Audited Supplier polyamide 6 resin (Tech nylStar), reinforced of 25% of mineral filler, for injection moulding
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | ||
| S 52G1 MX25 Grey 2408 is a grade based on a non-phosphorous and non-halogenated flame retardant system and on a patented high flow polyamide 6 resin (Tech nylStar), reinforced of 25% of mineral filler, for injection moulding. This grade offers a high fluidity as well as a robust glow wire resistance. | ||
| General | ||
| Form Resin Pellets | ||
| Filler 25 % Mineral | ||
| Feature Non-Brominated & Non- High Reflection | ||
| Chlorinated Flame R t d t |
||
| Uses Electrical | ||
| Physical Nominal Value Test Method | ||
| Water Absorption(24 hr;23 °C) 1.1 % ISO 62 | ||
| Molding shrinkage, parallel(50% RH;23 °C;72 hr) 0.6 % | ||
| Molding shrinkage, normal(50% RH;23 °C;72 hr) 0.7 % | ||
| Mechanical Nominal Value Test Method | ||
| Dry: Tensile Modulus(1 mm/min) 6800 MPa ISO 527-1/-2 | ||
| Condition: Tensile Modulus(1 mm/min) 4500 MPa ISO 527-1/-2 | ||
| Dry: Stress at break 70 MPa ISO 527-1/-2 | ||
| Condition: Stress at break 55 MPa ISO 527-1/-2 | ||
| Dry: Strain at break 2 % ISO 527-1/-2 | ||
| Condition: Strain at break 4 % ISO 527-1/-2 | ||
| Dry: Charpy Impact Strength(23 °C) 30 kJ/m² ISO 179/1eU | ||
| Condition: Charpy Impact Strength(23 °C) 50 kJ/m² ISO 179/1eU | ||
| Dry: Charpy Notched Impact Strength(23 °C) 3 kJ/m² ISO 179 1eA | ||
| Condition: Charpy Notched Impact Strength(23 °C) 6 kJ/m² ISO 179 1eA | ||
| Izod impact strength, Notched(23 °C) 28 kJ/m² ISO 180/1U | ||
| Notched Izod Impact Strength(23 °C) 3.5 kJ/m² ISO 180/1A | ||
| Thermal | Nominal Value | Test Method |
| Melting Temperature(10 °C/min) | 220 °C | ISO 11357-1 |
| Flammability 0.75 mm 1.5 mm 3 mm |
V-2 V-2 V-0 |
UL 94 |
| Glow Wire Flammability Index 1.5 mm 3 mm |
960 °C 960 °C |
IEC 60695-2-12 |
| Glow Wire Ignition Temperature [GWIT] 0.75 mm 1.5 mm |
725 °C 960 °C |
IEC 60695-2-13 |
| Oxygen Index | 29 % | |
| Electrical | Nominal Value | Test Method |
| Comparative Tracking Index(Solution A) | 600 V | IEC 60112 |
| Processing | Nominal Value | |
| Drying Temperature | 80 °C | |
| Dry Time(with a dehumidified air drying point mini -20°C) | equipment, dew | 2 - 4 hr |
| Suggested Max Moisture | 0.002 | |
| Rear Temperature | 230 - 235 °C | |
| Middle Temperature | 235 - 240 °C | |
| Front Temperature | 240 - 245 °C | |
| Mold Temperature | 60 - 90 °C | |