Product Description | ||||||
LNP THERMOCOMP MFB82I compound is based on Polypropylene (PP) resin containing 10% glass fiber, 40% glass bead. Added features of this grade include: Improved Impact. | ||||||
General | ||||||
Form | Resin Pellets | |||||
Filler | 40 % Glass Bead | 10 % Glass Fiber | ||||
Feature | Low Warpage | High Impact | Structural | |||
Enhanced Ductility | ||||||
UL Yellow Card | E207780-101344665 E45329-101282765 |
|||||
Uses Consumer | Electrical | |||||
Physical | Nominal Value | Test Method | ||||
Molding Shrinkage, Flow, Tensile Bar | 0.1 - 0.3 % | Method | ||||
Density / Specific Gravity | 1.32 g/cm³ | ISO 1183 | ||||
Mechanical | Nominal Value | Test Method | ||||
Izod Impact, Unnotched(80*10*4;23 °C) | 35 kJ/m² | ISO 180/1U | ||||
Izod Impact, Notched(80*10*4;23 °C) | 14 kJ/m² | ISO 180/1A | ||||
Tensile Stress, Break(5 mm/min) | 50 MPa | ISO 527 | ||||
Tensile Strain, Break(5 mm/min) | 3.5 % | ISO 527 | ||||
Tensile Modulus(1 mm/min) | 4500 MPa | ISO 527 | ||||
Flexural Stress, break(2 mm/min) | 58 MPa | ISO 178 | ||||
Flexural Modulus(2 mm/min) | 3800 MPa | ISO 178 | ||||
Thermal | Nominal Value | Test Method | ||||
UL Recognized(≥ 0.75 mm) | HB | UL 94 | ||||
CTE, Flow(23°C to 60°C) | 3.7E-05 1/°C | ISO 11359-2 | ||||
CTE, XFlow(23°C to 60°C) | 1.3E-04 1/°C | ISO 11359-2 | ||||
HDT/Af(1.8) | 133 °C | ISO 75/Af | ||||
Relative Temp Index, Elec | 65 °C | UL 746B | ||||
Relative Temp Index, Mechanical with Impact | 65 °C | UL 746B | ||||
Relative Temp Index, Mechanical without Impact | 65 °C | UL 746B | ||||
Processing | Nominal Value | |||||
Drying Temperature<Injection> | 80 °C | |||||
Drying Time<Injection> | 4 hrs | |||||
Melt Temperature<Injection> | 225 - 250 °C | |||||
Front, Zone 3 Temperature<Injection> | 240 - 250 °C | |||||
Middle, Zone 2 Temperature<Injection> | 215 - 225 °C | |||||
Rear, Zone 1 Temperature<Injection> | 195 - 205 °C | |||||
Mold Temperature<Injection> | 30 - 50 °C | |||||
Back Pressure<Injection> | 0.2 - 0.3 MPa | |||||
Screw Speed <Injection> | 30 - 60 rpm |