Product Description | ||||
LNP LUBRICOMP C2801 compound is based on Polycarbonate / Acrylonitrile Butadiene Styrene (PC/ABS) blend containing 5% PTFE. Added features of this grade include: Wear Resistant and Flame Retardant suitable for moving components in business equipment. Medium Heat performance. |
||||
General | ||||
Form | Resin Pellets | |||
Filler | 5 % PTFE | |||
Feature | ||||
UL Yellow Card | E121562-221032 E207780-228469 |
|||
Uses |
Automotive Electrical |
Consumer Industria Building and Construction |
||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.22 | ASTM D792 | ||
Mold Shrinkage, Flow(3.2 mm) | 0.4 - 0.5 % | SABIC Method | ||
Mold Shrinkage, XFlow(3.2 mm) | 0.3 - 0.5 % | SABIC Method | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Notched(23 °C) | 133 J/m | ASTM D256 | ||
Tensile Stress, Yield(50 mm/min;Type I) | 62 MPa | ASTM D638 | ||
Tensile Stress, Break(50 mm/min;Type I) | 51 MPa | ASTM D638 | ||
Tensile Strain, Break(50 mm/min;Type I) | 110 % | ASTM D638 | ||
Flexural Stress, Yield(2.6 mm/min;100 mm;Span) | 95 MPa | ASTM D790 | ||
Flexural Modulus(2.6 mm/min;100 mm;Span) | 2720 MPa | ASTM D790 | ||
K-Factor Xe-10(PV =2000 psi-fpm vs Steel) | 430 | SABIC Method | ||
Coefficient of Friction, Steel, Static | 0.16 | ASTM D1894 | ||
Coefficient Of Friction, Steel, Kinetic | 0.21 | ASTM D1894 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 2.5 mm ≥ 1.5 mm ≥ 1 mm |
5VB V-0 V-1 |
UL 94 |
Heat Deflection Temperature[HDT], Unannealed(1.82 MPa;6.4 mm) | 82 °C | ASTM D648 |
Relative Temp Index, Elec | 60 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 60 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 60 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Comparative Tracking Index, CTI | PLC 1 | UL 746A |
Hot-wire Ignition, HWI( ≥ 1.5 mm) | PLC 3 | UL 746A |
High Amp Arc Ignition, HAI( ≥ 1.5 mm) | PLC 0 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 75 - 80 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 8 hrs | |
Maximum Moisture Content<Injection> | 0.04 % | |
Melt Temperature<Injection> | 230 - 275 °C | |
Nozzle Temperature<Injection> | 230 - 275 °C | |
Front, Zone 3 Temperature<Injection> | 225 - 275 °C | |
Middle, Zone 2 Temperature<Injection> | 215 - 260 °C | |
Rear, Zone 1 Temperature<Injection> | 210 - 255 °C | |
Mold Temperature<Injection> | 50 - 70 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 30 - 80 % | |
Vent Depth <Injection> | 0.038 - 0.076 mm |