Product Description |
Thermally conductive Nylon 6,6. |
General |
Form Resin Pellets |
Feature Thermally Conductive |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.41 g/cm³ ASTM D792 |
Molding Shrinkage, Flow 0.40 % ASTM D955 |
Molding Shrinkage, Across Flow 0.20 % ASTM D955 |
Mechanical Nominal Value Test Method |
Tensile Modulus(50 mm/min) 9180 MPa ASTM D638 |
Tensile Strength, Break(50 mm/min) 57.0 MPa ASTM D638 |
Tensile Elongation, Break(50 mm/min) 2.0 % ASTM D638 |
Flexural Modulus(1.3 mm/min;50 mm;Span) 7400 MPa ASTM D790 |
Flexural Strength, Break(1.3 mm/min;50 mm;Span) 105 MPa ASTM D790 |
Notched Izod Impact(23 °C) 37 J/m ASTM D256 |
Thermal Nominal Value Test Method |
Thermal Conductivity, Thru-Plane 0.50 - 0.75 W/m-K Internal Method |
Thermal Conductivity, in-plane 3.0 - 5.0 W/m-K Internal Method |
Electrical Nominal Value Test Method |
Surface Resistivity 5.0E+12 ohms ASTM D257 |
Processing |
Nominal Value |
Drying Temperature<Injection> |
80 - 85 °C |
Drying Time<Injection> |
2.0 - 4.0 hr |
Suggested Max Moisture<Injection> |
0.10 % |
Rear Temperature<Injection> |
255 - 270 °C |
Middle Temperature<injection> |
260 - 280 °C |
Front Temperature<Injection> |
270 - 290 °C |
Nozzle Temperature<Injection> |
280 - 300 °C |
Processing Temp, Melt<Injection> |
270 - 300 °C |
Mold Temperature<Injection> |
70 - 105 °C |
Injection Rate<Injection> |
Fast |
Back Pressure<Injection> |
0.138 MPa |
Screw Speed <Injection> |
60 - 80 rpm |