Audited Supplier XHT214-XH, the ultimate solution for demanding applications requiring high-flow and excellent resistance to heat.
This high quality polycarbonate copolymer is engineered to perform even in the most challenging environments.
With its superior flow properties, XHT214-XH is easy to mold into complex shapes and parts with exceptional accuracy. Its unique formulation guarantees high heat stability, making it perfect for applications exposed to extreme temperatures.
XHT214-XH is available in an array of attractive opaque and limited transparent colors to suit any design requirement.
| General | |||||
| Form | Resin Pellets | ||||
| Feature | Good Thermal | ||||
| Uses | Automotive | Consumer | Electrical | ||
| Physical | Nominal Value | Test Method | |||
| Density / Specific Gravity | 1.2 1.2 g/cm³ |
ASTM D792 ISO 1183 |
|||
| Mold Shrinkage, Flow(3.2 mm) | 0.6 - 0.9 % | SABIC Method | |||
| Melt Flow Rate[MFR](330 °C;2.16 kgf) | 46 g/10min | ASTM D1238 | |||
| Water Absorption(23 °C;saturated) | 0.3 % | ISO 62-1 | |||
| Moisture Absorption(50% RH;23 °C) | 0.23 % | ISO 62 | |||
| Melt Volume Rate, MVR(2.16 kg;330 °C) | 43 cm³/10 min | ISO 1133 | |||
| Mechanical | Nominal Value | Test Method | |||
| Izod Impact, Notched 23 °C -30 °C 80*10*4;23 °C 80*10*4;-30 °C |
115 J/m 75 J/m 11 kJ/m² 10 kJ/m² |
ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A |
|||
| Instrumented Dart Impact, Total Energy(23 °C) | 68 J | ASTM D3763 | |||
| Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0 |
NB kJ/m² NB kJ/m² |
ISO 180/1U | |||
| Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
10 kJ/m² 9 kJ/m² |
ISO 180/1A | |||
| Charpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 |
12 kJ/m² 9 kJ/m² |
ISO 179 1eA | |||
| Charpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 |
NB kJ/m² NB kJ/m² |
ISO 179 1eU |
| Tensile Stress, Yield 50 mm/min;Type I 50 mm/min |
70 MPa 70 MPa |
ASTM D638 ISO 527 |
| Tensile Stress, Break 50 mm/min;Type I 50 mm/min |
60 MPa 60 MPa |
ASTM D638 ISO 527 |
| Tensile Strain, Yield 50 mm/min;Type I 50 mm/min |
6.5 % 6.5 % |
ASTM D638 ISO 527 |
| Tensile Strain, Break 50 mm/min;Type I 50 mm/min |
90 % 90 % |
ASTM D638 ISO 527 |
| Tensile Modulus 5 mm/min 1 mm/min |
2600 MPa 2600 MPa |
ASTM D638 ISO 527 |
| Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min |
110 MPa 100 MPa |
ASTM D790 ISO 178 |
| Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
2550 MPa 2450 MPa |
ASTM D790 ISO 178 |
| Thermal | Nominal Value | Test Method |
| UL Recognized(≥ 1.5 mm) | HB | UL 94 |
| Glow Wire Ignition Temperature [GWIT](3 mm) | 875 °C | IEC 60695-2-13 |
| Glow Wire Flammability Index 3 mm 2 mm 1 mm |
960 °C 960 °C 960 °C |
IEC 60695-2-12 |
| Vicat Softening Temperature | ||
| Rate B/50 | 161 °C | ASTM D1525 |
| Rate B/50 | 160 °C | ISO 306 |
| Rate B/120 | 162 °C | ISO 306 |
| Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
155 °C 145 °C |
ASTM D648 |
| CTE, Flow -40 - 40 °C -40 - 40 °C |
6.0E-05 1/°C 6.0E-05 1/°C |
ASTM E831 ISO 11359-2 |
| CTE, XFlow -40 - 40 °C -40 - 40 °C |
6.0E-05 1/°C 6.0E-05 1/°C |
ASTM E831 ISO 11359-2 |
| Thermal Conductivity @ 25 °C(25 °C) | 0.2 W/m-K | ASTM C177 |
| Ball Pressure Test(125°C +/- 2°C) | PASSES | IEC 60695-10-2 |
| HDT/Bf(0.45) | 155 °C | ISO 75/Bf |
| HDT/Af(1.8) | 142 °C | ISO 75/Af |
| Metallized Haze Onset | 155 °C | SABIC Method |
| Relative Temp Index, Elec | 150 °C | UL 746B |
| Relative Temp Index, Mechanical with Impact | 130 °C | UL 746B |
| Relative Temp Index, Mechanical without Impact | 150 °C | UL 746B |
| Electrical | Nominal Value | Test Method |
| Volume Resistivity | > 1.0E+17 ohms·cm | ASTM D257 |
| Surface Resistivity | > 1.E +17 ohms | ASTM D257 |
| Dielectric Strength, in Oil(3.2 mm) | 22.6 kV/mm | ASTM D149 |
| Dissipation Factor 100 Hz 1.0e+6 Hz |
3 3.1 |
ASTM D150 |
| Comparative Tracking Index, CTI | PLC 3 | UL 746A |
| Hot-wire Ignition, HWI(1.5 mm) | PLC 3 | UL 746A |
| High Amp Arc Ignition, HAI(1.5 mm) | PLC 0 | UL 746A |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 125 °C | |
| Drying Time<Injection> | 4 - 6 hrs | |
| Maximum Moisture Content<Injection> | 0.02 % | |
| Melt Temperature<Injection> | 290 - 350 °C | |
| Nozzle Temperature<Injection> | 285 - 345 °C | |
| Front, Zone 3 Temperature<Injection> | 290 - 350 °C | |
| Middle, Zone 2 Temperature<Injection> | 280 - 340 °C | |
| Rear, Zone 1 Temperature<Injection> | 270 - 330 °C | |
| Mold Temperature<Injection> | 85 - 130 °C | |
| Back Pressure<Injection> | 0.3 - 0.7 MPa | |
| Screw Speed<Injection> | 40 - 90 rpm | |
| Shot To Cylinder Size<Injection> | 40 - 60 % | |
| Vent Depth<Injection> | 0.025 - 0.08 mm |