Feature: | Plastics |
---|---|
CAS No.: | 9003-56-9 |
Formula: | C45h51n3X2 |
Samples: |
25kg/bag
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | |||||
Superior flow, injection molding ABS for thin-wall medical applications. Biocompatible (ISO 10993). FDA compliant. Gamma & EtO sterilizable. | |||||
General | |||||
Form | Resin Pellets | ||||
Feature |
Biocompatible Fda |
Medical Disinfection Application Excellent Processabilit |
Gamma Sterilizable Eto Sterilization X-Ra Sterilizable |
||
UL Yellow Card E121562-220727 | |||||
Electronic Displays Constraction |
Fluid Handling | Pharmaceuticals | |||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.04 g/cm³ 1.06 g/cm³ |
ASTM D792 ISO 1183 |
|||
Melt Mass-Flow Rate, MFR 230 °C;3.8 kg 220 °C;5 kg |
12 g/10min 12 g/10min |
ASTM D1238 ISO 1133 |
|||
Molding Shrinkage, Flow(3.2 mm) | 0.50 - 0.80 % | Internal Method | |||
Melt Viscosity(240 °C;1.0e+3 sec^-1) | 173 Pa · s | ISO 11443 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | ||
5 mm/min | 2480 MPa 2450 MPa |
ASTM D638 ISO 527-2/1 |
Tensile Strength, Yield | ||
5 mm/min;Type I | 46.0 MPa 40.0 MPa |
ASTM D638 ISO 527-2/5 |
Tensile Strength, Break | ||
5 mm/min;Type I | 35.0 MPa 35.0 MPa |
ASTM D638 ISO 527-2/5 |
Tensile Elongation, Yield | ||
5 mm/min;Type I | 2.0 % 2.0 % |
ASTM D638 ISO 527-2/5 |
Tensile Elongation, Break | ||
5 mm/min;Type I | 18 % 35 % |
ASTM D638 ISO 527-2/5 |
Flexural Modulus 1.3 mm/min;50 mm;Span 2 mm/min |
2620 MPa 2500 MPa |
ASTM D790 ISO 178 |
Flexural Stress, at Yield(2 mm/min) | 70.0 MPa | ISO 178 |
Flexural Stress, Yield(1.3 mm/min;50 mm;Span) | 79.0 MPa | ASTM D790 |
Charpy Notched Impact Strength(23 °C;80*10*4;sp=62mm 0) |
23 kJ/m² | ISO 179 1eA |
Notched Izod Impact | ||
-30 °C | 80 J/m | ASTM D256 |
23 °C | 240 J/m | ASTM D256 |
80*10*4 mm;-30 °C | 7.0 kJ/m² | ISO 180/1A |
80*10*4 mm;23 °C | 16 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 21.0 J | ASTM D3763 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;3.2 mm 1.8 MPa;3.2 mm 80*10*4 mm;1.8 MPa;4 mm;64 mm;Span |
93.0 °C 77.0 °C 80.0 °C |
ASTM D648 ASTM D648 ISO 75-2/Af |
Vicat Softening Temperature 50 °C/h;50 N;Rate A;Loading 2 |
98.0 °C 100 °C |
ISO 306/B120 |
CLTE, Flow(-40 - 40 °C) | 8.8E-5 cm/cm/°C | ISO 11359-2 |
CLTE, Transverse(-40 °C) | 8.5E-5 cm/cm/°C | ISO 11359-2 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 90 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.10 % | |
Suggested Shot Size<Injection> | 50 - 70 % | |
Rear Temperature<Injection> | 190 - 200 °C | |
Middle Temperature<injection> | 200 - 210 °C | |
Front Temperature<Injection> | 205 - 225 °C | |
Nozzle Temperature<Injection> | 205 - 245 °C | |
Processing Temp, Melt<Injection> | 205 - 245 °C | |
Mold Temperature<Injection> | 50 - 70 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed<Injection> | 30 - 60 rpm | |
Vent Depth<Injection> | 0.038 - 0.051 mm |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |