PA6 Resin Containing Mineral and Glass Fiber Improved UV Stability

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA6-PX11311U
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Nylon 6 resin containing mineral and glass fiber for Non-Chlorinated Flame  Retardant
 Heat-conducting nylon

Product Description

Product Description
compound is based on Nylon 6 resin containing mineral and glass fiber. Added features of this grade include: Thermally Conductive, Electrically Insulative and Non-Brominated, Non-Chlorinated Flame  Retardant.
General
Form		Resin Pellets
Filler
Feature		Thermally Conductive	Non-Brominated & Non-			Non-Chlorinated Electrically Isolative
			Chlorinated Flame R  t   d    t
UL Yellow Card	E207780 - 101282911
Uses	Consumer                         Industria     Building and Construction			Electrical
Physical			Nominal Value	Test  Method
Density / Specific Gravity			1.79 g/cm³	ASTM D792
Mold Shrinkage, Flow(24 hrs)			0.42 %	ASTM D955
Mold Shrinkage, XFlow(24 hrs)			0.58 %	ASTM D955
Water Absorption
24 hrs;23 °C			0.04 %	ISO 62-1
24 hrs;23 °C			0.23 %	Method
Moisture Absorption(50% RH;23 °C)			0.04 %	ISO 62
UV light, water exposure/immersion			f2	UL 746C
Mechanical			Nominal Value		Test Method
Izod Impact, Unnotched
23 °C			326 J/m		ASTM D4812
80*10*4;23 °C			23 kJ/m²		ISO 180/1U
Izod Impact, Notched
23 °C			30 J/m		ASTM D256
80*10*4;23 °C			3 kJ/m²		ISO 180/1A
Tensile Stress, Break
5 mm/min;Type I			98 MPa		ASTM D638
5 mm/min			108 MPa		ISO 527
Tensile Strain, Break
5 mm/min;Type I			1.3 %		ASTM D638
5 mm/min			1.3 %		ISO 527
Tensile Modulus
5 mm/min			1.3E+04 MPa		ASTM D638
1 mm/min			1.3E+04 MPa		ISO 527
Flexural Stress, Yield(1.3 mm/min;50 mm;span)			167 MPa		ASTM D790
Flexural Stress, break
1.3 mm/min;50 mm;span			176 MPa		ASTM D790
2 mm/min			186 MPa		ISO 178
Flexural Modulus
1.3 mm/min;50 mm;span			1.2E+04 MPa		ASTM D790
2 mm/min			1.3E+04 MPa		ISO 178
Impact Strength			2.4 - 27 kJ/m²		ISO R179
Thermal			Nominal Value		Test Method
UL Recognized(≥ 0.8 mm)			V-0		UL 94
Glow Wire Ignition Temperature [GWIT] 1 mm 3 mm			750 °C 800 °C		IEC 60695-2-13
Glow Wire Flammability Index 3 mm 1 mm			960 °C 960 °C		IEC 60695-2-12
Heat Deflection Temperature[HDT](0.45 MPa;3.2 mm)			227 °C		ASTM D648
Heat Deflection Temperature[HDT], Unannealed(1.82 MPa;6.4 mm)			215 °C		ASTM D648
CTE, Flow(40°C to 120°C)			4.1E-05 1/°C		ASTM E831
CTE, XFlow(40°C to 120°C)			8.5E-05 1/°C		ASTM E831
Thermal conductivity through plane
10*10*3mm sample			1.4 W/m-K		ASTM E1461-07
?80*3mm discs			0.9 W/m-K		ISO 22007-2
Thermal conductivity in plane
25*0.4mm disc			1.8 W/m-K		ASTM E1461-07
?80*3mm discs			1.9 W/m-K		ISO 22007-2
Ball Pressure Test(125°C +/- 2°C)			PASSES		IEC 60695-10-2
HDT/Bf(0.45)			228 °C		ISO 75/Bf
HDT/Af(1.8)			208 °C		ISO 75/Af
Relative Temp Index, Elec			130 °C		UL 746B
Relative Temp Index, Mechanical with Impact			105 °C		UL 746B
Relative Temp Index, Mechanical without Impact			140 °C		UL 746B
Electrical			Nominal Value		Test Method
Surface Resistivity			> 1.E+15 ohms		ASTM D257
Dielectric Strength, in Oil(1 mm)			> 10 kV/mm		ASTM D149
Dielectric Constant, Dk(1.1e+9 Hz)			4.84		ASTM ES 7-83
Dissipation Factor, Df(1.1e+9 Hz)			9.9E-03		ASTM ES 7-83
Comparative Tracking Index			600 V		IEC 60112
Comparative Tracking Index, CTI			PLC 0		UL 746A
Hot-wire Ignition, HWI ≥ 3 mm ≥ 1 mm ≥ 0.8 mm			PLC 0 PLC 2 PLC 3		UL 746A
High Amp Arc Ignition, HAI( ≥ 0.8 mm)			PLC 0		UL 746A
Processing					Nominal Value
Drying Temperature<Injection>					80 °C
Drying Time<Injection>					4 hrs
Maximum Moisture Content<Injection>					0.15 - 0.25 %
Melt Temperature<Injection>					270 - 295 °C
Front, Zone 3 Temperature<Injection>					270 - 290 °C
Middle, Zone 2 Temperature<Injection>					270 - 290 °C
Rear, Zone 1 Temperature<Injection>					260 - 275 °C
Mold Temperature<Injection>					85 - 100 °C
Back Pressure<Injection>					0.2 - 0.3 MPa
Screw Speed <Injection>					20 - 60 rpm

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....