Feature: | Plastics |
---|---|
CAS No.: | 32131-17-2 |
Formula: | C36h66n6o6 |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
A 218 V15 BK 21N-XH is a heat-stabilized polyamide 66 material with 15% glass fiber reinforcement, designed specifically for injection molding. This grade showcases a remarkable balance of thermal and mechanical properties, making it highly versatile and reliable for various applications.
General |
|||
Form Resin Pellets |
|||
Filler 15 % Glass Fiber |
|||
Feature Anti Aging |
|||
Usage |
Industrial Applications Electrical applications |
Connector Consumer |
|
Physical Nominal Value Test Method |
|||
Density / Specific Gravity 1.24 g/cm³ ISO 1183 |
|||
Water Absorption(24 hr, 23°C) 1.1 % ISO 62 |
|||
Molding shrinkage, parallel(72 hr, 23°C, 50% RH) 0.5 % |
ISO 294-4, ISO 2577 |
||
Molding shrinkage, normal(72 hr, 23°C, 50% RH) 1.4 % |
ISO 294-4, ISO 2577 |
Mechanical |
Nominal Value |
Test Method |
Tensile Modulus 1 mm/min;dry 1 mm/min;conditioned |
6200 MPa 4300 MPa |
ISO 527-1/-2 |
Stress at break dry conditioned |
125 MPa 90 MPa |
ISO 527-1/-2 |
Strain at break dry conditioned |
3 % 8 % |
ISO 527-1/-2 |
Flexural Modulus 2 mm/min;dry 2 mm/min;conditioned |
5300 MPa 3500 MPa |
ISO 178 |
Flexural Strength(2 mm/min;conditioned) |
115 MPa |
ISO 178 |
C harpy Impact Strength, Unnotched 23 °C;dry 23 °C;conditioned |
40 kJ/m² 65 kJ/m² |
ISO 179 1eU |
C harpy Notched Impact Strength 23 °C;dry 23 °C;conditioned |
5 kJ/m² 6.5 kJ/m² |
ISO 179 1eA |
Izod impact strength, Notched 23 °C;dry 23 °C;conditioned |
40 kJ/m² 65 kJ/m² |
ISO 180/1U |
Notched Izod Impact Strength 23 °C;dry 23 °C;conditioned |
5 kJ/m² 10 kJ/m² |
ISO 180/1A |
Thermal |
Nominal Value |
Test Method |
Melting Temperature(10°C/min) |
263 °C |
ISO 11357-1 |
Temp. of deflection under load(1.8 MPa) |
245 °C |
ISO 75 |
Flammability(3 mm) |
HB |
UL 94 |
Oxygen Index |
24 % |
Electrical |
Nominal Value |
Test Method |
Volume Resistivity |
1E+11 ohms ·cm |
IEC 62631-3-1 |
Surface Resistivity |
6E+015 Ohms |
IEC 62631-3-1 |
Comparative Tracking Index(Solution A) |
400 V |
IEC 60112 |
Dielectric Strength(1 mm) |
31 kV/mm |
IEC 60243-1 |
Processing |
Nominal Value |
|
Suggested Max Moisture |
0.2 % |
|
Rear Temperature |
270 - 280 °C |
|
Middle Temperature |
275 - 285 °C |
|
Front Temperature |
280 - 290 °C |
|
Blow Molding Mold Temperature |
70 - 100 °C |