glow Wire Ignition Temperature [GWIT](0.75 mm) 675 °C | IEC 60695-2-13 | |||
| Processing | Nominal Value | |||
| Drying Temperature | 80 °C | |||
| Dry Time(with a dehumidified air drying equipment, dew point mini -20°C) |
2 - 4 h | |||
| Suggested Max Moisture | 0.002 | |||
| Rear Temperature | 265 - 275 °C | |||
| Middle Temperature | 270 - 280 °C | |||
| Front Temperature | 280 - 290 °C | |||
| Mold Temperature | 60 - 90 °C | |||