Resin Is a Non-Reinforced Blend of Polyphenylene Ether (PPE) + Polystyrene (PS) Designed

• Feature: Plastics
• CAS No.: 25766-59-0
• Formula: C6h4c(CH3)2c6h4oco2-]N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: MPPE/PS-NHP8000VT3
• EINECS: 618-371-8
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Polycarbonate
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

 This grade is targeted for electrical vehicle battery pack insulation sheet/film

Product Description

Product Description
NHP8000VT3 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS) designed for high heat resistance, ultra-thin-wall FR and High tracking resistance performance. This extrusion and injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries CTI 600V / PLC 0 and UL94 flame rating of V0 at 0.25mm. NHP8000VT3 is based on a unique co-polymer technology and exhibits high impact, high heat resistance, dimensional stability, hydrolytic stability, strong electrical performance, low moisture absorption and low specific gravity. This grade is targeted for electrical vehicle (EV) battery pack insulation sheet/film, bus bar insulation layer and other high voltage electric components.
General
Form                                        Resin Pellets
Low Warpage                    Low Shrinkage                  Non-Brominated
Feature	Chlorinated Flame   Retardant			Good Thermal   Hydrolysis Resistance Li  ht W  i  ht
g    mpac                           ow    o s ure                          g    -    e g
Hood
Household electrics                 Energy Storage
Physical                                                                                                                      Nominal Value                                                        Test Method
Density / Specific Gravity                                                     1.10 g/cm³                                             ISO 1183
Melt Mass-Flow Rate, MFR(300 °C;5 kg)                             12 g/10min                                             ASTM D1238
Molding Shrinkage, Flow                                                     0.73 %                                                    Internal Method
Molding Shrinkage, Across Flow                                         0.79 %                                                    Internal Method
Water Absorption(24 hr;23 °C)                                            0.040 %                                                  ISO 62
Mechanical		Nominal Value			Test Method
Tensile Modulus(5 mm/min)		2490 MPa			ASTM D638
Tensile Strength, Yield(5 mm/min;Type I)		66.8 MPa			ASTM D638
Tensile Elongation, Yield(5 mm/min;Type I)		4.2 %			ASTM D638
Tensile Elongation, Break(5 mm/min;Type I)		11 %			ASTM D638
Flexural Modulus(1.3 mm/min;50 mm;Span)		2600 MPa			ASTM D790
Flexural Strength(1.3 mm/min;50 mm;Span)		108 MPa			ASTM D790
Notched Izod Impact -40 °C 23 °C		84 J/m 210 J/m			ASTM D256
Unnotched Izod Impact -40 °C 23 °C		1800 J/m No Break			ASTM D4812
Thermal		Nominal Value			Test Method
Deflection Temperature Under Load, Unannealed 0.45 MPa;3.2 mm 1.8 MPa;3.2 mm		150 °C 133 °C			ASTM D648
Vicat Softening Temperature 50 °C/h;10 N;Rate A;Loading 1 50 °C/h;50 N;Rate A;Loading 2		166 °C 155 °C			ASTM D1525
Ball Pressure Test(123 - 127 °C)		Pass			IEC 60695-10-2
Ball Pressure Test, Approximate Maximum(140 °C)		Pass			IEC 60695-10-2
Flame Rating(> 0.25 mm)		V-0			UL 94
Electrical		Nominal Value			Test Method
Surface Resistivity		7.5E+16 ohms			ASTM D257
Volume Resistivity		6.2E+15 ohms ·cm			ASTM D257
Comparative Tracking Index, CTI		PLC 0			UL 746A
Processing			Nominal Value
Drying Temperature<Injection>			100 - 120 °C
Drying Time<Injection>			3.0 - 5.0 hr
Rear Temperature<Injection>			280 - 330 °C
Middle Temperature<injection>			280 - 330 °C
Front Temperature<Injection>			280 - 330 °C
Nozzle Temperature<Injection>			250 - 330 °C
Processing Temp, Melt<Injection>			280 - 330 °C
Mold Temperature<Injection>			70 - 120 °C
Back Pressure<Injection>			3.00 - 8.00 MPa
Screw Speed <Injection>			20 - 100 rpm

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....