Thermally Conductive Electrically Insulative Non-Brominated Chlorinated Fr Nylon 6 Resin

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA6- PX13012XH
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 30% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Glass Fiber Reinforced Polyamide 6 Injection Molding Resin with Improved Thermal Conductivity

 

Product Description
PX13012-XH compound is the good proposal for the thermal conductivity requirements. Made from Nylon 6 resin, this compound is engineered to perfection to deliver superior performance and reliability. The key highlight of this grade is its proprietary thermal filler that ensures efficient heat transfer and distribution for effective thermal management.     Additionally, PX13012-XH compound comes equipped with a range of added features such as electrically insulative and non-brominated, non-chlorinated flame retardant properties, making it the ultimate choice for a wide range of applications.     The Thermally Conductive feature of this compound ensures efficient heat transfer, while the Electrically Insulative property makes it ideal for electrical applications that require non-conductive materials. The non-brominated, non-chlorinated flame retardant feature provides extra safety while using this compound.     Overall, if you are looking for a high-quality, reliable, and efficient thermal conductivity solution, PX13012-XH compound is the perfect choice for you!
General
Form	Resin Pellets
Thermally Conductive Feature			Non-Brominated & Non- Chlorinated Flame            Retardant		Non-Chlorinated Electrically Isolative
Consumer                         Industria   Building and Construction				Electrical
Physical	Nominal Value			Test Method
Molding Shrinkage, Flow, Tensile Bar		0.7 %		SABIC Method
Mold Shrinkage, Flow 24 hrs 24 hrs		0.55 % 0.55 %		ASTM D955 ISO 294
Mold Shrinkage, XFlow 24 hrs 24 hrs		0.65 % 0.65 %		ASTM D955 ISO 294
Density / Specific Gravity		1.68 g/cm³		ISO 1183
Water Absorption(24 hrs;23 °C)		0.23 %		ISO 62-1

 

 

Mechanical	Nominal Value	Test Method
Izod Impact, Unnotched 23 °C 80*10*4;23 °C	152 J/m 9 kJ/m²	ASTM D4812 ISO 180/1U
Izod Impact, Notched 23 °C 80*10*4;23 °C	15 J/m 3 kJ/m²	ASTM D256 ISO 180/1A
Tensile Stress, Yield(5 mm/min;Type I)	68 MPa	ASTM D638
Tensile Strain, Break 5 mm/min;Type I 5 mm/min	1.2 % 1.1 %	ASTM D638 ISO 527
Tensile Modulus 5 mm/min 1 mm/min	1.0E+04 MPa 1.3E+04 MPa	ASTM D638 ISO 527
Flexural Stress, break(1.3 mm/min;50 mm;span)	119 MPa	ASTM D790
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min	1.2E+04 MPa 1.2E+04 MPa	ASTM D790 ISO 178
Tensile Stress, Break(5 mm/min)	75 MPa	ISO 527
Flexural Stress, Yield(2 mm/min)	105 MPa	ISO 178

 

Thermal	Nominal Value	Test Method
UL Recognized(≥ 0.8 mm)	V-0	UL 94
Glow Wire Ignition Temperature [GWIT] 0.8 mm 1.6 mm 3 mm	750 °C 775 °C 800 °C	IEC 60695-2-13
Glow Wire Flammability Index 0.8 mm 1.6 mm 3 mm	960 °C 960 °C 960 °C	IEC 60695-2-12
Heat Deflection Temperature[HDT](0.45 MPa;3.2 mm)	203 °C	ASTM D648
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1 82 MPa)	137 °C	ASTM D648
CTE, Flow -40 - 40 °C -30°C to 80°C	3.3E-05 1/°C 3.9E-05 1/°C	ASTM E831 ISO 11359-2
CTE, XFlow -40 - 40 °C -30°C to 80°C	4.4E-05 1/°C 5.5e-05 1/°C	ASTM E831 ISO 11359-2
Thermal conductivity through plane(60*60*3mm plaque)	1.2 W/m-K	ISO 22007-2
Thermal conductivity in plane(60*60*3mm plaque)	5.5 W/m-K	ISO 22007-2
Ball Pressure Test(165°C +/- 2°C)	PASSES	IEC 60695-10-2
HDT/Bf(0.45)	203 °C	ISO 75/Bf
HDT/Af(1.8)	160 °C	ISO 75/Af
Relative Temp Index, Elec	130 °C	UL 746B
Relative Temp Index, Mechanical with Impact	100 °C	UL 746B
Relative Temp Index, Mechanical without Impact	130 °C	UL 746B

 

Electrical	Nominal Value	Test Method
Surface Resistivity	4.0E+14 ohms	ASTM D257
Dielectric Strength, in Oil(1.6 mm)	7.2 kV/mm	ASTM D149
Dielectric Strength(1.6 mm)	6.1 kV/mm	IEC 60243-1
Comparative Tracking Index, CTI	PLC 0	UL 746A
Comparative Tracking Index	600 V	IEC 60112
Hot-wire Ignition, HWI(≥ 0.8 mm)	PLC 0	UL 746A
High Amp Arc Ignition, HAI(≥ 0.8 mm)	PLC 0	UL 746A
Processing		Nominal Value
Drying Temperature<Injection>		80 °C
Drying Time<Injection>		4 hrs
Maximum Moisture Content<Injection>		0.25 %
Minimum Moisture Content<Injection>		0.15 %
Melt Temperature<Injection>		270 - 295 °C
Front, Zone 3 Temperature<Injection>		270 - 290 °C
Middle, Zone 2 Temperature<Injection>		270 - 290 °C
Rear, Zone 1 Temperature<Injection>		260 - 275 °C
Mold Temperature<Injection>		85 - 100 °C
Back Pressure<Injection>		0.2 - 0.3 MPa
Screw Speed<Injection>		20 - 60 rpm

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....