Product Description | ||||
Chemical abbreviation according to ISO 1043-1: POM-HI Molding compound ISO 9988- POM-K, M-GNPR, 05-001 POM copolymer, modified Easy flowing, elastomer-containing injection molding type based on HOSTAFORM C 27021 with high toughness, and slightly lower hardness, rigidity and chemical resistance than the basic type; high resistance to thermal and oxidative degradation. UL-registration in natural and a thickness more than 1.57 mm as UL 94 HB. Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm thickness. Ranges of applications: For thin-walled molded parts with high energy-absorbing capacity. UL = Underwriters Laboratories (USA) FMVSS = Federal Motor Vehicle Safety Standard (USA) | ||||
General | ||||
Form | Resin Pellets | |||
Feature | Chemical Resistant Excellent Processability Outdoor High Energy Absorption |
|||
UL Yellow Card E42337-234627 | ||||
Uses | Thin-walled Parts | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.37 g/cm³ | ISO 1183 | ||
Melt Volume-Flow Rate, MVR(190 °C;2.16 kg) | 18 cm³/10 min | ISO 1133 | ||
Molding Shrinkage, Across Flow | 1.7 % | ISO 294-4 | ||
Molding Shrinkage, Flow | 1.8 % | ISO 294-4 | ||
Water Absorption, Saturation(23 °C) | 0.65 % | ISO 62 | ||
Water Absorption, Equilibrium(50% RH;23 °C) | 0.25 % | ISO 62 | ||
Ball Indentation Hardness(30s) | 90.0 MPa | ISO 2039-1 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | 1700 MPa | ISO 527-2/1A |
Tensile Stress, Yield | 44.0 MPa | ISO 527-2/1A/50 |
Tensile Strain, Yield | 10 % | ISO 527-2/1A/50 |
Nominal Tensile Strain at Break | 35 % | ISO 527-2/1A/50 |
Tensile creep modulus 1 hr 1000 hr |
1400 MPa 800 MPa |
ISO 899-1 |
Flexural Modulus(23 °C) | 1700 MPa | ISO 178 |
Charpy Notched Impact Strength -30 °C 23 °C |
6.0 kJ/m² 11 kJ/m² |
ISO 179 1eA |
Charpy Unnotched Impact Strength(-30 °C) | 110 kJ/m² | ISO 179 1eU |
Charpy Unnotched Impact Strength, Partial Break(23 °C) | 150 kJ/m² | ISO 179 1eU |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed(1.8 MPa) | 77.0 °C | ISO 75-2/A |
Vicat Softening Temperature | 125 °C | ISO 306/B50 |
Melting Point(10 °C/min) | 166 °C | ISO 11357-3 |
CLTE, Flow | 1.3E-4 cm/cm/°C | ISO 11359-2 |
Flame Rating 1.6 mm 3.2 mm |
HB HB |
UL 94 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 1.0E+13 ohms | IEC 60093 |
Volume Resistivity | 1.0E+13 ohms·cm | IEC 60093 |
Electric Strength | 28 kV/mm | IEC 60243-1 |
Relative Permittivity 100 Hz 1000000 Hz |
4.40 4.40 |
IEC 60250 |
Dissipation Factor 100 Hz 1000000 Hz |
0.010 0.020 |
IEC 60250 |
Comparative Tracking Index | 600 V | IEC 60112 |
Processing | Nominal Value |
Drying Temperature<Injection> | 100 - 120 °C |
Drying Time<Injection> | 3.0 - 4.0 hr |
Suggested Max Moisture<Injection> | 0.15 % |
Hopper Temperature<Injection> | 20 - 30 °C |
Rear Temperature<Injection> | 170 - 180 °C |
Middle Temperature<injection> | 180 - 190 °C |
Front Temperature<Injection> | 190 - 200 °C |
Nozzle Temperature<Injection> | 190 - 200 °C |
Processing Temp, Melt<Injection> | 190 - 200 °C |
Mold Temperature<Injection> | 60 - 70 °C |
Injection Rate<Injection> | Slow-Moderate |
Back Pressure<Injection> | < 2.00 MPa |
Feeding Zone Temperature<Injection> | 60 - 80 °C |
Zone4 temperature<Injection> | 190 - 200 °C |
Hot Runner Temperature<Injection> | 190 - 200 °C |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |